Heat and radiofrequency plasma glow discharge pretreatment of a titanium alloy: evidence [corrected] for enhanced osteoinductive properties.

It is believed that orthopedic and implant longevity can be improved by optimizing fixation, or direct bone-implant contact, through the stimulation of new bone formation around the implant. The purpose of this study was to determine whether heat (600°C) or radiofrequency plasma glow discharge (RFGD) pretreatment of Ti6Al4V stimulated calcium-phosphate mineral formation in cultures of attached MC3T3 osteoprogenitor cells with or without a fibronectin coating. Calcium-phosphate mineral was analyzed by flame atomic absorption spectrophotometry, scanning electron microscopy (SEM)/electron dispersive X-ray microanalysis (EDAX) and Fourier transformed infrared spectroscopy (FTIR). RFGD and heat pretreatments produced a general pattern of increased total soluble calcium levels, although the effect of heat pretreatment was greater than that of RFGD. SEM/EDAX showed the presence of calcium-and phosphorus-containing particles on untreated and treated disks that were more numerous on fibronectin-coated disks. These particles were observed earliest (1 week) on RFGD-pretreated surfaces. FTIR analyses showed that the heat pretreatment produced a general pattern of increased levels of apatite mineral at 2-4 weeks; a greater effect was observed for fibronectin-coated disks compared to uncoated disks. The observed findings suggest that heat pretreatment of Ti6Al4V increased the total mass of the mineral formed in MC3T3 osteoprogenitor cell cultures more than RFGD while the latter pretreatment hastened the early deposition of mineral. These findings help to support the hypothesis that the pretreatments enhance the osteoinductive properties of the alloy.

Heat and radiofrequency plasma glow discharge pretreatment of a titanium alloy promote bone formation and osseointegration.

Orthopedic and dental implants manifest increased failure rates when inserted into low density bone. We determined whether chemical pretreatments of a titanium alloy implant material stimulated new bone formation to increase osseointegration in vivo in trabecular bone using a rat model. Titanium alloy rods were untreated or pretreated with heat (600°C) or radiofrequency plasma glow discharge (RFGD). The rods were then coated with the extracellular matrix protein fibronectin (1 nM) or left uncoated and surgically implanted into the rat femoral medullary cavity. Animals were euthanized 3 or 6 weeks later, and femurs were removed for analysis. The number of trabeculae in contact with the implant surface, surface contact between trabeculae and the implant, and the length and area of bone attached to the implant were measured by histomorphometry. Implant shear strength was measured by a pull-out test. Both pretreatments and fibronectin enhanced the number of trabeculae bonding with the implant and trabeculae-to-implant surface contact, with greater effects of fibronectin observed with pretreated compared to untreated implants. RFGD pretreatment modestly increased implant shear strength, which was highly correlated (r(2) = 0.87-0.99) with measures of trabecular bonding for untreated and RFGD-pretreated implants. In contrast, heat pretreatment increased shear strength 3-5-fold for both uncoated and fibronectin-coated implants at 3 and 6 weeks, suggesting a more rapid increase in implant-femur bonding compared to the other groups. In summary, our findings suggest that the heat and RFGD pretreatments can promote the osseointegration of a titanium alloy implant material.

Structure-activity relationship of human bone sialoprotein peptides.

In the current study, the relationship between the structure of the RGD-containing human bone sialoprotein (hBSP) peptide 278-293 and its attachment activity toward osteoblast-like (MC3T3) cells was investigated. This goal was accomplished by examining the comparative cell-attachment activities of several truncated forms of peptide 278-293. Computer modeling of the various peptides was also performed to assess the role of secondary structure in peptide bioactivity. Elimination of tyrosine-278 at the N-terminus resulted in a more dramatic loss of cell-attachment activity compared with the removal of either tyrosine-293 or the arg-ala-tyr (291-293) tripeptide. Although replacement of the RGD (arg-gly-asp) peptide moiety with peptide KAE (lys-ala-glu) resulted in a dramatic loss of cell-attachment activity, a peptide containing RGE (arg-gly-glu) in place of RGD retained 70-85% of the parental peptide's attachment activity. These results suggest that the N-terminal RGD-flanking region of hBSP peptide 278-293, in particular the tyrosine-278 residue, represents a second cell-attachment site that stabilizes the RGD-integrin receptor complex. Computer modeling also suggested that a ß-turn encompassing RGD or RGE in some of the hBSP peptides may facilitate its binding to integrins by increasing the exposure of the tripeptide. This knowledge may be useful in the future design of biomimetic peptides which are more effective in promoting the attachment of osteogenic cells to implant surfaces in vivo.

