The effect of various bases on the fracture resistance of amalgam.
Oper Dent
; 19(6): 211-6, 1994.
Article
em En
| MEDLINE
| ID: mdl-9028239
ABSTRACT
UNLABELLED This study compared the compressive force required to fracture amalgam over nine base materials a calcium hydroxide product (Dycal); two autocured glass ionomers (GlasIonomer Base Cement and Ketac-Bond); three light-cured glass ionomers (Photac-Bond, Variglass VLC, and Vitrebond); two light-cured resins (Timeline and VLC Dycal); and a zinc phosphate cement (Fleck's Zinc Cement). For the control group, 10 aluminum dies (25 mm x 12 mm x 10 mm) were milled with 3.0 mm x 3.0 mm slots, which were filled with hand-condensed Tytin amalgam with no underlying base. For experimental groups, 10 aluminum dies of equal dimension were milled with 3.5 mm x 3.0 mm slots. Following manufacturer's instructions, the nine base materials were successively placed in these 10 dies using a depth-limiting device made of light-transmitting clear acrylic to ensure a 0.5 mm thickness, and Tytin amalgam was again condensed over each base such that the depth of the amalgam equalled that in the control. All test specimens were stored in 100% humidity for 48 hours then fractured in compression on an Instron machine. Mean force, in Newtons (S D in parentheses), required to fracture the specimens was CONTROL 1934(210), Zinc Cement 1874(147), GlasIonomer Base Cement 1839(174), Ketac-Bond 1723(225), Vitrebond 1485(155), Photac-Bond 1422(294), Advanced Formula II Dycal 1296(237), VLC Dycal 1035(116), Variglass 909(294) and Timeline 906(275). ANOVA and Student-Newman-Keuls statistical analysis (alpha = 0.05) indicated that the autocuring glass ionomers, GlasIonomer Base Cement and Ketac-Bond, and a zinc phosphate cement, Zinc Cement, provided significantly more fracture resistance for amalgam than the other bases tested and were not statistically different from a no-base control.
Buscar no Google
Coleções:
01-internacional
Base de dados:
MEDLINE
Assunto principal:
Amálgama Dentário
/
Forramento da Cavidade Dentária
Idioma:
En
Revista:
Oper Dent
Ano de publicação:
1994
Tipo de documento:
Article
País de afiliação:
Estados Unidos