Comparison of cracking activity of the core-shell composite MCM-41/HY & MCM-48/HY catalysts in the synthesis of organic liquid fuel from Mahua oil.

A synergistic catalyst was architectured using the hydrothermal crystallization method. Mesoporous material with pore diameter less than 20 nm was grown on the microporous Zeolite HY. The catalysts were characterized by XRD, ICP-OES, BET, TPD, SEM and TEM techniques. The SEM picture portrayed excellent core - shell morphology and TEM analysis corresponded to the XRD reports. Mahua oil was cracked in a pilot scale reactor over the synthesized catalysts at an optimized reaction condition (Temperature: 400 οC; WHSV: 4.6 h-1). The gaseous and liquid products of reaction were analyzed by Residual Gas analyzer and GCMS respectively. The NMR spectral analysis of fuel showed low traces of aromatics. The produced fuel was analyzed for its significant properties like calorific value, fire point, flash point and viscosity.

Microwave assisted biodiesel production from chicken feather meal oil using Bio-Nano Calcium oxide derived from chicken egg shell.

Environmental concerns have initiated the search for greener measures to mitigate pollution issues. Bio Nano CaO was synthesized by reducing CaO extracted from chicken egg shell using tea decoction. The synthesized material was characterized by physico-chemical techniques such as XRD, TGA, BET surface area analyser, TGA and SEM techniques. XRD studied confirmed the crystalline nature of material. The prepared material was found to be stable till 450 οC from TGA study. The SEM pictures displayed uniform and discrete particles which portrays the high probable sites that maximises the catalytic activity. The optimization of microwave assisted Biodiesel synthesis from chicken feather oil through Transesterification process using the bio-synthesized catalytic material was the main aim of the study. A 500 W microwave irradiation of Chicken feather meal oil using 8:1 Methanol:Oil input, 1% Bio Nano CaO concentration, 5 min of reaction time resulted in 95% conversion of chicken feather meal oil into chicken feather meal methyl esters. The Biodiesel was showed low viscosity (4.15 mm2/s), high heating value (50 MJ/kg), high flash point (153οC), reasonable pour point (12 οC) and good cetane number (50 min). The future works will be concentrated on the engine studies related to Torque, fuel consumption, emission data by using the synthesized Biodiesel.