Poly(dl-lactide) Polymer Blended with Mineral Phases for Extrusion 3D Printing-Studies on Degradation and Biocompatibility.

A promising therapeutic option for the treatment of critical-size mandibular defects is the implantation of biodegradable, porous structures that are produced patient-specifically by using additive manufacturing techniques. In this work, degradable poly(DL-lactide) polymer (PDLLA) was blended with different mineral phases with the aim of buffering its acidic degradation products, which can cause inflammation and stimulate bone regeneration. Microparticles of CaCO3, SrCO3, tricalcium phosphates (α-TCP, ß-TCP), or strontium-modified hydroxyapatite (SrHAp) were mixed with the polymer powder following processing the blends into scaffolds with the Arburg Plastic Freeforming 3D-printing method. An in vitro degradation study over 24 weeks revealed a buffer effect for all mineral phases, with the buffering capacity of CaCO3 and SrCO3 being the highest. Analysis of conductivity, swelling, microstructure, viscosity, and glass transition temperature evidenced that the mineral phases influence the degradation behavior of the scaffolds. Cytocompatibility of all polymer blends was proven in cell experiments with SaOS-2 cells. Patient-specific implants consisting of PDLLA + CaCO3, which were tested in a pilot in vivo study in a segmental mandibular defect in minipigs, exhibited strong swelling. Based on these results, an in vitro swelling prediction model was developed that simulates the conditions of anisotropic swelling after implantation.

A comparative analysis of 3D printed scaffolds consisting of poly(lactic-co-glycolic) acid and different bioactive mineral fillers: aspects of degradation and cytocompatibility.

Their excellent mechanical properties, degradability and suitability for processing by 3D printing technologies make the thermoplastic polylactic acid and its derivatives favourable candidates for biomaterial-based bone regeneration therapies. In this study, we investigated whether bioactive mineral fillers, which are known to promote bone healing based on their dissolution products, can be integrated into a poly(L-lactic-co-glycolic) acid (PLLA-PGA) matrix and how key characteristics of degradation and cytocompatibility are influenced. The polymer powder was mixed with particles of CaCO3, SrCO3, strontium-modified hydroxyapatite (SrHAp) or tricalcium phosphates (α-TCP, ß-TCP) in a mass ratio of 90 : 10; the resulting composite materials have been successfully processed into scaffolds by the additive manufacturing method Arburg Plastic Freeforming (APF). Degradation of the composite scaffolds was investigated in terms of dimensional change, bioactivity, ion (calcium, phosphate, strontium) release/uptake and pH development during long-term (70 days) incubation. The mineral fillers influenced the degradation behavior of the scaffolds to varying degrees, with the calcium phosphate phases showing a clear buffer effect and an acceptable dimensional increase. The amount of 10 wt% SrCO3 or SrHAp particles did not appear to be appropriate to release a sufficient amount of strontium ions to exert a biological effect in vitro. Cell culture experiments with the human osteosarcoma cell line SAOS-2 and human dental pulp stem cells (hDPSC) indicated the high cytocompatibility of the composites: For all material groups cell spreading and complete colonization of the scaffolds over the culture period of 14 days as well as an increase of the specific alkaline phosphatase activity, typical for osteogenic differentiation, were observed.

Cell-Material Interactions in Direct Contact Culture of Endothelial Cells on Biodegradable Iron-Based Stents Fabricated by Laser Powder Bed Fusion and Impact of Ion Release.

Additive manufacturing is a promising technology for the fabrication of customized implants with complex geometry. The objective of this study was to investigate the initial cell-material interaction of degradable Fe-30Mn-1C-0.02S stent structures in comparison to conventional 316L as a reference, both processed by laser powder bed fusion. FeMn-based alloys have comparable mechanical properties with clinically applied AISI 316L for a corrosion-resistant stent material. Different corrosion stages of the as-built Fe-30Mn-1C-0.02S stent surfaces were simulated by pre-conditioning in DMEM under cell culture conditions for 2 h, 7 days, and 28 days. Human umbilical vein endothelial cells (HUVECs) were directly seeded onto the pre-conditioned samples, and cell viability, adherence, and morphology were analyzed. These studies were accompanied by measurements of iron and manganese ion release and Auger electron spectroscopy to evaluate the influence of corrosion products and degradation on the cells. In the initial phase (2 h of pre-conditioning), HUVECs were able to attach but the cell number decreased over the cultivation period of 14 days and the CD31 staining pattern of intercellular contacts was disordered. At later time points of corrosion (7 and 28 days of pre-conditioning), CD31 staining was distinctly located at the intercellular contacts, and the cell density increased after seeding and was stable for up to 14 days. Formation of a complex degradation layer, which had a composition and thickness dependent on the pre-conditioning time, led to a reduced ion release and finally showed a positive effect on cell survival. Concluding, our data suggest the suitability of Fe-30Mn-1C-0.02S for in vivo applications.

Three-dimensional plotting of a cell-laden alginate/methylcellulose blend: towards biofabrication of tissue engineering constructs with clinically relevant dimensions.

Biofabrication of tissue engineering constructs with tailored architecture and organized cell placement using rapid prototyping technologies is a major research focus in the field of regenerative therapies. This study describes a novel alginate-based material suitable for both cell embedding and fabrication of three-dimensional (3D) structures with predefined geometry by 3D plotting. The favourable printing properties of the material were achieved by using a simple strategy: addition of methylcellulose (MC) to a 3% alginate solution resulted in a strongly enhanced viscosity, which enabled accurate and easy deposition without high technical efforts. After scaffold plotting, the alginate chains were crosslinked with Ca2+ ; MC did not contribute to the gelation and was released from the scaffolds during the following cultivation. The resulting constructs are characterized by high elasticity and stability, as well as an enhanced microporosity caused by the transient presence of MC. The suitability of the alginate/MC blend for cell embedding was evaluated by direct incorporation of mesenchymal stem cells during scaffold fabrication. The embedded cells showed high viability after 3 weeks of cultivation, which was similar to those of cells within pure alginate scaffolds which served as control. Maintenance of the differentiation potential of embedded cells, as an important requirement for the generation of functional tissue engineering constructs, was proven for adipogenic differentiation as a model for soft tissue formation. In conclusion, the temporary integration of MC into a low-concentrated alginate solution allowed the generation of scaffolds with dimensions in the range of centimetres without loss of the positive properties of low-concentrated alginate hydrogels with regard to cell embedding. Copyright © 2015 John Wiley & Sons, Ltd.