RESUMO
This research aimed to evaluate the effect of adding different polymeric waste percentages and types on the physical, mechanical, thermal, and durability properties of soil-cement bricks. Tire and polyethylene terephthalate (PET) waste were evaluated at 1.5 and 3.0% (mass/mass). The soil was characterized in terms of shrinkage, compaction, consistency limits, particle size, and chemical analyses, whereas the waste particles were submitted to morphological characterization. The bricks were produced in an automatic press with a 90:10 (mass/mass) soil:cement ratio. The soil-cement bricks were characterized by density, moisture, water absorption, loss of mass by immersion, compressive strength, thermal conductivity, and microstructural analysis. PET waste stood out for its use as reinforcement in soil-cement bricks. The best performance was obtained for bricks reinforced with 1.5% PET, which showed a significant compressive strength improvement, meeting the marketing standards criteria, even after the durability test, as well as obtaining the lowest thermal conductivity values. The percentage increase from 1.5 to 3.0% fostered a significant water absorption and loss of mass increase, as well as a significant compressive strength reduction of the bricks.
Assuntos
Materiais de Construção , Solo , Força Compressiva , Materiais de Construção/análise , Polietilenotereftalatos , Condutividade TérmicaRESUMO
This study aimed to evaluate the effect of using expanded vermiculite and its impact on the production of concrete roof tiles. The control treatment and replacement of 12.5, 25, 37.5, and 50% sand by vermiculite were evaluated. The concrete roof tiles were moulded by the simultaneous pressing and extrusion mechanical process. The control trace was comprised by 21.95% CPV-ARI cement, 65.85% sand, and 12.20% limestone. After production, the concrete roof tiles were cured for 28 days. The physical (roof tiles classification, samples dry weight, water absorption, and porosity), mechanical (splitting tensile strength), and microstructural properties were evaluated. All treatments were assessed before and after accelerated ageing. The thermal properties of the modification in the concrete roof tiles' composition were also analysed. The evaluated amounts of vermiculite significantly affected the physical, mechanical, and thermal properties of concrete roof tiles. The use of vermiculite in concrete roof tiles reduced their dry weight and thermal conductivity, not impairing their durability. The use of 31.0% vermiculite in concrete roof tiles was suggested for better thermal insulation optimization (20.29% reduction) and weight reduction (7.92% and 7.94% at 28 days of curing and after accelerated ageing, respectively), along with adequate physical, mechanical, and durability properties.
Assuntos
Materiais de Construção , Areia , Silicatos de Alumínio , Materiais de Construção/análise , Condutividade TérmicaRESUMO
The need for environmental preservation requires civil engineering to reach new concepts and technical solutions aiming at the sustainability of its activities and products. In this context, this study aimed to evaluate the effect of using different types and percentages of vegetable particles on the physical, mechanical, and thermal properties of soil-cement bricks. Bamboo, rice husk, and coffee husk particles at 1.5 and 3% percentages and a control treatment not using the particle were evaluated. The chemical properties, shrinkage, compaction, consistency limits, and grain size were characterized for the soil; and the anatomical, chemical, and physical properties for the lignocellulosic particles. The bricks were produced using an automatic press and characterized after the curing process for density, water absorption, porosity, loss of mass by immersion, compressive strength, durability, and thermal conductivity. The increase in the lignocellulosic waste percentage caused a mechanical strength decrease and bricks' porosity and water absorption increase. However, it caused a decrease in density and an enhancement in loss of mass and thermal insulation properties. The bricks produced with rice husk obtained the best results in terms of mechanical and thermal properties, and were still among the best treatments for physical properties, standing out among the lignocellulosic waste as an alternative raw material source for soil-cement brick production.