Titanium alloy surface oxide modulates the conformation of adsorbed fibronectin to enhance its binding to α(5) ß(1) integrins in osteoblasts.

Our laboratory has previously demonstrated that heat (600°C) or radiofrequency plasma glow discharge (RFGD) pretreatment of a titanium alloy (Ti6Al4V) increased the net negative charge of the alloy's surface oxide and the attachment of osteoblastic cells to adsorbed fibronectin. The purpose of the current study was to investigate the biological mechanism by which these surface pretreatments enhance the capacity of fibronectin to stimulate osteoblastic cell attachment. Each pretreatment was found to increase the binding (measured by ELISA) of a monoclonal anti-fibronectin Ig to the central integrin-binding domain of adsorbed fibronectin, and to increase the antibody's inhibition of osteogenic cell attachment (measured by hexosaminidase assay). Pretreatments also increased the binding (measured by ELISA) of anti-integrin IgG's to the α(5) and ß(1) integrin subunits that became attached to fibronectin during cell incubation. These findings suggest that negatively charged surface oxides of Ti6Al4V cause conformational changes in fibronectin that increase the availability of its integrin-binding domain to α(5) ß(1) integrins.

Early changes in prostaglandins precede bone formation in a rabbit model of heterotopic ossification.

We have tested the hypothesis that the formation of heterotopic ossification (HO) in a rabbit model is correlated with a local increase in specific prostaglandins that may modulate mechanisms of ossification. Rabbits were sacrificed at 1 to 21 days following the daily forcible flexion of immobilized knees. The extraction and analysis of prostaglandins (PG) E2, F2alpha, D2, 6-keto-F1alpha, and thromboxane B2 in vastus intermedius muscles of manipulated legs revealed increases compared to control hindlimbs for all five prostaglandins, albeit of differing magnitude. The earliest increase was observed for PGF2alpha after 24 h (to 2.6-fold of control) with peak levels observed at day ten (185-fold of control). PGE2 was increased above control from 2 to 21 days following manipulation, with a peak level of 33-fold of control after 10 days. In a separate arm of the study, the role of PGE2 was investigated through the use of pharmacological antagonist of the PGE2 receptors and one of its second messengers, cAMP. Rabbits were preadministered the PGE2/PGD receptor antagonist AH 6809 or the cAMP antagonist Rp-cAMP prior to undergoing the regimen of limb immobilization and passive exercise. Both AH 6809 and Rp-cAMP were found to prevent the later development of radiographically documented heterotopic ossification in 15 out of 16 animals, thus identifying prostaglandins as being required for the development of ectopic bone. In this latter group, all but one pharmacologically treated animal showed an absence of HO at 3, 4, 5, or 6 weeks. These findings suggest an obligate cascade of prostaglandins for HO that offers the potential for novel prophylactic therapies, including those that target receptors for specific prostaglandins.

Heat or radiofrequency plasma glow discharge treatment of a titanium alloy stimulates osteoblast gene expression in the MC3T3 osteoprogenitor cell line.

