Most tablets put on the market are coated with polymers soluble in water. The Opadry II 85 series from Colorcon Inc., is a family of PVA-based products marketed since the 1990s. Despite numerous publications on the properties of PVA, to date, limited work has been undertaken to determine the physico-chemical parameters (i.e., UV light, high temperature, and relative humidity) that could affect the performance of PVA-based coatings. To this end, we performed artificial ageing processes on samples made of Opadry Orange II or of some selected components of this coating and analysed them by means of a multidisciplinary approach, using, for example, FTIR, NMR, rheology, and DMTA measurements. In this way, we analysed the influence of the critical components of the Opadry Orange II formula, such as titanium dioxide and aluminium hydroxide, on the coating characteristics under ageing conditions.
RESUMEN
In this paper, poly-ether-ether-ketone (PEEK) carbon-nanotube (CNT) self-monitoring composites at different levels of filler loading (i.e., 3, 5 and 10% by weight) have been extruded as 3D-printable filaments, showing gauge factor values of 14.5, 3.36 and 1.99, respectively. CNT composite filaments of 3 and 5 wt% were 3D-printed into tensile samples, while the PEEK 10CNT filament was found to be barely printable. The 3D-printed PEEK 3CNT and PEEK 5CNT composites presented piezo-resistive behavior, with an increase in electrical resistance under mechanical stress, and showed an average gauge factor of 4.46 and 2.03, respectively. Mechanical tests highlighted that 3D-printed samples have a laminate-like behavior, presenting ultimate tensile strength that is always higher than 60 MPa, hence they offer the possibility to detect damages in an orthogonal direction to the applied load wit high sensitivity.
RESUMEN
The health monitoring of structures is of great interest in order to check components' structural life and monitor damages during operation. Self-monitoring materials can provide both the structural and monitoring functionality in one component and exploit their piezoresistive behavior, namely, the variation of electrical resistivity with an applied mechanical strain. In this work, self-monitoring plies were developed to be inserted into glass-fiber reinforced epoxy-based laminates in order to achieve structural monitoring. Nanocomposite epoxy-based resins were developed employing different contents of high surface area carbon black (CB, 6 wt%) and multiwall carbon nanotubes (MWCNT, 0.75 and 1 wt%), and rheologically and thermomechanically characterized. Self-monitoring plies were manufactured by impregnating glass woven fabrics with the resins, and were laminated with non-sensing plies via a vacuum-bag process to produce sensored laminates. The self-monitoring performance of the laminates was assessed during monotonic and cyclic three-point bending tests, as well as ball drop impact tests. A higher sensitivity was found for the CB-based systems (Gauge Factor 6.1), while MWCNTs (0.55 and 1.04) ensure electrical percolation at lower filler contents, as expected. The systems also showed the capability of being used to predict residual life and damage occurred under impact.