Structural Health Monitoring with Sensor Data and Cosine Similarity for Multi-Damages.

There is a large risk of damage, triggered by harsh ocean environments, associated with offshore structures, so structural health monitoring plays an important role in preventing the occurrence of critical and global structural failure from such damage. However, obstacles, such as applicability in the field and increasing calculation costs with increasing structural complexity, remain for real-time structure monitoring offshore. Therefore, this study proposes the comparison of cosine similarity with sensor data to overcome such challenges. As the comparison target, this method uses the rate of changes of natural frequencies before and after the occurrence of various damage scenarios, including not only single but multiple damages, which are organized by the experiment technique design. The comparison method alerts to the occurrence of damage using a normalized warning index, which enables workers to manage the risk of damage. By comparison, moreover, the case most similar with the current status is directly figured out without any additional analysis between monitoring and damage identification, which renders the damage identification process simpler. Plus, the averaged rate of errors in detection is suggested to evaluate the damage level more precisely, if needed. Therefore, this method contributes to the application of real-time structural health monitoring for offshore structures by providing an approach to improve the usability of the proposed technique.

Interfacial Bond Properties of Underwater Concrete Coated with Bisphenol A Epoxy Resins.

This study investigated changes in the interfacial properties of epoxy-coated concrete exposed to various conditions, regarding the epoxy type, coating equipment, and exposure environment and period. The measured coating thickness and pull-off bond strength exhibited diverse trends, depending on the exposure period and conditions. In the real sea (RS) environment, the average bond strengths for bisphenol A (BPA) (E1), BPA with zinc powder (E2), and BPA with cresyl glycidyl ether (E3) were 1.26, 1.93, and 1.92 MPa, respectively. The coating method did not significantly affect the measured coating thickness and strength values. The conventional roller (D1) exhibited the highest thickness variation, with a value of 214.45 µm. The RS condition significantly increased the coating thickness (34% to 158%) compared to the tap water (TW) condition. The exposure conditions had little impact on bond strength except for E3, which showed an increased strength (2.71 MPa) over 7-91 days, especially under RS conditions, while E2 remained constant at approximately 1.82 MPa. This study offers insights into factors influencing marine concrete coating performance and discusses limitations and future work.

Effects of Water Exposure on the Interfacial Bond between an Epoxy Resin Coating and a Concrete Substrate.

Interfacial bond properties of six different epoxy resins used to coat submerged concrete structures were investigated. Test variables included coating type, coating equipment, and underwater curing time. Coating thickness and pull-off bond strength were measured using commercially available test equipment. Coating thickness and bond strength varied greatly depending on the manufacturer. The standard (control) coating equipment positively influenced the bond strength compared to other equipment. The effect of curing time on the bond properties was not significant within the range of 24 to 72 h. Lastly, some important considerations for the underwater coating of actual marine and coastal concrete structures were discussed, and suggestions for future research are presented.