Ethylene-alt-α-Olefin Copolymers by Hydrogenation of Highly Stereoregular cis-1,4 Polydienes: Synthesis and Structural Characterization.

The homogeneous non-catalytic hydrogenation of several types of iso- and syndiotactic cis-1,4 poly(1,3-diene)s with diimide, formed by thermal decomposition of p-toluene-sulfonyl-hydrazide, was examined. Perfectly alternating ethylene/1-alkene copolymers having different tacticity (i.e., isotactic and syndiotactic), which in some cases are difficult to synthesize by simple stereospecific co-polymerization of the corresponding monomers, were obtained. All the copolymers synthesized were fully characterized from a structural, morphological, and rheological point of view through different analytical techniques (FT-IR, NMR, GPC, DSC, RX).

Novel Cobalt Dichloride Complexes with Hindered Diphenylphosphine Ligands: Synthesis, Characterization, and Behavior in the Polymerization of Butadiene.

Two novel cobalt diphenylphosphine complexes were synthesized by reacting cobalt(II) chloride with tert-butyl(diphenyl)phosphine (PtBuPh2) and (S)-(+)neomenthyldiphenylphosphine [(S)-NMDPP]. The crystal structure of the former was determined by single-crystal X-ray diffraction studies. The two complexes were then used in combination with methylaluminoxane (MAO) for the polymerization of 1,3-butadiene: crystalline highly syndiotactic 1,2 poly(1,3-butadiene)s were obtained, with a 1,2 content and a syndiotactic index (percentage of syndiotactic triads [rr]) up to 95% and 85%, respectively. The results obtained further support and confirm what was already observed in the polymerization of 1,3-butadiene with CoCl2(PRPh2)2-MAO (R = methyl, ethyl, normal-propyl, iso-propyl, and cyclohexyl): the nature of the phosphine ligand strongly affects the polymerization stereoselectivity, the polymer syndiotacticity increasing with increasing phosphine ligand steric hindrance.

Isotactic and Syndiotactic Alternating Ethylene/Propylene Copolymers Obtained Through Non-Catalytic Hydrogenation of Highly Stereoregular cis-1,4 Poly(1,3-diene)s.

The homogeneous non-catalytic hydrogenation of cis-1,4 poly(isoprene), isotactic cis-1,4 poly(1,3-pentadiene) and syndiotactic cis-1,4 poly(1,3-pentadiene) with diimide, formed by thermal decomposition of para-toluenesulfonylhydrazide, is examined. Perfectly alternating ethylene/propylene copolymers having different tacticity (i.e., isotactic and syndiotactic), which are difficult to synthesize by stereospecific copolymerization of the corresponding monomers, are obtained. Both isotactic and syndiotactic alternating ethylene/propylene copolymers are amorphous, with very low glass transition temperatures.