BioPEGylation of polyhydroxyalkanoates: influence on properties and satellite-stem cell cycle.

The addition of poly(ethylene glycol), PEG, to bioprocessing systems producing polyhydroxyalkanoates (PHAs), has been reported as a means of their molecular weight control and can also support bioPEGylation, resulting in hybrids with amphiphillic properties. However, the study of such natural-synthetic hybrids of PHA-b-PEG is still in its infancy. In this study, we report the influence of bioPEGylation of polyhydroxyoctanoate (PHO) on its physiochemical, material, and biological properties. Consistent with previous studies, bioPEGylation with diethylene glycol (DEG) showed a significant reduction in PHA molecular weight (57%). In comparison to solvent cast films of PHO, PHO-b-DEG films possessed a noticeable X-ray diffraction peak at 9.82 degrees and increased Young's modulus of 11 Gpa (83%). Potential biocompatibility was investigated by measuring the early phase of apoptosis in myoblastic satellite-stem cells (C2C12). Comparative analysis of cell proliferation and progression in the presence of the mcl-PHA and its hybrid showed that the latter induced significant cell cycle progression: the first time a biomaterial has been shown to do so. Microtopographies of the film surfaces demonstrated that these differences were not due to changes in surface morphology; both polymers possessed average surface rugosities of 1.4 +/- 0.2 microm. However, a slight decrease in surface hydrophobicity (3.5 +/- 0.9 degrees) due to the hydrophilic DEG may have exerted an influence. The results support the further study of bioPEGylated PHAs as potential biomaterials in the field of tissue engineering.

Biosynthesis and characterization of deuterated polyhydroxyoctanoate.

The synthesis of a polyhydroxyalkanoate with medium chain length alkyl substituents by Pseudomonas oleovoranswas investigated using protonated and deuterated forms of octanoic acid in a minimal salts medium. Cultivation with deuterated octanoic acid resulted in a reduced rate of polymer accumulation compared to that with its protonated counterpart (107 and 207 mg of polymer L(-1) of medium h(-1) of cultivation, respectively). Nuclear magnetic resonance and gas chromatography coupled mass spectrometry of the derivatized polymer was used to establish the extent and distribution of deuterium in the biopolymer. A partially deuterated heteropolymer with 3-hydroxyoctanoic acid as the main constituent was produced. Deuteration is an important tool for contrast variation studies using neutron scattering, but predicates that the deuterated polymer is otherwise comparable in its physiochemical and material properties to its protonated counterpart. In studies reported here, the deuterated biopolymer exhibited an additional diffraction maximum at 7.55 A and slight differences in its melting point (60 and 55 degrees C) and glass transition temperature (-39 and -36 degrees C) when compared to its protonated equivalent. While significant differences between the protonated and deuterated biopolymers were determined, our results support the use of this deuterated polyhydroxyalkanoate in its application in investigations using analytical neutron scattering techniques.

Biosynthesis of natural-synthetic hybrid copolymers: polyhydroxyoctanoate-diethylene glycol.

A new natural-synthetic hybrid biomaterial has been isolated from the growth of Pseudomonas oleovorans in the presence of diethylene glycol (DEG). DEG was consumed by P. oleovorans with 20 mM sodium octanoate in modified E* medium, but its presence in the fermentation medium retarded cell growth and viability, influencing production and composition of polyhydroxyalkanoates with medium chain length substituents (mclPHAs) and consequently attenuating PHA yield. DEG affected the composition of the mclPHA with an increase in the C8 component: polyhydroxyoctanoate (PHO). Gas chromatography-mass spectrometry (GC-MS) was used to quantitatively monitor DEG in the system and reveal its cellular adsorption and penetration. Intracellularly, the DEG significantly reduced the molar mass of the mclPHA; PHO with a bimodal distribution of high and low molecular weight fractions was observed. 1H NMR, 2-D COSY, and heteronuclear single quantum coherence spectra confirmed that the high molecular weight fraction consisted of PHO chains terminated by DEG. Thus, the synthesis of this natural-synthetic hybrid copolymer, PHO-DEG, opens the way for microbial synthesis of a wide variety of PHA-DEG copolymers with a range of bioactive properties.