RESUMO
High-nickel ternary materials are currently the most promising lithium battery cathode materials due to their development and application potential. Nevertheless, these materials encounter challenges like cation mixing, lattice oxygen loss, interfacial reactions, and microcracks. These issues are exacerbated at high voltages, compromising their cyclic stability and safety. In this study, we successfully prepared Nb5+-doped high-nickel ternary cathode materials via a high-temperature solid-phase method. We investigated the impact of Nb5+ doping on the microstructure and electrochemical properties of LiNi0.88Co0.05Mn0.07O2 ternary cathode materials by varying the amount of Nb2O5 added. The experimental results suggest that Nb5+ doping does not alter the crystal structure but modifies the particle morphology, yielding radially distributed, elongated, rod-like structures. This morphology effectively mitigates the anisotropic volume changes during cycling, thereby bolstering the material's cyclic stability. The material exhibits a discharge capacity of 224.4 mAh g-1 at 0.1C and 200.3 mAh g-1 at 1C, within a voltage range of 2.7 V-4.5 V. Following 100 cycles at 1C, the capacity retention rate maintains a high level of 92.9%, highlighting the material's remarkable capacity retention and cyclic stability under high-voltage conditions. The enhancement of cyclic stability is primarily due to the synergistic effects caused by Nb5+ doping. Nb5+ modifies the particle morphology, thereby mitigating the formation of microcracks. The formation of high-energy Nb-O bonds prevents oxygen precipitation at high voltages, minimizes the irreversibility of the H2-H3 phase transition, and thereby enhances the stability of the composite material at high voltages.
RESUMO
Nickel cobalt manganese ternary cathode materials are some of the most promising cathode materials in lithium-ion batteries, due to their high specific capacity, low cost, etc. However, they do have a few disadvantages, such as an unstable cycle performance and a poor rate performance. In this work, polyethylene oxide (PEO) with high ionic conductance and flexibility was utilized as a multifunctional binder to improve the electrochemical performance of LiNi0.6Co0.2Mn0.2O2 cathode materials. Scanning electron microscopy showed that the addition of PEO can greatly improve the adhesion of the electrode components and simultaneously enhance the integrity of the electrode. Thus, the PEO-based electrode (20 wt% PEO in PEO/PVDF) shows a high electronic conductivity of 19.8 S/cm, which is around 15,000 times that of the pristine PVDF-based electrode. Moreover, the PEO-based electrode exhibits better cycling stability and rate performance, i.e., the capacity increases from 131.1 mAh/g to 147.3 mAh/g at 2 C with 20 wt% PEO addition. Electrochemical impedance measurements further indicate that the addition of the PEO binder can reduce the electrode resistance and protect the LiNi0.6Co0.2Mn0.2O2 cathode materials from the liquid electrolyte attack. This work offers a simple yet effective method to improve the cycling performance of the ternary cathode materials by adding an appropriate amount of PEO as a binder in the electrode fabrication process.
RESUMO
To address increasingly prominent energy problems, lithium-ion batteries have been widely developed. The high-nickel type nickel-cobalt-manganese (NCM) ternary cathode material has attracted attention because of its high energy density, but it has problems such as cation mixing. To address these issues, it is necessary to start from the surface and interface of the cathode material, explore the mechanism underlying the material's structural change and the occurrence of side reactions, and propose corresponding optimization schemes. This article reviews the defects caused by cation mixing and energy bands in high-nickel NCM ternary cathode materials. This review discusses the reasons why the core-shell structure has become an optimized high-nickel ternary cathode material in recent years and the research progress of core-shell materials. The synthesis method of high-nickel NCM ternary cathode material is summarized. A good theoretical basis for future experimental exploration is provided.