Characterization of various acrylate based artificial teeth for denture fabrication.

Acrylic resins-based artificial teeth are frequently used for the fabrication of dentures has and contribute a very strong share in the global market. However, the scientific literature reporting the comparative analysis data of various artificial teeth is scarce. Focusing on that, the present study investigated various types of commercially available artificial teeth, composed of polymethyl methacrylate (PMMA). Artificial teeth are characterized for chemical analysis, morphological features, thermal analysis, and mechanical properties (surface hardness, compressive strength). Different types of artificial teeth showed distinct mechanical (compression strength, Vickers hardness) and thermal properties (thermal gravimetric analysis) which may be attributed to the difference in the content of PMMA and type and quantity of different fillers in their composition. Thermogravimetric analysis (TGA) results exhibited that vinyl end groups of PMMA degraded above 200 °C, whereas 340-400 °C maximum degradation temperature was measured by differential thermal analysis (DTA) for all samples. Crisma brand showed the highest compressive strength and young modulus (88.6 MPa and 1654 MPa) while the lowest value of Vickers hardness was demonstrated by Pigeon and Vital brands. Scanning electron microscope (SEM) photographs showed that Crisma, Pigeon, and Vital exhibited characteristics of a brittle fracture; however, Artis and Well bite brands contained elongated voids on their surfaces. According to the mechanical analysis and SEM data, Well bite teeth showed a significantly higher mechanical strength compared to other groups. However, no considerable difference was observed in Vickers hardness of all groups. Graphical abstract.

Mechanical and antibacterial properties of conventional pit and fissure sealants with addition of miswak fibers.

The occlusal surface of a tooth is affected by the development of biofilm in pits and fissures as bacteria and food particles accumulate in its complex structure. In this study, miswak fibers containing cellulose and antimicrobial extract were incorporated in commercial pit and fissure sealants. The miswak powder was characterized by different analytical techniques. The powder was mixed in different ratios (0-5%) into a pit and fissure sealant to result in five sealants (Groups 0-5), and their mechanical properties i.e. flexural strength, compressive strength, and Vickers hardness were evaluated. The sealants were also evaluated against streptococcus mutans oral pathogenic bacteria. SEM analysis confirmed irregular shape and micron-size particles of miswak powder. The infrared spectral analysis and X-ray differential peaks showed characteristic peaks related to miswak fibers. The particle appearance increased in prepared pits and fissure sealants with higher loading of miswak powder in SEM analysis. The flexural strength, compressive strength, and Vickers hardness values were obtained in the range of 148-221 (±16.6: p-value < 0.001) MPa, 43.1-50.3 MPa (±1.7: p-value <0.001), and 15.2-21.26 VHN (±0.56: p-value <0.001) for control and prepared sealant specimens respectively. In the antibacterial study, the zone of inhibitions increased with increased content of miswak from 15.6 ± 0.45 mm (Group 1) to 20.3 ± 0.32 mm (Group 5). The MIC was calculated to be 0.039%. The prepared experimental sealant had acceptable mechanical and good antibacterial properties therefore it could be recommended as an efficient pit and fissure sealant.

Effect of Ionic Liquids on Mechanical, Physical, and Antifungal Properties and Biocompatibility of a Soft Denture Lining Material.

This study aims to evaluate the effect of ionic liquids and their structure on the mechanical (tensile bond strength (TBS) and Shore A hardness), mass change, and antifungal properties of soft denture lining material. Butyl pyridinium chloride (BPCL) and octyl pyridinium chloride (OPCL) were synthesized, characterized, and mixed in concentrations ranging from 0.65-10% w/w with a soft denture liner (Molloplast-B) and were divided into seven groups (C, BPCL1-3, and OPCL1-3). The TBS of bar-shaped specimens was calculated on a Universal Testing Machine. For Shore A hardness, disc-shaped specimens were analyzed using a durometer. The mass change (%) of specimens was calculated by the weight loss method. The antifungal potential of ionic liquids and test specimens was measured using agar well and disc diffusion methods (p ≤ 0.05). The alamarBlue assay was performed to assess the biocompatibility of the samples. The mean TBS values of Molloplast-B samples were significantly lower (p ≤ 0.05) for all groups except for OPCL1. Compared with the control, the mean shore A hardness values were significantly higher (p ≤ 0.05) for samples in groups BPCL 2 and 3. After 6 weeks, the OPCL samples showed a significantly lower (p ≤ 0.05) mass change as compared to the control. Agar well diffusion methods demonstrated a maximum zone of inhibition for 2.5% OPCL (20.5 ± 0.05 mm) after 24 h. Disc diffusion methods showed no zones of inhibition. The biocompatibility of the ionic liquid-modified sample was comparable to that of the control. The addition of ionic liquids in Molloplast-B improved the liner's surface texture, increased its hardness, and decreased its % mass change and tensile strength. Ionic liquids exhibited potent antifungal activity.

Dental Composites with Calcium / Strontium Phosphates and Polylysine.

PURPOSE: This study developed light cured dental composites with added monocalcium phosphate monohydrate (MCPM), tristrontium phosphate (TSrP) and antimicrobial polylysine (PLS). The aim was to produce composites that have enhanced water sorption induced expansion, can promote apatite precipitation and release polylysine. MATERIALS AND METHODS: Experimental composite formulations consisted of light activated dimethacrylate monomers combined with 80 wt% powder. The powder phase contained a dental glass with and without PLS (2.5 wt%) and/or reactive phosphate fillers (15 wt% TSrP and 10 wt% MCPM). The commercial composite, Z250, was used as a control. Monomer conversion and calculated polymerization shrinkage were assessed using FTIR. Subsequent mass or volume changes in water versus simulated body fluid (SBF) were quantified using gravimetric studies. These were used, along with Raman and SEM, to assess apatite precipitation on the composite surface. PLS release was determined using UV spectroscopy. Furthermore, biaxial flexural strengths after 24 hours of SBF immersion were obtained. RESULTS: Monomer conversion of the composites decreased upon the addition of phosphate fillers (from 76 to 64%) but was always higher than that of Z250 (54%). Phosphate addition increased water sorption induced expansion from 2 to 4% helping to balance the calculated polymerization shrinkage of ~ 3.4%. Phosphate addition promoted apatite precipitation from SBF. Polylysine increased the apatite layer thickness from ~ 10 to 20 µm after 4 weeks. The novel composites showed a burst release of PLS (3.7%) followed by diffusion-controlled release irrespective of phosphate addition. PLS and phosphates decreased strength from 154 MPa on average by 17% and 18%, respectively. All formulations, however, had greater strength than the ISO 4049 requirement of > 80 MPa. CONCLUSION: The addition of MCPM with TSrP promoted hygroscopic expansion, and apatite formation. These properties are expected to help compensate polymerization shrinkage and help remineralize demineralized dentin. Polylysine can be released from the composites at early time. This may kill residual bacteria.