We present an effective method for direct fiber coupling of a quantum dot (QD) that is deterministically incorporated into a cylindrical mesa. For precise positioning of the fiber with respect to the QD-mesa, we use a scanning procedure relying on interference of light reflected back from the fiber end-face and the top surface of the mesa, applicable for both single-mode and multi-mode fibers. The central part of the fiber end-face is etched to control the required distance between the top surface of the mesa and the fiber core. Emission around 1260â nm from a fiber-coupled InGaAs/GaAs QD is demonstrated and its stability is proven over multiple cooling cycles. Moreover, a single photon character of emission from such system for a line emitting above 1200â nm is proven experimentally by photon autocorrelation measurements with an obtained value of the second order correlation function at zero time-delay well below 0.5.
RESUMEN
Zinc gallate (ZnGa2O4) spinel ceramics doped with Mn2+ ions was prepared by a solid-state reaction at 1200 °C in air. Manganese concentration was equal to 0.05 mol.% of MnO with respect to ZnO. Ceramics produced in this way show an efficient green emission at about 505 nm under UV or X-ray excitations, which is caused by Mn2+ ions. This green emission is observed also as a relatively long afterglow (visible to the naked eye in the dark for about one hour) after switching-off the X-ray excitation. Time profiles of the beginning of glow and afterglow have been studied together with thermally stimulated (TSL) and optically stimulated (OSL) luminescence. Experimental results demonstrate a presence of few types of shallow and deep traps responsible for the observed afterglow and TSL/OSL emission of the material. The possibility of pulsed optical stimulation and time-resolved OSL characteristics of ZnGa2O4: Mn2+ has been reported for the first time. The presented results suggest the ZnGa2O4: Mn2+ spinel as a promising material for further fundamental research and possibility of application as a green long-lasting phosphor or storage phosphor for TSL/OSL radiation dosimetry.