RESUMEN
Structural flexibility is an intrinsic feature of zeolites, and the characterization of such dynamic behavior is key to maximizing their performance and realizing their potential in both existing and emerging applications. Here, the flexibility of a high-aluminum nano-sized RHO zeolite is directly visualized with in situ TEM for the first time. Variable temperature experiments directly observe the physical expansion of the discrete nanocrystals in response to changes in both guest-molecule chemistry (Ar vs CO2) and temperature. The observations are complemented by operando FTIR spectroscopy verifying the nature of the adsorbed CO2 within the pore network, the desorption kinetics of carbonate species, and changes to the structural bands at high temperatures. Quantum chemical modeling of the RHO zeolite structure substantiates the effect of cation (Na+ and Cs+) mobility in the absence and presence of CO2 on the flexibility behavior of the structure. The results demonstrate the combined influences of temperature and CO2 on the structural flexibility consistent with the experimental microscopy observations.
RESUMEN
Zeolites with uniform micropores are important shape-selective catalysts. However, the external acid sites of zeolites have a negative impact on shape-selective catalysis, and the microporosity may lead to serious diffusion limitation. Herein, we report on the direct synthesis of hierarchical hollow STW-type zeolite single crystals with a siliceous exterior. In an alkalinous fluoride medium, the nucleation of highly siliceous STW zeolites takes place first, and the nanocrystals are preferentially aligned on the outer surface of the gel agglomerates to grow into single crystalline shells upon crystallization. The lagged crystallization of the internal Al-rich amorphous gels onto the inner surface of nanocrystalline zeolite shells leads to the formation of hollow cavities in the core of the zeolite crystals. The hollow zeolite single crystals possess a low-to-high aluminum gradient from the surface to the core, resulting in an intrinsic inert external surface, and exhibit superior catalytic performance in toluene methylation reactions.
RESUMEN
The identification of acid and nonacid species at the external surface of zeolites remains a major challenge, in contrast to the extensively-studied internal acid sites. Here, it is shown that the synthesis of zeolite ZSM-5 samples with distinct particle sizes, combined with solid-state NMR and computational studies of trimethylphosphine oxide (TMPO) adsorption, provides insight into the chemical species on the external surface of the zeolite crystals. 1 H-31 P HETCOR NMR spectra of TMPO-loaded zeolites exhibit a broad correlation peak at δP â¼35-55â ppm and δH â¼5-12â ppm assigned to external SiOH species. Pore-mouth Brønsted acid sites exhibit 31 P and 1 H NMR resonances and adsorption energies close to those reported for internal acid sites interacting with TMPO. The presence of an external tricoordinate Al-Lewis site interacting strongly with TMPO is suggested, resulting in 31 P resonances that overlap with the peaks usually ascribed to the interaction of TMPO with Brønsted sites.
Asunto(s)
Zeolitas , Zeolitas/química , Espectroscopía de Resonancia Magnética/métodos , Imagen por Resonancia Magnética , Ácidos/químicaRESUMEN
The mesopores formation in zeolite crystals has long been considered to occur through the stochastic hydrolysis and removal of framework atoms. Here, we investigate the NH4 F etching of representative small, medium, and large pore zeolites and show that the zeolite dissolution behavior, therefore the mesopore formation probability, is dominated by zeolite architecture at both nano- and sub-nano scales. At the nano-scale, the hidden mosaics of zeolite structure predetermine the spatio-temporal dissolution of the framework, hence the size, shape, location, and orientation of the mesopores. At the sub-nano scale, the intrinsic micropore size and connectivity jointly determine the diffusivity of reactant and dissolved products. As a result, the dissolution propensity varies from removing small framework fragments to consuming nanodomains and up to full digestion of the outmost part of zeolite crystals. The new knowledge will lead to new understanding of zeolite dissolution behavior and new adapted strategies for tailoring hierarchical zeolites.
