Influence of Oxygen Gas Ratio on the Properties of Aluminum-Doped Zinc Oxide Films Prepared by Radio Frequency Magnetron Sputtering.
J Nanosci Nanotechnol
; 16(5): 5138-42, 2016 May.
Article
em En
| MEDLINE
| ID: mdl-27483888
ABSTRACT
Aluminum-doped zinc oxide (AZO) thin films were deposited on glass and polyimide substrates using radio frequency magnetron sputtering. We investigated the effects of the oxygen gas ratio on the properties of the AZO films for Cu(In,Ga)Se2 thin-film solar cell applications. The structural and optical properties of the AZO thin films were measured using X-ray diffraction (XRD), field emission scanning electron microscope (FE-SEM), and UV-Visible-NIR spectrophotometry. The oxygen gas ratio played a crucial role in controlling the optical as well as electrical properties of the films. When oxygen gas was added into the film, the surface AZO thin films became smoother and the grains were enlarged while the preferred orientation changed from (0 0 2) to (1 0 0) plane direction of the hexagonal phase. An improvement in the transmittance of the AZO thin films was achieved with the addition of 2.5-% oxygen gas. The electrical resistivity was highly increased even for a small amount of the oxygen gas addition.
Buscar no Google
Coleções:
01-internacional
Base de dados:
MEDLINE
Idioma:
En
Revista:
J Nanosci Nanotechnol
Ano de publicação:
2016
Tipo de documento:
Article