Physisorbed water layer formation on fully hydroxylated mesoporous silicas.
J Colloid Interface Sci
; 291(2): 353-60, 2005 Nov 15.
Article
em En
| MEDLINE
| ID: mdl-15996677
ABSTRACT
Kinetic adsorption isotherms were obtained by gravimetric determination of water adsorption into fully hydroxylated mesoporous silicas using samples exposed to controlled humidity air at 22+/-2 degrees C. Twenty kinetic isotherms at several relative humidities (11, 33, 43, 51, 75, and 85%) were obtained with 11 different batches of silica using this simple procedure to obtain quantitative information on the formation of H2O adsorbates. The H2O surface concentrations obtained from the plateau data of individual kinetic adsorption isotherms at 43 and 51% RH, typically precise to about +/-1%, show that a complete monolayer is formed with negligible second-layer adsorption at these relative humidities. This monolayer has a surface concentration of 7.68+/-0.30 micromol H2O/m2, which is lower than the quasi-equilibrium concentration at these relative humidities obtained by the conventional equilibrium-isotherm procedure. Comparison with the Kiselev-Zhuravlev concentration of silanol groups on fully hydroxylated silicas (7.6+/-0.8 micromol SiOH/m2) confirms 11 H2OSiOH stoichiometry of this monolayer. The presence of partial-layer structures at 2.85+/-0.1 and 5.7+/-0.1 micromol H2O/m2 is suggested by isotherms at 11 and 33% RH, respectively, while a bilayer at approximately 14+/-1 micromol H2O/m2 is suggested by kinetic isotherms at 75 and 85% RH.
Buscar no Google
Coleções:
01-internacional
Base de dados:
MEDLINE
Idioma:
En
Revista:
J Colloid Interface Sci
Ano de publicação:
2005
Tipo de documento:
Article
País de afiliação:
Brasil