RESUMO
Fe-based superconductors exhibit a diverse interplay between charge, orbital, and magnetic ordering. Variations in atomic geometry affect electron hopping between Fe atoms and the Fermi surface topology, influencing magnetic frustration and the pairing strength through changes of orbital overlap and occupancies. Here, we experimentally demonstrate a systematic approach to realize superconductivity without chemical doping in BaFe2As2, employing geometric design within an epitaxial heterostructure. We control both tetragonality and orthorhombicity in BaFe2As2 through superlattice engineering, which we experimentally find to induce superconductivity when the As-Fe-As bond angle approaches that in a regular tetrahedron. This approach to superlattice design could lead to insights into low-dimensional superconductivity in Fe-based superconductors.
RESUMO
We obtain the through-thickness elastic stiffness coefficient (C33) in nominal 9 nm and 60 nm BaFe2As2 (Ba-122) thin films by using picosecond ultrasonics. Particularly, we reveal the increase in elastic stiffness as film thickness decreases from bulk value down to 9 nm, which we attribute to the increase in intrinsic strain near the film-substrate interface. Our density functional theory (DFT) calculations reproduce the observed acoustic oscillation frequencies well. In addition, temperature dependence of longitudinal acoustic (LA) phonon mode frequency for 9 nm Ba-122 thin film is reported. The frequency change is attributed to the change in Ba-122 orthorhombicity (a-b)/(a+b). This conclusion can be corroborated by our previous ultrafast ellipticity measurements in 9 nm Ba-122 thin film, which exhibit strong temperature dependence and indicate the structural phase transition temperature Ts.
RESUMO
Superconducting radio-frequency (SRF) resonator cavities provide extremely high quality factors > 1010 at 1-2 GHz and 2 K in large linear accelerators of high-energy particles. The maximum accelerating field of SRF cavities is limited by penetration of vortices into the superconductor. Present state-of-the-art Nb cavities can withstand up to 50 MV/m accelerating gradients and magnetic fields of 200-240 mT which destroy the low-dissipative Meissner state. Achieving higher accelerating gradients requires superconductors with higher thermodynamic critical fields, of which Nb3Sn has emerged as a leading material for the next generation accelerators. To overcome the problem of low vortex penetration field in Nb3Sn, it has been proposed to coat Nb cavities with thin film Nb3Sn multilayers with dielectric interlayers. Here, we report the growth and multi-technique characterization of stoichiometric Nb3Sn/Al2O3 multilayers with good superconducting and RF properties. We developed an adsorption-controlled growth process by co-sputtering Nb and Sn at high temperatures with a high overpressure of Sn. The cross-sectional scanning electron transmission microscope images show no interdiffusion between Al2O3 and Nb3Sn. Low-field RF measurements suggest that our multilayers have quality factor comparable with cavity-grade Nb at 4.2 K. These results provide a materials platform for the development and optimization of high-performance SIS multilayers which could overcome the intrinsic limits of the Nb cavity technology.