Multifunctional amorphous FeCoNiTixSi high-entropy alloys with excellent electromagnetic-wave absorption performances.

Amorphous high-entropy alloys (HEAs) as electromagnetic-wave absorbing materials have been rarely reported. In this work, amorphous FeCoNiTixSi HEAs were synthesized by introducing a high content of large-atom Ti using the high-energy ball-milling technique. This amorphous structure could improve the saturated magnetization and coercivity of HEAs, but slightly degraded the mechanical and oxidation resistance properties. In terms of electromagnetic properties, FeCoNiTi0.01Si and FeCoNiTiSi exhibit excellent electromagnetic-wave absorption performances, with significant absorptions of -68.4 dB at 6.14 GHz and -63.4 dB at 9.12 GHz, corresponding to bandwidths of 5.15 GHz (1.69 mm) and 3.64 GHz (1.43 mm), respectively. Overall, the prepared FeCoNiTixSi HEAs exhibited superior comprehensive performances compared to other HEA absorption materials. This work provided a novel strategy for the development of new electromagnetic-wave absorption materials with low weight, high absorption efficiency, and resistance to harsh environments.

Efficient and Homogeneous Carbonitriding of High-Entropy Alloys by a Mechanochemical Process for Obtaining Coordinated Electromagnetic Matching.

Optimizing the impedance matching via electromagnetic adjustment is considered an effective strategy to accomplish exceptional electromagnetic wave absorption (EMA) performance. Here, we report an efficient and green process to obtain the carbonitriding FeCoNiCr high-entropy alloys (HEAs) with flake-shaped morphology by using organic cyanide (Dicyandiamide, C2H4N4) as nitrogen and carbon sources. The carbonitriding effects on the phase structure, magnetic properties, mechanical hardness, corrosion resistance, high-temperature oxidation resistance, and EMA performances were investigated systematically. The carbonitriding process optimized the impedance match by decreasing the dielectric constant via introducing the nonmetallic C and N. The #CN10 sample exhibited outstanding EMA performances with a minimum reflection loss of -32.3 dB at 7.89 GHz and a broad effective bandwidth of 4.46 GHz, which covered the majority of X-band. In addition, the carbonitriding FeCoNiCr HEAs had great mechanical properties, excellent corrosion resistance, and high-temperature oxidation resistance, indicating excellent adaptability to harsh environments as well as good EMA performances. This work provides a new idea for the preparation and design of carbonitriding EMA materials.