RESUMEN
The effect of Mn on interfacial Sn segregation during the selective oxidation of Fe-(0-10)Mn-0.03Sn (at.%) alloys was determined for annealing conditions compatible with continuous galvanizing. Significant Sn enrichment was observed at the substrate free surface and metal/oxide interface for all annealing conditions and Mn levels. Sn enrichment at the free surface was insensitive to the Mn alloy concentration, which was partially attributed to the opposing effects of Mn on segregation thermodynamics and kinetics: Mn increases the driving force for Sn segregation via reducing Sn solubility in Fe but also reduces the effective Sn diffusivity by increasing the austenite volume fraction. This insensitivity was exacerbated by the depletion of solute Mn near the surface due to the selective oxidation of Mn. Thus, Sn segregation occurred in regions with a local Mn concentration lower than the nominal bulk composition of the alloys suggested. Sn enrichment at the metal/external oxide interface was reduced compared to the free surface and decreased with increasing bulk Mn content, which was attributed to changes in the external oxide morphology and metal/internal oxide interfaces acting as Sn sinks.
RESUMEN
Process maps were developed using a combination of microstructural analysis and DICTRA-based modeling to predict the austenite vol.% as a function of the intercritical annealing parameters and starting microstructure. The maps revealed a strong dependence of the calculated austenite fraction (vol.%) on the Mn content (4-12 wt.%) and intercritical annealing temperatures (600 °C to 740 °C). The calculations were carried out for constant carbon, Al, and Si contents of 0.2 wt.%, 1.5 wt.%, and 1.0 wt.%, respectively. A modified empirical equation proposed by Koistinen and Marburger was employed to calculate the room-temperature retained austenite vol.% as a function of the intercritical annealing temperature, including the effect of the austenite composition. The process maps offer valuable insights for designing intercritical treatments of medium-Mn steels, aiding in the optimization of steel properties for automotive applications.