RESUMEN
The preparation of defect-free MFI crystals containing single-site framework Mo through a hydrothermal postsynthesis treatment is reported. The insertion of single Mo sites in the MFI zeolite samples with different crystal sizes of 100, 200, and 2000 nm presenting a diverse concentration of silanol groups is revealed. The nature of the silanols and their role in the incorporation of Mo into the zeolite structure are elucidated through an extensive spectroscopic characterization (29Si NMR, 1H NMR, 31P NMR, and IR) combined with X-ray diffraction and HRTEM. In addition, a DFT-based theoretical modeling of a large Si154O354H92 nanoparticle containing 600 atoms is carried out to understand the expansion of the unit cell volume measured by X-ray diffraction. An accurate quantification of the silanols in the MFI crystals with different particle sizes and the insertion of Mo in the zeolitic framework is reported for the first time. The results confirmed that the non-H-bonded silanols seem to be the gateway for the insertion of single Mo atoms in the zeolite structure. Such materials with single metal sites present high crystallinity and perfect structure, thus providing great stability in catalytic applications.
RESUMEN
Zeolites have been game-changing materials in oil refining and petrochemistry over the last 60 years and have the potential to play the same role in the emerging processes of the energy and environmental transition. Although zeolites are crystalline inorganic solids, their structures are not perfect and the presence of defect sites - mainly Brønsted acid sites and silanols - influences their thermal and chemical resistance as well as their performances in key areas such as catalysis, gas and liquid separations and ion-exchange. In this paper, we review the type of defects in zeolites and the characterization techniques used for their identification and quantification with the focus on diffraction, spectroscopic and modeling approaches. More specifically, throughout the review, we will focus on silanol (Si-OH) defects located within the micropore structure and/or on the external surface of zeolites. The main approaches applied to engineer and heal defects and their consequences on the properties and applications of zeolites in catalysis and separation processes are highlighted. Finally, the challenges and opportunities of silanol defect engineering in tuning the properties of zeolites to meet the requirements for specific applications are presented.
RESUMEN
Crystalline porous materials (CPMs) with uniform and regular pore systems show great potential for separation applications using membrane technology. Along with the research on the synthesis of precisely engineered porous structures, significant attention has been paid to the practical application of these materials for preparation of crystalline porous membranes (CPMBs). In this review, the progress made in the preparation of thin, large area and defect-free CPMBs using classical and novel porous materials and processing is presented. The current state-of-the-art of scalable CPMBs with different nodes (inorganic, organic and hybrid) and various linking bonds (covalent, coordination, and hydrogen bonds) is revealed. The advances made in the scalable production of high-performance crystalline porous membranes are categorized according to the strategies adapted from polymer membranes (interfacial assembly, solution-casting, melt extrusion and polymerization of CPMs) and tailored based on CPM properties (seeding-secondary growth, conversion of precursors, electrodeposition and chemical vapor deposition). The strategies are compared and ranked based on their scalability and cost. The potential applications of CPMBs have been concisely summarized. Finally, the performance and challenges in the preparation of scalable CPMBs with emphasis on their sustainability are presented.
RESUMEN
Offretite zeolite synthesis in the presence of cetyltrimethylammonium bromide (CTABr) is reported. The offretite crystals were synthesized with a high crystallinity and hexagonal prismatic shape after only 72 h of hydrothermal treatment at 180 °C. The CTABr has dual-functions during the crystallization of offretite, viz. as structure-directing agent and as mesoporogen. The resulting offretite crystals, with a Si/Al ratio of 4.1, possess more acid sites than the conventional offretite due to their high crystallinity and hierarchical structure. The synthesized offretite is also more reactive than its conventional counterpart in the acylation of 2-methylfuran for biofuel production under non-microwave instant heating condition, giving 83.5% conversion with 100% selectivity to the desired product 2-acetyl-5-methylfuran. Hence, this amphiphile synthesis approach offers another cost-effective and alternative route for crystallizing zeolite materials that require expensive organic templates.
