RESUMO
Spent bleaching clay, a solid waste generated during the refining process of vegetable oils, lacks an efficient treatment solution. In this study, spent bleaching clay was innovatively employed to fabricate ceramic foams. The thermal stability analysis, microstructure, and crystal phase composition of the ceramic foams were characterized by TG-DSC, SEM, and XRD. An investigation into the influence of Al2O3 content on the ceramic foams was conducted. Results showed that, as the Al2O3 content increased from 15 wt% to 30 wt%, there was a noticeable decrease in bulk density and linear shrinkage, accompanied by an increase in compressive strength. Additionally, the ceramic foams were used as catalyst supports, to synthesize ZSM-5@ceramic foam composite catalysts for pyrolysis of waste oil. The open pores of the ZSCF catalyst not only reduced diffusion path length but also facilitated the exposure of more acid sites, thereby increasing the utilization efficiency of ZSM-5 zeolite. This, in turn, engendered a significant enhancement in monocyclic aromatic hydrocarbons content from 39.15 % (ZSM-5 powder catalyst) to 78.96 %. Besides, a larger support pore size and a thicker ZSM-5 zeolite coating layer led to an increase in monocyclic aromatic hydrocarbons content. As the time on stream was extended to 56 min, the monocyclic aromatic hydrocarbon content obtained with the composite catalyst remained 12.41 % higher than that of the ZSM-5 powder catalyst. These findings validate the potential of the composite catalyst. In essence, this study advances the utilization of spent bleaching clay and introduces a novel concept for ceramic foam fabrication. Furthermore, it contributes to the scaling up of catalytic pyrolysis technology.