Narrowband silicon waveguide Bragg reflector achieved by highly ordered graphene oxide gratings.

Graphene oxide (GO) ultrathin film can be wafer-scale deposited by spin coating, can be patterned by laser interference lithography and oxygen plasma etching, can be thinned atomically (0.26 nm/min) and oxidized by ozone treatment, and is a relatively transparent and low-refractive-index material compared to pristine graphene. All those unique properties prompt us to realize a low-loss (∼5 dB/cm), high-extinction-ratio (19 dB), and narrowband (0.425 nm) GO/silicon hybrid waveguide Bragg reflector by transferring 7-nm-thick GO gratings (n=1.58) atop a silicon strip waveguide. Unlike a sidewall-corrugated strip waveguide Bragg reflector that generally exhibits distorted corrugation profiles and is sensitive to fabrication errors, the as-realized GO-grating-covered strip waveguide Bragg reflector exhibits a stable reflecting wavelength and controllable reflection bandwidth that can be well predicted by numerical simulations.

Effective Synthesis of Highly Oxidized Graphene Oxide That Enables Wafer-scale Nanopatterning: Preformed Acidic Oxidizing Medium Approach.

Demand for rapid and massive-scale exfoliation of bulky graphite remains high in graphene commercialization and property manipulation. We report a procedure utilizing "preformed acidic oxidizing medium (PAOM)" as a modified version of the Hummers' method for fast and reliable synthesis of graphene oxide. Pre-mixing of KMnO4 and concentrated H2SO4 prior to the addition of graphite flakes enables the formation of effectively and efficiently oxidized graphene oxide (EEGO) featured by its high yields and suspension homogeneity. PAOM expedites diffusion of the Mn-oxidants into the graphite galleries, resulting in the rapid graphite oxidation, capable of oxidizing bulky graphite flakes (~0.8 mm in diameter) that can not be realized by the Hummers' method. In the scale-up tests, ten-time amount of graphite can be completely exfoliated by PAOM without need of extended reaction time. The remarkable suspension homogeneity of EEGO can be exploited to deposit ultra-flat coating for wafer-scale nanopatterning. We successfully fabricated GO optical gratings with well-defined periodicity (300 nm) and uniform thickness (variation <7 nm). The combination of the facile and potent PAOM approach with the wafer-scale patterning technique may realize the goal for massive throughput graphene nanoelectronics.