RESUMEN
Zeoliteâ Y and its ultra-stabilized hierarchical derivative (USY) are the most widely used zeolite-based heterogeneous catalysts in oil refining, petrochemisty, and other chemicals manufacturing. After almost 60â years of academic and industrial research, their resilience is unique as no other catalyst displaced them from key processes such as FCC and hydrocracking. The present study highlights the key difference leading to the exceptional catalytic performance of USY versus the parent zeoliteâ Y in a multi-technique study combining advanced spectroscopies (IR and solid-state NMR) and molecular modeling. The results highlight a hitherto unreported proton transfer involving inaccessible active sites in sodalite cages that contributes to the exceptional catalytic performance of USY.
RESUMEN
Green and efficient synthesis of titanium-containing molecular sieves is limited by the quantity of environmentally unfriendly additives and complicated synthesis procedures required. Oligomerization of Ti monomers into anatase TiO2 is the typical outcome of such procedures because of a mismatch between hydrolysis rates of Si and Ti precursors. We report a simple and generic additive-free route for the synthesis of Ti-containing molecular sieves (MFI, MEL, and BEA). This approach successfully reverses the formation of Ti oligomers to match hydrolysis rates of Ti and Si species with the assistance of hydroxyl free radicals generated inâ situ from ultraviolet irradiation. Moreover, fantastic catalytic performance for propene epoxidation with H2 and O2 was observed. Compared with the conventional hydrothermal method, this approach opens up new opportunities for high-efficiency, environmentally benign, and facile production of pure titanium-containing molecular sieves.
RESUMEN
Silver cations were introduced in nanosized BEA-type zeolite containing organic template by ion-exchange followed by chemical reduction towards preparation of photoactive materials (Ag0 -BEA). The stabilization of highly dispersed Ag0 nanoparticles with a size of 1-2â nm in the BEA zeolite was revealed. The transient optical response of the Ag-BEA samples upon photoexcitation at 400â nm was studied by femtosecond absorption. The photodynamic of the hot electrons was found to depend on the sample preparation. The lifetime of the hot electrons in the Ag-BEA samples containing small Ag nanoparticles (1-2â nm) is significantly shortened in comparison to bear Ag nanoparticles with a size of 10â nm. While for the larger Ag nanoparticles, the energy absorbed in the conduction band is decaying by electron-phonon coupling into the metal lattice, the high surface-to-volume ratio of the small Ag nanoparticles favors the dissipation of the energy of the hot electrons from the metal nanoparticles (Ag0 ) towards the zeolitic micro-environment. This finding is encouraging for further applications of Ag-containing zeolites in photocatalysis and plasmonic chemistry.
RESUMEN
We outline two methodologies to selectively characterize the Brønsted acidity of the external surface of FAU-type zeolites by IR and NMR spectroscopy of adsorbed basic probe molecules. The challenge and goal are to develop reliable and quantitative IR and NMR methodologies to investigate the accessibility of acidic sites in the large pore FAU-type zeolite Y and its mesoporous derivatives often referred to as ultra-stable Y (USY). The accessibility of their Brønsted acid sites to probe molecules (n-alkylamines, n-alkylpyridines, n-alkylphosphine- and phenylphosphine-oxides) of different molecular sizes is quantitatively monitored either by IR or 31 P NMR spectroscopy. It is now possible, for the first time to quantitatively discriminate between the Brønsted acidity located in the microporosity and on the external surface of large pore zeolites. For instance, the number of external acid sites on a Y (LZY-64) zeolite represents 2 % of its total acid sites while that of a USY (CBV760) represents 4 % while the latter has a much lower framework Si/Al ratio.
