BioPEGylation of polyhydroxybutyrate promotes nerve cell health and migration.

This study reports on the superior suitability of Polyhydroxybutyrate-polyethylene glycol hybrid polymers biosynthesised by Cupriavidus necator over PHB as biomaterials for tissue engineering. Incorporation of PEG106 (DEG) during PHB biosynthesis reduced crystallinity, molecular weight, and hydrophobicity while improving mechanical properties. In vitro olfactory ensheathing cell (OEC) proliferation was enhanced by cultivation on PHB-b-DEG films. Cultivation on PHB and PHB-b-DEG films showed no cytotoxic responses and cell viability and membrane integrity was sustained. PHB-b-DEG films promoted OECs entering into the DNA replication (S) phase and mitotic (G2-M) phase during the cell growth cycle and apoptosis was low. This study also confirmed an association between the level of neurite-outgrowth inhibitory protein (Nogo) and receptor pair Ig-like receptor B (PirB) expression and cell proliferation, both being down-regulated in cells grown on hybrid films when compared with PHB and asynchronous growth. Thus, DEG-terminated PHB-based biomaterials have great potential as biological scaffolds supporting nerve repair.

Using Humidity to Control the Morphology and Properties of Electrospun BioPEGylated Polyhydroxybutyrate Scaffolds.

Electrospinning produces nanofibrous scaffolds with potential for tissue engineering and wound repair. Spinning parameters control scaffold morphology and properties. BioPEGylation of polyhydroxybutyrate (PHB) introduces terminal hydrophilic groups into the hydrophobic chain, making this natural-synthetic hybrid copolymer more susceptible to humidity. Varying the humidity from 10 to 50% RH during electrospinning had a relatively little effect on polyhydroxybutyrate (PHB) average fiber and pore diameters, which remained around 3.0 and 8.7 µm, respectively. In contrast, fiber and pore diameters for electrospun bioPEGylated PHB scaffolds varied significantly with humidity, peaking at 30% RH (5.5 and 14.1 µm, respectively). While scaffolds showed little change, hydrophobicity decreased linearly with humidity during electrospinning. Compared to solvent-cast films, electrospun scaffolds showed significantly greater average cell spread. A 108% increase for olfactory ensheathing cells (OECs) cultivated on bioPEGylated PHB scaffolds was proportionally greater than their counterparts on electrospun PHB scaffolds, (70%). OECS grown on BioPEGylated PHB scaffolds were over twice the size, 260 ± 20 µm diameter, than those on PHB electrospun scaffolds, 110 ± 18 µm diameter. Electrospun scaffolds also promoted cell health compared to their solvent-cast counterparts, with increases in the mitochondrial activity of 165 ± 13 and 196 ± 13% for PHB and bioPEGylated PHB, respectively. OECS cultivated on electrospun scaffolds of bioPEGylated PHB had significantly better membrane integrities compared to their counterparts on solvent-cast films, 47 ± 5% reducing to 17 ± 6%. The combination of bioPEGylation and humidity during electrospinning permitted significant controllable changes to scaffold morphology and properties. These changes resulted in the significantly greater promotion of cell growth on electrospun bioPEGylated PHB scaffolds compared to their solvent-cast counterparts and electrospun PHB.

Electrospun polyhydroxybutyrate and poly(L-lactide-co-ε-caprolactone) composites as nanofibrous scaffolds.

Electrospinning can produce nanofibrous scaffolds that mimic the architecture of the extracellular matrix and support cell attachment for tissue engineering applications. In this study, fibrous membranes of polyhydroxybutyrate (PHB) with various loadings of poly(L-lactide-co-ε-caprolactone) (PLCL) were successfully prepared by electrospinning. In comparison to PLCL scaffolds, PLCL blends with PHB exhibited more irregular fibre diameter distributions and higher average fibre diameters but there were no significant differences in pore size. PLCL/PHB scaffolds were more hydrophilic (<120°) with significantly reduced tensile strength (ca. 1 MPa) compared to PLCL scaffolds (150.9 ± 2.8° and 5.8 ± 0.5 MPa). Increasing PLCL loading in PHB/PLCL scaffolds significantly increased the extension at break, (4-6-fold). PLCL/PHB scaffolds supported greater adhesion and proliferation of olfactory ensheathing cells (OECs) than those exhibiting asynchronous growth on culture plates. Mitochondrial activity of cells cultivated on the electrospun blended membranes was enhanced compared to those grown on PLCL and PHB scaffolds (212, 179, and 153%, resp.). Analysis showed that PLCL/PHB nanofibrous membranes promoted cell cycle progression and reduced the onset of necrosis. Thus, electrospun PLCL/PHB composites promoted adhesion and proliferation of OECs when compared to their individual PLCL and PHB components suggesting potential in the repair and engineering of nerve tissue.