PURPOSE: The purpose of this study was to determine whether increasing the Ti6Al4V surface oxide negative charge through heat (600℃) or radiofrequency plasma glow discharge (RFGD) pretreatment, with or without a subsequent coating with fibronectin, stimulated osteoblast gene marker expression in the MC3T3 osteoprogenitor cell line. METHODS: Quantitative real-time polymerase chain reaction was used to measure changes over time in the mRNA levels for osteoblast gene markers, including alkaline phosphatase, bone sialoprotein, collagen type I (α1), osteocalcin, osteopontin and parathyroid hormone-related peptide (PTH-rP), and the osteoblast precursor genes Runx2 and osterix. RESULTS: Osteoprogenitors began to differentiate earlier on disks that were pretreated with heat or RFGD. The pretreatments increased gene marker expression in the absence of a fibronectin coating. However, pretreatments increased osteoblast gene expression for fibronectin-coated disks more than uncoated disks, suggesting a surface oxide-mediated specific enhancement of fibronectin's bioactivity. Heat pretreatment had greater effects on the mRNA expression of genes for PTH-rP, alkaline phosphatase and osteocalcin while RFGD pretreatment had greater effects on osteopontin and bone sialoprotein gene expression. CONCLUSIONS: The results suggest that heat and RFGD pretreatments of the Ti6Al4V surface oxide stimulated osteoblast differentiation through an enhancement of (a) coated fibronectin's bioactivity and (b) the bioactivities of other serum or matrix proteins. The quantitative differences in the effects of the two pretreatments on osteoblast gene marker expression may have arisen from the unique physico-chemical characteristics of each resultant oxide surface. Therefore, engineering the Ti6Al4V surface oxide to become more negatively charged can be used to accelerate osteoblast differentiation through fibronectin-dependent and independent mechanisms.

Effects of coating a titanium alloy with fibronectin on the expression of osteoblast gene markers in the MC3T3 osteoprogenitor cell line.

PURPOSE: A number of environmental and patient-related factors contribute to implant failure. A significant fraction of these failures can be attributed to limited osseointegration resulting from poor bone healing responses. The overall goal of this study was to determine whether surface treatment of a titanium-aluminum-vanadium alloy (Ti-6Al-4V) implant material in combination with a biomimetic protein coating could promote the differentiation of attached osteoblastic cells. The specific aims of the study were to investigate whether osteoprogenitor cells cultured on a rigorously cleaned implant specimen showed a normal pattern of differentiation and whether preadsorbed fibronectin accelerated or enhanced osteoblast differentiation. MATERIALS AND METHODS: Ti-6Al-4V disks were rigorously cleaned, passivated in nitric acid, and dry heat- sterilized; some of the disks were then coated with 1 nmol/L fibronectin. MC3T3 osteoprogenitor cells were then cultured on the pretreated disks for several weeks. Quantitative real-time polymerase chain reaction was performed to measure changes over time in the mRNA levels of osteoblast genes. RESULTS: Fibronectin increased the peak expression of all analyzed osteoblast gene markers. "Early" genes that normally mark the proliferative phase (0 to 10 days) of osteoblastic development showed peak expression within the first 10 days after cell attachment to the titanium alloy. In contrast, "late" genes that normally mark the differentiation (10 to 20 days) and mineralization (20 to 36 days) phases of osteoblastogenesis achieved peak expression only after approximately 3 to 4 weeks of culture. CONCLUSIONS: Osteoprogenitors cultured on a rigorously cleaned Ti-6Al-4V alloy were found to demonstrate a normal pattern of osteoblast differentiation. Preadsorbed fibronectin was observed to stimulate osteoblast differentiation during the mineralization phase of osteoblastogenesis.

Surface oxide net charge of a titanium alloy: modulation of fibronectin-activated attachment and spreading of osteogenic cells.

In the current study, we have altered the surface oxide properties of a Ti6Al4V alloy using heat treatment or radiofrequency glow discharge (RFGD) in order to evaluate the relationship between the physico-chemical and biological properties of the alloy's surface oxide. The effects of surface pretreatments on the attachment of cells from two osteogenic cell lines (MG63 and MC3T3) and a mesenchymal stem cell line (C3H10T1/2) to fibronectin adsorbed to the alloy were measured. Both heat and RFGD pretreatments produced a several-fold increase in the number of cells that attached to fibronectin adsorbed to the alloy at a range of coating concentrations (0.001-10nM FN) for each cell line tested. An antibody (HFN7.1) directed against the central integrin binding domain of fibronectin produced a 65-70% inhibition of cell attachment to fibronectin-coated disks, indicating that cell attachment to the metal discs was dependent on fibronectin binding to cell integrin receptors. Both treatments also accelerated the cell spreading response manifested by extensive flattening and an increase in mean cellular area. The treatment-induced increases in the cell attachment activity of adsorbed fibronectin were correlated with previously demonstrated increases in Ti6Al4V oxide negative net surface charge at physiological pH produced by both heat and RFGD pretreatments. Since neither treatment increased the adsorption mass of fibronectin, these findings suggest that negatively charged surface oxide functional groups in Ti6Al4V can modulate fibronectin's integrin receptor activity by altering the adsorbed protein's conformation. Our results further suggest that negatively charged functional groups in the surface oxide can play a prominent role in the osseointegration of metallic implant materials.