RESUMEN
The O2 and CO2 sorption properties of nanosized zeolite X with faujasite type structure through a partial ionic exchange of sodium (Na+) by trivalent cations (Gd3+ and Ce3+) were evaluated. Three faujasite samples were studied, the as-synthesized Na-X possessing Na+ solely, and the modified samples Na-Gd-X and Na-Ce-X containing Gd3+ (1.8 wt%) and Ce3+ (0.82 wt%), respectively. Incorporating scarce amounts of trivalent cations modified the adsorption affinity of zeolites towards O2 and CO2 as demonstrated by in situ Fourier-transform infrared spectroscopy (FTIR). While Na-Ce-X encounters the highest O2 physisorption capacity, the Na-Gd-X is adsorbing the highest quantities of molecular CO2. All three samples exhibit the chemisorbed CO2 in the form of carbonates, while the Na-X stores carbonates in monodentate and polydentate forms, the Na-Gd-X and Na-Ce-X allow the formation of polydentate carbonates only. Density functional theory (DFT) calculations revealed that trivalent cations tend to adsorb gases through two cations simultaneously which explains the presence of polydentate carbonates exclusively in the corresponding modified zeolites. The DFT results confirmed the higher affinity of Na-Gd-X and Na-Ce-X nanocrystals towards O2 in the presence of CO2. The affinity of Na-Gd-X and Na-Ce-X nanocrystals towards O2 opens the door of their use as oxygen transporters for medical applications where CO2 is constantly present. The toxicity of the nanosized zeolites and their performance in O2 release are reported too.
RESUMEN
The development of catalysts that can operate under exceptionally harsh and unconventional conditions is of critical importance for the transition of the energy and chemicals industries to low-emission and renewable chemical feedstocks. In this review we will highlight materials and more specifically metal-containing zeolite catalysts that have been tested under harsh reaction conditions such as high temperature light alkane conversion and biomass valorization. Particular attention will be given to studies that explore the stability and recyclability of metal-containing zeolite catalysts operating in continuous modes. Metal-containing zeolites are considered as an important class of catalysts operating outside the comfort zone of current heterogeneous catalytic reactions in both gas and liquid phase reactions. The relationship between the properties of the metal-containing zeolite and catalytic performance will be explored.
RESUMEN
The current energy transition presents many technological challenges, such as the development of highly stable catalysts. Herein, we report a novel "top-down" synthesis approach for preparation of a single-site Mo-containing nanosized ZSM-5 zeolite which has atomically dispersed framework-molybdenum homogenously distributed through the zeolite crystals. The introduction of Mo heals most of the native point defects in the zeolite structure resulting in an extremely stable material. The important features of this single-site Mo-containing ZSM-5 zeolite are provided by an in-depth spectroscopic and microscopic analysis. The material demonstrates superior thermal (up to 1000 °C), hydrothermal (steaming), and catalytic (converting methane to hydrogen and higher hydrocarbons) stability, maintaining the atomically disperse Mo, structural integrity of the zeolite, and preventing the formation of silanols.
RESUMEN
Thin membranes (900â nm) were prepared by direct transformation of infiltrated amorphous precursor nanoparticles, impregnated in a graphene oxide (GO) matrix, into hydroxy sodalite (SOD) nanocrystals. The amorphous precursor particles rich in silanols (Si-OH) enhanced the interactions with the GO, thus leading to the formation of highly adhesive and stable SOD/GO membranes via strong bonding. The cross-linking of SOD nanoparticles with the GO in the membranes promoted both the high gas permeance and enhanced selectivity towards H2 from a mixture containing CO2 and H2 O. The SOD/GO membranes are moisture resistance and exhibit steady separation performance (H2 permeance of about 4900â GPU and H2 /CO2 selectivity of 56, with no degradation in performance during the test of 50â h) at high temperature (200 °C) under water vapor (4â mol %).
