Study on the Polymer Morphology and Electro-Optical Performance of Acrylate/Epoxy Resin-Based Polymer-Stabilized Liquid Crystals Based on Stepwise Photopolymerization.

Stepwise photopolymerization is a miraculous strategy modulating the polymer skeleton and electro-optical properties of light modulators based on liquid crystal/polymer composites. However, owing to the indistinct polymerization mechanism and curing condition discrepancy, the required polymer structures and electro-optical properties are hard to be controlled precisely. Herein, a novel polymer-stabilized liquid crystal film based on acrylate/epoxy resin is proposed, fabricated and the relationships between preparation process, polymer content, polymer morphology and electro-optical properties are studied. The in-situ photopolymerization of acrylate/epoxy resin liquid crystalline polymer is fulfilled using cation photo-initiator UV 6976. The distinct photopolymerization speed between acrylate and epoxy resin benefits the polymer morphology control, and with accurate containment of the polymerization process and polymer composition, the superior electro-optical properties at a higher polymer content are acquired. The polymer morphology and electro-optical properties are influenced by the polymer content and mass ratio between acrylate and epoxy resin. The best electro-optical properties among samples are attained by controlling the mass ratio between acrylate and epoxy resin to 1:1, integrating higher densities of scattering centers and lower anchoring effect. With higher polymer content, the strategy of increasing the mass ratio of E6M benefits the improvement of E-O properties for alleviating polymer density. This work provides insights to stepwise polymerization of liquid crystalline monomers and offers a fancy strategy for the preparation of novel liquid crystal dimming films.

Reverse-Mode Polymer-Stabilized Liquid Crystal Films with Enhanced Peel Strength and Electro-Optical Performance Based on Photoreactive Self-Assembly Alignment Layers and Patterned Polymer Walls.

Polymer-stabilized liquid crystal (PSLC) is a promising material toward the practical application of serving as energy-saving reverse-mode smart windows owing to its superior electro-optical (E-O) properties, simple and efficient processability, and compatibility to most practical circumstances. However, its feeble peel strength originated from low polymer content and poor adhesion between polymer networks and substrates inhibited its large-scale flexible film production. It is still a challenging task to derive good mechanical properties and superior E-O performance for PSLCs at the same time. In this study, a highly durable liquid crystal/polymer composite film showing enhanced peel strength and excellent E-O properties was attained by simultaneously building photoreactive self-assemble alignment layers through an efficient one-step method and the sculpture of a patterned polymer wall structure. This film has comprehensive ascendant E-O properties of lower driving voltages, faster response times, and higher contrast ratio, together with an over 30 times lift of the peel strength. The effectuation mechanisms of the alignment, E-O properties, peel-strength, microstructures, and cyclic durability of the films have been systematically studied. This novel liquid crystal/polymer composite film demonstrates advantages in every aspect of performance compared to traditional PSLC devices, which hoards promising applications in smart windows for cars and buildings.