RESUMO
: Nanodrugs have in recent years been a subject of great debate. In 2017 alone, almost 50 nanodrugs were approved for clinical use worldwide. Despite the advantages related to nanodrugs/nanomedicine, there is still a lack of information regarding the biological safety, as the real behavior of these nanodrugs in the body. In order to better understand these aspects, in this study, we evaluated the effect of polylactic acid (PLA) nanoparticles (NPs) and magnetic core mesoporous silica nanoparticles (MMSN), of 1000 nm and 50 nm, respectively, on human cells. In this direction we evaluated the cell cycle, cytochemistry, proliferation and tubulogenesis on tumor cells lines: from melanoma (MV3), breast cancer (MCF-7, MDA-MB-213), glioma (U373MG), prostate (PC3), gastric (AGS) and colon adenocarcinoma (HT-29) and non-tumor cell lines: from human melanocyte (NGM), fibroblast (FGH) and endothelial (HUVEC), respectively. The data showed that an acute exposure to both, polymeric nanoparticles or MMSN, did not show any relevant toxic effects on neither tumor cells nor non-tumor cells, suggesting that although nanodrugs may present unrevealed aspects, under acute exposition to human cells they are harmless.
Assuntos
Nanopartículas/toxicidade , Ciclo Celular , Proliferação de Células , Óxido Ferroso-Férrico/química , Fibroblastos/metabolismo , Fibroblastos/fisiologia , Células HT29 , Células Endoteliais da Veia Umbilical Humana/metabolismo , Células Endoteliais da Veia Umbilical Humana/fisiologia , Humanos , Células MCF-7 , Nanopartículas/química , Poliésteres/química , Dióxido de Silício/químicaRESUMO
To evaluate the effect of incorporating niobium phosphate bioactive glass (NbG) into commercial etch-and-rinse adhesive systems, with and without silane, on their degree of conversion (DC) (%) and microtensile bond strength (µTBS). The NbG micro-filler was added to two etch-and-rinse adhesive systems: One Step (OS) and Prime & Bond (PB) at 40% concentration. The following groups were formed: control without glass addition OS; addition of unsilanized NbG (OSNbG); addition of silanized NbG (OSNbGS); control without glass PB; addition of unsilanized NbG (PBNbG); addition of silanized NbG (PBNbGS). The DC was determined using total Fourier spectroscopy reflection (FTIR/ATR). For µTBS testing, 48 human third molars (n=8) were restored and sliced to obtain specimens (0.8 mm2) and they were tested at two different time intervals: immediately and after 6 months. The fracture mode was evaluated with a stereoscopic loupe (40×) and by scanning electron microscopy (SEM). The data were subjected to ANOVA and Tukey tests (a=0.05). NbG addition did not compromise the adhesive system DC values (p>0.05). Furthermore, the NbG added to the adhesive systems did not affect µTBS values (p>0.05). Fracture occurred predominantly at the dentin-adhesive interface. NbG bioactive glass did not affect the DC or microtensile bond strength results.
Assuntos
Colagem Dentária , Nióbio/química , Fosfatos/química , Resistência à Tração , Cimentos Dentários , Análise do Estresse Dentário , Microscopia Eletrônica de Varredura , Espectroscopia de Infravermelho com Transformada de FourierRESUMO
Abstract To evaluate the effect of incorporating niobium phosphate bioactive glass (NbG) into commercial etch-and-rinse adhesive systems, with and without silane, on their degree of conversion (DC) (%) and microtensile bond strength (μTBS). The NbG micro-filler was added to two etch-and-rinse adhesive systems: One Step (OS) and Prime & Bond (PB) at 40% concentration. The following groups were formed: control without glass addition OS; addition of unsilanized NbG (OSNbG); addition of silanized NbG (OSNbGS); control without glass PB; addition of unsilanized NbG (PBNbG); addition of silanized NbG (PBNbGS). The DC was determined using total Fourier spectroscopy reflection (FTIR/ATR). For μTBS testing, 48 human third molars (n=8) were restored and sliced to obtain specimens (0.8 mm2) and they were tested at two different time intervals: immediately and after 6 months. The fracture mode was evaluated with a stereoscopic loupe (40×) and by scanning electron microscopy (SEM). The data were subjected to ANOVA and Tukey tests (a=0.05). NbG addition did not compromise the adhesive system DC values (p>0.05). Furthermore, the NbG added to the adhesive systems did not affect μTBS values (p>0.05). Fracture occurred predominantly at the dentin-adhesive interface. NbG bioactive glass did not affect the DC or microtensile bond strength results.
Resumo Avaliar o efeito da incorporação de vidro niobofosfato bioativo (NbG, 40% em peso) em dois sistemas adesivos simplificados convencionais (One Step [OS] e Prime & Bond {PB}) com e sem silano, no grau de conversão (%) e resistência de união (RU) após 6 meses. Os seguintes grupos foram testados: Controle OS: sem adição de partículas; OS e adição de NbG sem silano (OSNbG); OS e adição de partículas silanizadas NbG (OSNbGS); Controle PB: sem adição de partículas; PB e adição de partículas de NbG sem silano (PBNbG); PB e adição de partículas silanizadas NbG (PBNbGS). O grau de conversão (GC) foi determinado utilizando espectroscopia de Fourier (FTIR/ATR). Para RU, 48 terceiros molares humanos (n=8) foram restaurados e cortados para obter corpos-de-prova (0,8 mm2) e, em seguida, testados em dois momentos: imediato e após seis meses. O padrão de fratura foi avaliado com lupa estereoscópica (40×) e microscópio eletrônico de varredura (MEV). Os dados foram submetidos à análise de variância e Tukey (a=0,05). NbG não comprometeu valores de GC dos sistemas adesivos (p>0,05). Além disso, a adição de NbG aos sistemas adesivos não afetou os valores de RU (p>0,05). O padrão de fratura ocorreu predominantemente na interface dentina-adesivo. NbG não afetou os resultados de GC e RU.