Paramagnetic Carbon Nanosheets with Random Hole Defects and Oxygenated Functional Groups.

Ordered graphitic carbon nanosheets (GCNs) were, for the first time, synthesized by the direct condensation of multifunctional phenylacetyl building blocks (monomers) in the presence of phosphorous pentoxide. The GCNs had highly ordered structures with random hole defects and oxygenated functional groups, showing paramagnetism. The results of combined structural and magnetic analyses indicate that the hole defects and functional groups are associated with the appearance and stabilization of unpaired spins. DFT calculations further suggest that the emergence of stabilized spin moments near the edge groups necessitates the presence of functionalized carbon atoms around the hole defects. That is, both hole defects and oxygenated functional groups are essential ingredients for the generation and stabilization of spins in GCNs.

Impact of Through-Hole Defects on the Electro-Explosive Properties of Exploding Foil Transducers.

This study examines the impact of surface defects on the electro-explosive properties of metal explosive foil transducers. Specifically, it focuses on the effects of defects in the bridge foil and their influence on the electrical explosion time and transduction efficiency. To analyze these effects, a current-voltage simulation model is developed to simulate the behavior of a defective bridge foil. The simulation results are validated through experimental current-voltage measurements at both ends of the bridge area. The findings reveal that the presence of through-hole defects on the surface of the bridge foil leads to an advancement in the electrical explosion time and a reduction in the transduction efficiency of the bridge foil. A performance comparison is made between the defective bridge foil and a defect-free copper foil. As observed, a through-hole defect with a radius of 20 µm results in a 1 ns advance in the blast time and a 1.52% decrease in energy conversion efficiency. Similarly, a through-hole defect with a radius of 50 µm causes a 51 ns advancement in the blast time and a 13.96% reduction in the energy conversion efficiency. These findings underscore the detrimental effects of surface defects on the electro-explosive properties, emphasizing the importance of minimizing defects to enhance their performance.

Magnetic Charge Model for Leakage Signals from Surface Defects in Ferromagnetic Material.

A novel three-dimensional theoretical model of magnetic flux leakage (MFL) is proposed in this paper based on the magnetic dipole model. The magnetic dipole model assumes that a ferromagnetic specimen with defects is exposed to a uniform external magnetic field that causes a uniform magnetization around the defect surface. Under this assumption, the MFL can be regarded as arising from magnetic charges on the defect surface. Previous theoretical models were mostly used to analyze simple crack defects such as cylindrical and rectangular cracks. In this paper, we developed a magnetic dipole model for more complex defect shapes such as circular truncated holes, conical holes, elliptical holes, and double-curve-shaped crack holes to complement the existing defect shapes. Experimental results and comparisons with previous models demonstrate that the proposed model provides a better approximation of complex defect shapes.

Carbon Material With Ordered Sub-Nanometer Hole Defects.

A holey carbon material with ordered sub-nanometer hole defects was synthesized from oxidative cyclodehydrogenation of a polyhexaphenylbenzene precursor. Band gap of around 2.2 eV is formed due to the narrow connection between the hexabenzocoronene subunits. It has weak interlayer interaction energy compared with graphene and shows easy dispersion in a wide range of solvents, surprisingly including water. Density functional theory calculations confirmd the excellent dispersion of this material in water. This new carbon material was then proved as effective support for various inorganic nanoparticles of small sizes. The supported iron nanoparticles showed enzyme-like catalysis behavior in nitrophenyl reduction reaction by NaBH4, exemplifying the great potential of this new material in catalysis.

Biocompatibility and osteoconduction of macroporous silk fibroin implants in cortical defects in sheep.

The goal of the presented study was to compare the biocompatibility and cellular responses to porous silk fibroin (SF) scaffolds produced in a water-based (UPW) or a solvent based process (HFIP) using two different SF sources. For that reason, four different SF scaffolds were implanted (n=6) into drill hole defects in the cancellous bone of the sheep tibia and humerus. The scaffolds were evaluated histologically for biocompatibility, cell-material interaction, and cellular ingrowth. New bone formation was observed macroscopically and histologically at 8 weeks after implantation. For semiquantitative evaluation, the investigated parameters were scored and statistically analyzed (factorial ANOVA). All implants showed good biocompatibility as evident by low infiltration of inflammatory cells and the absent encapsulation of the scaffolds in connective tissue. Multinuclear foreign body giant cells (MFGCs) and macrophages were present in all parts of the scaffold at the material surface and actively degrading the SF material. Cell ingrowth and vascularization were uniform across the scaffold. However, in HFIP scaffolds, local regions of void pores were present throughout the scaffold, probably due to the low pore interconnectivity in this scaffold type in contrast to UPW scaffolds. The amount of newly formed bone was very low in both scaffold types but was more abundant in the periphery than in the center of the scaffolds and for HFIP scaffolds mainly restricted to single pores.