Differential Photoaging Effects on Colored Nanoplastics in Aquatic Environments: Physicochemical Properties and Aggregation Kinetics.

Nanoplastics (NPs) have different colors, which could affect their photoaging processes in aquatic environments. This study investigated the effects of irradiation on physicochemical properties and aggregation kinetics of five colored NPs. Photodegradation rates and photooxidation degrees ranked white ≈ yellow > red > blue ≈ black NPs, indicating that NPs with longer color wavelengths photoaged faster. The discoloration process followed color fading (2-14 days, except for white NPs), yellowing (10-16 days), yellow fading (18 days), and turning transparent (20-22 days). White NPs exhibited a different photoaging sequence (C-H → C-OH → C═O → O-C═O) from others. Photodegradation was mainly controlled by singlet oxygen, producing 13 chemicals that were mostly organic acids. The overall colloidal stability of pristine NPs ranked blue > yellow > red > black > white. Irradiation for 16 days retarded aggregation of white and other NPs in NaCl solution, raising the critical coagulation concentration (CCC) by 82.14 and 0.85-7.90%, respectively. Contrarily, irradiation promoted aggregation in CaCl2 solution by reducing the CCC of white (67.37%) and other (33.33-37.58%) NPs. The findings demonstrate that colored NPs underwent photoaging processes different from white/transparent NPs, which were focused by previous work, highlighting the important role of color in their environmental fate and transport.

Heteroaggregation kinetics of oppositely charged nanoplastics in aquatic environments: Effects of particle ratio, solution chemistry, and interaction sequence.

Interactions between positively charged amino-modified (APS) and negatively charged bare (BPS) polystyrene nanoplastics may cause heteroaggregation in aquatic environments. This study investigated the effects of particle concentration ratio, solution chemistry [electrolytes, pH, and natural organic matter (NOM)], and interaction sequence on their heteroaggregation kinetics. In the absence of electrolytes and NOM, the APS/BPS ratio for attaining maximum heteroaggregation rate (khetero) increased from APS/BPS= 3/7 to APS/BPS= 1/1 as pH increased from 4 to 10, indicating that electrostatic interactions dominated heteroaggregation. In the absence of NOM, khetero ranked APS/BPS= 2/3 > APS/BPS= 1/1 > APS/BPS= 3/2. Colloidal stability decreased linearly as pH increased from 4 to 8 at APS/BPS= 1/1, while diffusion-limited heteroaggregation persisted at pH 10. In NaCl solution, humic acid (HA) retarded heteroaggregation more effectively than sodium alginate (SA) via steric hindrance and weakening electrostatic interactions, following the modified Derjaguin-Landau-Verwey-Overbeek (MDLVO) theory. Compared with simultaneous interactions among APS, BPS, NaCl, and NOM, the NOM retardation effects on heteroaggregation weakened if delaying its interaction with others. In CaCl2 solution, the effects of NOM on heteroaggregation depended on counterbalance among charge screening, steric hindrance, and calcium bridging. These findings highlight the important role of heteroaggregation between oppositely charged nanoplastics on their fate and transport in aquatic environments.