RESUMO
Magnetoelastic dilatometry of the piezomagnetic antiferromagnet UO2 was performed via the fiber Bragg grating method in magnetic fields up to 150 T generated by a single-turn coil setup. We show that in microsecond timescales, pulsed-magnetic fields excite mechanical resonances at temperatures ranging from 10 to 300 K, in the paramagnetic as well as within the robust antiferromagnetic state of the material. These resonances, which are barely attenuated within the 100-µs observation window, are attributed to the strong magnetoelastic coupling in UO2 combined with the high crystalline quality of the single crystal samples. They compare well with mechanical resonances obtained by a resonant ultrasound technique and superimpose on the known nonmonotonic magnetostriction background. A clear phase shift of π in the lattice oscillations is observed in the antiferromagnetic state when the magnetic field overcomes the piezomagnetic switch field H[Formula: see text] T. We present a theoretical argument that explains this unexpected behavior as a result of the reversal of the antiferromagnetic order parameter at Hc.
RESUMO
We measure magnetic quantum oscillations in the underdoped cuprates YBa2Cu3O6+x with x=0.61, 0.69, using fields of up to 85 T. The quantum-oscillation frequencies and effective masses obtained suggest that the Fermi energy in the cuprates has a maximum at hole doping p approximately 0.11-0.12. On either side, the effective mass may diverge, possibly due to phase transitions associated with the T=0 limit of the metal-insulator crossover (low-p side), and the postulated topological transition from small to large Fermi surface close to optimal doping (high p side).
RESUMO
We explored high-field (60 T) magneto-resistance (MR) with two carbon nanotube (CNT) material classes: (1) unaligned single-wall CNTs (SWCNT) films with controlled metallic SWCNT concentrations and doping degree and (2) CNT fiber with aligned, long-length microstructure. All unaligned SWCNT films showed localized hopping transport where high-field MR saturation definitively supports spin polarization instead of a more prevalent wave function shrinking mechanism. Nitric acid exposure induced an insulator to metal transition and reduced the positive MR component. Aligned CNT fiber, already on the metal side of the insulator to metal transition, had positive MR without saturation and was assigned to classical MR involving electronic mobility. Subtracting high-field fits from the aligned fiber's MR yielded an unconfounded negative MR, which was assigned to weak localization. It is concluded that fluctuation induced tunnelling, an extrinsic transport model accounting for most of the aligned fiber's room temperature resistance, appears to lack MR field dependence.