Synthesis and Characterization of Novel Sprayed Ag-Doped Quaternary Cu2MgSnS4 Thin Film for Antibacterial Application.

In this work, the effects of silver doping with different Ag/(Ag + Cu) ratios (i.e., 2%, 5% and 10% at.% in the spray solution) on the structural, morphological, optical, electrical and antibacterial properties of Cu2MgSnS4 (CMTS) thin film grown by spray pyrolysis have been studied. The X-ray diffraction (XRD) and selected area electron diffraction (SAED) results have shown that the kesterite phase of CMTS thin films has a maximum crystallite size of about 19.60 nm for 5% Ag/(Ag + Cu). Scanning electron microscopy (SEM) images have shown spherical grain shapes. The transmission electron microscopy (TEM) and high-resolution TEM (HRTEM) microscopy observations confirmed the intrinsic reticular planes of CMTS thin film with (112) as a preferred orientation and interplanar spacing value of 3.1 Å. The optical properties showed high absorbance and an absorption coefficient of about 104 cm-1 in the visible region with an optical band gap energy of 1.51 eV. Impedance analysis spectroscopy demonstrated good electrical properties of the CMTS film obtained using 5% Ag/(Ag + Cu). The antibacterial activity of the undoped and Ag-doped particles of CMTS obtained using 5% Ag/(Ag + Cu) against different strains of pathogenic bacteria was tested using the agar well diffusion method. These results showed a significant antibacterial activity of the Ag-doped CMTS particle, which was much higher than the undoped CMTS particles. These experimental findings may open new practices for the Ag-doped CMTS compound, especially the one obtained using 5% Ag/(Ag + Cu), in antibacterial application.

Boosting Solar Cell Performance via Centrally Localized Ag in Solution-Processed Cu(In,Ga)(S,Se)2 Thin Film Solar Cells.

Fabrication of Cu(In,Ga)(S,Se)2 (CIGSSe) absorber films from environmentally friendly solutions under ambient air conditions for use in solar cells has shown promise for the low-cost mass production of CIGSSe solar cells. However, the limited power conversion efficiency (PCE) of these solar cells compared with their vacuum-processed counterparts has been a critical setback to their practical applications. This study aims to fabricate solution-processed CIGSSe solar cells with high PCEs by incorporation of Ag into the precursor layer of the CIGSSe absorber films. The results showed that Ag doping promoted grain growth by accelerating Se uptake, irrespective of the location within the CIGSSe film. Nevertheless, uniform Ag doping formed crevices that lowered the PCE of the cells, while centrally localizing the doped Ag prevented the formation of crevices, resulting in high PCEs up to 15.3%. Our results demonstrate that carefully doping Ag into a selected area of the precursor layer of the CIGSSe films can realize solution-processed chalcopyrite solar cells with high PCE.

Development of a novel functional core-shell-shell nanoparticles: From design to anti-bacterial applications.

This article reports the synthesis and functionalization of a novel CuO@SiO2-APTES@Ag0 core-shell-shell material using a simple and low-cost process. The growth, design strategies and synthesis approach are the key factors for the development of CuO@SiO2-APTES@Ag0 as efficient material with enhanced antibacterial activity. We investigated the morphology, surface charge, structure and stability of our new core-shell-shell by atomic force microscopy, scanning electron microscopy, energy dispersive X-ray, Fourier transform infrared and UV-visible spectroscopies, zeta potential measurements, and differential scanning calorimetry. The covalent surface grafting of APTES (3-(aminopropyl)triethoxysilane) onto CuO@SiO2 involving electrostatic interactions was confirmed. Size measurements and Scanning electron images showed that both APTES grafting and SiO2/Ag shells dropped on the surface of CuO produced structural compaction. UV-Vis spectroscopy proved to be a fast and convenient way to optically detect SiO2 shell on the surface of colloids. Additionally, the Ag-decorated CuO@SiO2-APTES surfaces were found to possess antibacterial activity and thermally more stable than undecorated surfaces. CuO@SiO2-APTES@Ag0 core-shell had antibacterial properties against Gram-positive bacteria making it a promising candidate for antibacterial applications.

Structural and Solar Cell Properties of a Ag-Containing Cu2ZnSnS4 Thin Film Derived from Spray Pyrolysis.

A silver (Ag)-incorporated kesterite Cu2ZnSnS4 (CZTS) thin film was fabricated by a facile spray pyrolysis method. Crystallographic analyses indicated successful incorporation of various amounts of Ag up to a Ag/(Ag + Cu) ratio of ca. 0.1 into the crystal lattice of CZTS in a homogeneous manner without formation of other impurity compounds. From the results of morphological investigations, Ag-incorporated films had larger crystal grains than the CZTS film. The sample with a relatively low Ag content (Ag/(Ag + Cu) of ca. 0.02) had a compact morphology without appreciable voids and pinholes. However, an increase in the Ag content in the CZTS film (Ag/(Ag + Cu) ca. 0.10) induced the formation of a large number of pinholes. As can be expected from these morphological properties, the best sunlight conversion efficiency was obtained by the solar cell based on the film with Ag/(Ag + Cu) of ca. 0.02. Electrostructural analyses of the devices suggested that the Ag-incorporated film in the device achieved reduction in the amounts of unfavorable copper on zinc antisite defects compared to the bare CZTS film. Moreover, the use of a Ag-incorporated film improved band alignment at the CdS(buffer)-CZTS interface. These alterations should also contribute to enhancement of device properties.