RESUMEN
Small-pore zeolites such as chabazite (CHA) are excellent candidates for the selective separation of CO2 ; however, the current synthesis involves several steps and the use of organic structure-directing agent (OSDA), increasing their cost and energy requirements. We report the synthesis of small-pore zeolite crystals (aluminosilicate) with CHA-type framework structure by direct synthesis in a colloidal suspension containing a mixture of inorganic cations only (Na+ , K+ , and Cs+ ). The location of CO2 molecules in the host structure was revealed by 3D electron diffraction (3D ED). The high sorption capacity for CO2 (3.8â mmol g-1 at 121â kPa), structural stability and regenerability of the discreate CHA zeolite nanocrystals is maintained for 10 consecutive cycles without any visible degradation. The CHA zeolite (Si:Al=2) reaches an almost perfect CO2 storage capacity (8 CO2 per unit cell) and high selectivity (no CH4 was adsorbed).
RESUMEN
Direct evidence of the successful incorporation of atomically dispersed molybdenum (Mo) atoms into the framework of nanosized MFI zeolite is demonstrated for the first time. Homogeneous distribution of Mo with a size of 0.05 nm is observed by scanning transmission electron microscopy high-angle annular dark-field imaging (STEM-HAADF). 31P magic-angle spinning nuclear magnetic resonance (MAS NMR) and Fourier-transform infrared (FT-IR) spectroscopy, using trimethylphosphine oxide (TMPO) and deuterated acetonitrile as probe molecules, reveal a homogeneous distribution of Mo in the framework of MFI nanozeolite, and the presence of Lewis acidity. 31P MAS NMR using TMPO shows probe molecules interacting with isolated Mo atoms in the framework, and physisorbed probe molecules in the zeolite channels. Moreover, 2D 31P-31P MAS radio frequency-driven recoupling NMR indicates the presence of one type of Mo species in different crystallographic positions in the MFI framework. The substitution of framework Si by Mo significantly reduces the silanol defect content, making the resulting zeolite highly hydrophobic. In addition, the insertion of Mo into the MFI structure induces a symmetry lowering, from orthorhombic ( Pnma), typical of high silica MFI, to monoclinic ( P21/ n), as well as an expansion of unit cell volume. The novel material opens many opportunities of catalysts design for application in mature and emerging fields.
RESUMEN
The synthesis of nanostructured zeolites enables modification of catalytically relevant properties such as effective surface area and diffusion path length. Nanostructured zeolites may be synthesized either in alkaline media, and so contain significant numbers of hydrophilic silanol groups, or in expensive and harmful fluoride-containing media. Here, we report and characterize, using a combination of experimental and theoretical techniques, the one-pot synthesis of silanol-free nanosized MFI-type zeolites by introducing atomically dispersed tungsten; this prevents silanol group occurrence by forming flexible W-O-Si bridges. These W-O-Si bonds are more stable than Si-O-Si in the all-silica MFI zeolite. Tungsten incorporation in nanosized MFI crystals also modifies other properties such as structural features, hydrophobicity and Lewis acidity. The effect of these is illustrated on the catalytic epoxidation of styrene and separation of CO2 and NO2. Silanol-free nanosized W-MFI zeolites open new perspectives for catalytic and separation applications.
RESUMEN
The aim of this paper is to discuss the benefits as well as the limitations of utilizing photopolymer materials in the design of holograms that are responsive to changes in their environment, such as changes in the concentration of a specific substance, temperature, and pressure. Three different case studies are presented, including both surface and volume phase holograms, in order to demonstrate the flexibility in the approach of utilizing holographic photopolymers for the design of sensors and interactive optical devices. First, a functionalized surface relief hologram is demonstrated to operate as an optical sensor for the detection of metal ions in water. The sensitivity and selectivity of the sensor are investigated. The second example demonstrates a volume transmission hologram recorded in a temperature-sensitive photopolymer and the memory effects of its exposure to elevated temperature. Finally, a pressure-sensitive reflection hologram that changes color under application of pressure is characterized, and its potential application in document authentication is described.