Surface oxide net charge of a titanium alloy: comparison between effects of treatment with heat or radiofrequency plasma glow discharge.

In the current study, we have compared the effects of heat and radiofrequency plasma glow discharge (RFGD) treatment of a Ti6Al4V alloy on the physico-chemical properties of the alloy's surface oxide. Titanium alloy (Ti6Al4V) disks were passivated alone, heated to 600 °C, or RFGD plasma treated in pure oxygen. RFGD treatment did not alter the roughness, topography, elemental composition or thickness of the alloy's surface oxide layer. In contrast, heat treatment altered oxide topography by creating a pattern of oxide elevations approximately 50-100 nm in diameter. These nanostructures exhibited a three-fold increase in roughness compared to untreated surfaces when RMS roughness was calculated after applying a spatial high-pass filter with a 200 nm-cutoff wavelength. Heat treatment also produced a surface enrichment in aluminum and vanadium oxides. Both RFGD and heat treatment produced similar increases in oxide wettability. Atomic force microscopy (AFM) measurements of metal surface oxide net charge signified by a long-range force of attraction to or repulsion from a (negatively charged) silicon nitride AFM probe were also obtained for all three experimental groups. Force measurements showed that the RFGD-treated Ti6Al4V samples demonstrated a higher net positive surface charge at pH values below 6 and a higher net negative surface charge at physiological pH (pH values between 7 and 8) compared to control and heat-treated samples. These findings suggest that RFGD treatment of metallic implant materials can be used to study the role of negatively charged surface oxide functional groups in protein bioactivity, osteogenic cell behavior and osseointegration independently of oxide topography.

The effects of COX-1 and COX-2 inhibitors on prostaglandin synthesis and the formation of heterotopic bone in a rat model.

INTRODUCTION: Traumatic heterotopic ossification (HO) is a common clinical condition associated with various orthopedic procedures that involve injury to soft tissues near bone. In this study, we tested the hypothesis that the prophylactic effects of NSAID's in the treatment of HO are mediated via inhibition of the COX-2 enzyme. Here we describe a rat model that simulates HO in the human that was used to test the above hypothesis. MATERIALS AND METHODS: Heterotopic ossification was surgically induced in the quadriceps by injury to the muscle and femoral periosteum and transplantation of donor bone marrow cells containing osteoprogenitors into the site of injury. HO was imaged and quantified by micro-CT scanning of femurs removed from sacrificed animals at 6 weeks post-injury, three-dimensional computer reconstructions of the scanned bones and computer-assisted morphometric analysis. Prostaglandin E(2) (PGE(2)) synthesis was quantified using an enzyme immunoassay system. The effects of a nonselective COX inhibitor or specific inhibitors of COX-1 or COX-2 following oral administration on the content of ectopic bone and PGE(2) were also measured. RESULTS: Micro-CT and histological analyses demonstrated that all of the femurs in operated limbs developed HO in the vastus lateralis muscle belly of the quadriceps close to the anterior femur. Only the COX-1,2 nonselective and COX-2 inhibitors significantly decreased HO formation (by about one-third in each case; P < 0.05). PGE(2) synthesis at the site of injury was increased 50- and 100-fold (to 25 ng/g tissue) within 1 and 7 days, respectively, post-injury with the levels declining to near baseline within 2 weeks of surgery. Both the COX-1,2 nonselective and COX-2 inhibitors significantly decreased PGE(2) levels to 25% of control HO levels within 24 h of the first administration, even at low dosages. The COX-1 inhibitor only produced the same effect after 1 week of administration. CONCLUSION: These findings suggest that although inhibitors of COX-2 or COX-1 reduced PGE(2) synthesis, only the COX-2 enzyme plays a role in the mechanism of traumatic HO.