NMR Crystallography Reveals Carbonate Induced Al-Ordering in ZnAl Layered Double Hydroxide.

Layered double hydroxides (LDHs) serve a score of applications in catalysis, drug delivery, and environmental remediation. Smarter crystallography, combining X-ray diffraction and NMR spectroscopy revealed how interplay between carbonate and pH determines the LDH structure and Al ordering in ZnAl LDH. Carbonate intercalated ZnAl LDHs were synthesized at different pH (pH 8.5, pH 10.0, pH 12.5) with a Zn/Al ratio of 2, without subsequent hydrothermal treatment to avoid extensive recrystallisation. In ideal configuration, all Al cations should be part of the LDH and be coordinated with 6 Zn atoms, but NMR revealed two different Al local environments were present in all samples in a ratio dependent on synthesis pH. NMR-crystallography, integrating NMR spectroscopy and X-ray diffraction, succeeded to identify them as Al residing in the highly ordered crystalline phase, next to Al in disordered material. With increasing synthesis pH, crystallinity increased, and the side phase fraction decreased. Using 1 H-13 C, 13 C-27 Al HETCOR NMR in combination with 27 Al MQMAS, 27 Al-DQ-SQ measurements and Rietveld refinement on high-resolution PXRD data, the extreme anion exchange selectivity of these LDHs for CO3 2- over HCO3 - was linked to strict Al and CO3 2- ordering in the crystalline LDH. Even upon equilibration of the LDH in pure NaHCO3 solutions, only CO3 2- was adsorbed by the LDH. This reveals the structure directing role of bivalent cations such as CO3 2- during crystallization of [M2+ 4 M3+ 2 (OH)2 ]2+ [A2- ]1 ⋅yH2 O LDH phases.

Material properties determining the insecticidal activity of highly divided porous materials on the pharaoh ant (Monomorium pharaonis).

BACKGROUND: Historically, inert insecticidal powders such as diatomaceous earth were researched for pest management applications, and it was revealed that these types of powders killed insects by desiccation. However, data on the critical material properties that affect their efficacy are sparse. The present study investigated the insecticidal effect of powdered materials on the pharaoh ant, a notorious domestic pest. RESULTS: The insecticidal activity of 24 porous materials was tested. Eight of these materials performed better than the benchmark, diatomaceous earth. Zeolite Y and carbon black II performed best, inducing 50% mortality within 40 and 55 minutes, respectively. Statistical analysis of seven material properties revealed that macroporous surface area and Brunauer-Emmett-Teller (BET) specific surface area were most predictive of insecticidal activity. For zeolites and ordered mesoporous silica materials, the most important parameters were, respectively, BET and large mesopore surface area. Finally, gas chromatography-mass spectrometry (GC-MS) analysis confirmed the adsorption of epicuticular hydrocarbons onto the zeolite powders. CONCLUSION: This study shows clear potential for the use of environmentally friendly, inert porous materials as insecticides against the pharaoh ant and identified the key material properties influencing insecticidal activity. The GC-MS data support the hypothesis that the mortality was caused by the removal of the protective epicuticular hydrocarbons. © 2017 Society of Chemical Industry.