Structural Characteristics and In Vitro Digestibility of Malic Acid-Treated Corn Starch with Different pH Conditions.

The objective of this study was to investigate the influence of pH value on the in vitro digestibility of malic acid-treated corn starch in relation to its structural properties. Varying pH values (1.5-8.5) of 2 M malic acid solution were combined with corn starch in a forced-air oven at 130 °C for 12 h. Using Fourier-transform infrared spectroscopy (FT-IR), carbonyl groups were detected in malic acid-treated corn starch, indicating cross-linking through esterification. As the pH value of malic acid-treated corn starch decreased from 8.5 to 1.5, the resistant starch content increased from 18.2 to 74.8%. This was the result of an increased degree of substitution and was maintained after gelatinization. The granular structure of malic acid-treated corn starches was not destroyed, and the starches maintained birefringence. This malic acid-treated corn starch could be utilized in heat processed foods such as bread and cookies as well as in products with reduced calories.

Impact of esterification with malic acid on the structural characteristics and in vitro digestibilities of different starches.

This research focused on the structural characteristics of resistant starches (RSs) that were obtained from corn, potato, and sweet potato and esterified by L-malic acid. Further, the unique effect of the degree of substitution (DS) on the crystalline properties was studied. Different starches were allowed to react with 2 M malic acid (pH 1.5) for 12 h at 130 °C. The shapes of the granules and the Maltese-cross shapes of samples were maintained and visible under an optical microscope. The FT-IR spectrum displayed evident carbonyl peaks at 1740 cm-1, and the onset temperature (To) and gelatinization enthalpy (∆H) gradually decreased as DS increased. The malic acid-treated starches exhibited an increased RS content compared to those of the control. The RS contents of potato, sweet potato, and corn, which were 65.5%, 70.0%, and 89.8% in the uncooked MT-samples, decreased to 57.3%, 63.8%, and 86.7% in the cooked MT-samples, respectively, and exhibited high heat stability; corn starch yielded the highest RS among them. The thermal and malic acid treatments resulted in the partial hydrolysis and rearrangement of the helix structure of crystalline area, which was affected by esterification. The result revealed that the RS content increased as that of DS escalated.

Structural characteristics of low-digestible sweet potato starch prepared by heat-moisture treatment.

The objectives of this study were to optimize the conditions for the preparation of sweet potato starch containing a high proportion of slowly digestible starch (SDS) by heat-moisture treatment (HMT), and to investigate the structural properties of SDS and resistant starch (RS) fractions isolated from this modified starch. Response surface methodology evaluation of considering temperature, time, and moisture content was conducted to determine the HMT condition for maximizing SDS yield. Maximum SDS content (50.9%) was obtained after 8.6 h at 113 °C with 22.8% moisture level. Scanning electron micrographs of RS fractions displayed growth ring structure and hollow regions. X-ray diffraction patterns of SDS + RS and RS fractions were not changed by HMT. Gelatinization enthalpy of the SDS + RS fraction was decreased more than that of the RS fraction. The results indicated that the SDS fraction consisted of less perfect crystallites and amorphous regions, whereas the RS fraction was composed mostly of crystalline regions.