RESUMO
The role of bulk defects in the oxygen chemistry on reduced rutile TiO(2)(110)-(1 × 1) has been studied by means of temperature-programmed desorption spectroscopy and scanning tunneling microscopy measurements. Following O(2) adsorption at 130 K, the amount of O(2) desorbing at â¼410 K initially increased with increasing density of surface oxygen vacancies but decreased after further reduction of the TiO(2)(110) crystal. We explain these results by withdrawal of excess charge (Ti(3+)) from the TiO(2)(110) lattice to oxygen species on the surface and by a reaction of Ti interstitials with O adatoms upon heating. Important consequences for the understanding of the O(2)-TiO(2) interaction are discussed.
RESUMO
MoS2 nanoparticles are proven catalysts for processes such as hydrodesulfurization and hydrogen evolution, but unravelling their atomic-scale structure under catalytic working conditions has remained significantly challenging. Ambient pressure X-ray Photoelectron Spectroscopy (AP-XPS) allows us to follow in situ the formation of the catalytically relevant MoS2 edge sites in their active state. The XPS fingerprint is described by independent contributions to the Mo 3d core level spectrum whose relative intensity is sensitive to the thermodynamic conditions. Density Functional Theory (DFT) is used to model the triangular MoS2 particles on Au(111) and identify the particular sulphidation state of the edge sites. A consistent picture emerges in which the core level shifts for the edge Mo atoms evolve counterintuitively toward higher binding energies when the active edges are reduced. The shift is explained by a surprising alteration in the metallic character of the edge sites, which is a distinct spectroscopic signature of the MoS2 edges under working conditions.