Stable and Fast-Response Capacitive Humidity Sensors Based on a ZnO Nanopowder/PVP-RGO Multilayer.

In this paper, capacitive-type humidity sensors were prepared by sequentially drop-coating the aqueous suspensions of zinc oxide (ZnO) nanopowders and polyvinyl pyrrolidone-reduced graphene oxide (PVP-RGO) nanocomposites onto interdigitated electrodes. Significant improvements in both sensitivity and linearity were achieved for the ZnO/PVP-RGO sensors compared with the PVP-RGO/ZnO, PVP-RGO, and ZnO counterparts. Moreover, the produced ZnO/PVP-RGO sensors exhibited rather small hysteresis, fast response-recovery time, and long-term stability. Based on morphological and structural analyses, it can be inferred that the excellent humidity sensing properties of the ZnO/PVP-RGO sensors may be attributed to the high surface-to-volume ratio of the multilayer structure and the supporting roles of the PVP-RGO nanocomposites. The results in this work hence provide adequate guidelines for designing high-performance humidity sensors that make use of the multilayer structure of semiconductor oxide materials and PVP-RGO nanocomposites.

Effects of UV-Ozone Treatment on Sensing Behaviours of EGFETs with Al2O3 Sensing Film.

The effects of UV-ozone (UVO) treatment on the sensing behaviours of extended-gate field-effect transistors (EGFETs) that use Al2O3 as the sensing film have been investigated. The Al2O3 sensing films are UVO-treated with various duration times and the corresponding EGFET sensing behaviours, such as sensitivity, hysteresis, and long-term stability, are electrically evaluated under various measurement conditions. Physical analysis is also performed to characterize the surface conditions of the UVO-treated sensing films using X-ray photoelectron spectroscopy and atomic force microscopy. It is found that UVO treatment effectively reduces the buried sites in the Al2O3 sensing film and subsequently results in reduced hysteresis and improved long-term stability of EGFET. Meanwhile, the observed slightly smoother Al2O3 film surface post UVO treatment corresponds to decreased surface sites and slightly reduced pH sensitivity of the Al2O3 film. The sensitivity degradation is found to be monotonically correlated with the UVO treatment time. A treatment time of 10 min is found to yield an excellent performance trade-off: clearly improved long-term stability and reduced hysteresis at the cost of negligible sensitivity reduction. These results suggest that UVO treatment is a simple and facile method to improve the overall sensing performance of the EGFETs with an Al2O3 sensing film.