Temperature dependent low energy electron microscopy study of Ge island growth on bare and Ga terminated Si(112).

The pre-adsorption of Ga on Si(112) leads to a drastic change of the morphology of subsequently grown Ge islands. In contrast to the case for Ge growth on bare Si(112), even nanowire growth can be achieved on Ga terminated Si(112). Employing low energy electron microscopy and low energy electron diffraction, the initial phase of Ge nucleation and Ge island growth was systematically analysed for growth temperatures between 420 and 610 °C, both on clean and on Ga terminated Si(112). In both cases the island density exhibits an Arrhenius-like behaviour, from which diffusion barrier heights of about 1.3 and 1.0 eV can be estimated for growth with and without Ga pre-adsorption, respectively. The Ge island shape on the bare Si(112) surface is found to be nearly circular over the whole temperature range, whereas the shapes of the Ge islands on the Ga terminated Si(112) become highly anisotropic for higher temperatures. Ge nanowires with sizes of up to 2 µm along the [Formula: see text] direction are observed.