The effect of post, core, crown type, and ferrule presence on the biomechanical behavior of endodontically treated bovine anterior teeth.

STATEMENT OF PROBLEM: Unresolved controversy exists concerning the remaining coronal tooth structure of anterior endodontically treated teeth and the best treatment option for restoring them. PURPOSE: The purpose of this study was to evaluate the effect of post, core, crown type, and ferrule presence on the deformation, fracture resistance, and fracture mode of endodontically treated bovine incisors. MATERIAL AND METHODS: One hundred and eighty bovine incisors were selected and divided into 12 treatment groups (n=15). The treatment variations were: with or without ferrule, restored with cast post and core, glass fiber post with composite resin core, or glass fiber post with fiber-reinforced core, and metal- or alumina-reinforced ceramic crown (n=15). The restored incisors were loaded at a 135-degree angle, and the deformation was measured using strain gauges placed on the buccal and proximal root surfaces. Specimens were subsequently loaded to the point of fracture. Strain and fracture resistance results were analyzed by 3-way ANOVA and Tukey HSD tests (α=.05). RESULTS: Ferrule presence did not significantly influence the buccal strain and fracture resistance for the ceramic crown groups, irrespective of core and crown type. Ferrule presence resulted in lower strains and higher fracture resistance in the metal crown groups, irrespective of core. The cast post and core showed lower strain values than groups with glass fiber posts when restored with metal crowns. CONCLUSIONS: Core type did not affect the deformation and fracture resistance of endodontically treated incisors restored with alumina-reinforced ceramic crowns. The presence of a ferrule improved the mechanical behavior of teeth restored with metal crowns, irrespective of core type.

Effect of Resin Cement Porosity on Retention of Glass-Fiber Posts to Root Dentin: An Experimental and Finite Element Analysis.

The aim of this study was to evaluate the effect of porosity of self-adhesive resin on the stress distribution, post retention and failure mode of fiber post cemented to human root dentin. Ten human central upper incisors with circular root canal were selected. They were sectioned with 15 mm and were endodontically filled. The roots were scanned using micro-CT after post space preparation for root filling remaining evaluation. Fiber posts were cemented using self-adhesive resin cement (Rely X U200, 3M-ESPE). Two 1-mm-thick slices from the cervical, medium and apical thirds were scanned for resin cement bubbles volume measurements and submitted to a push-out test (PBS). Three operators using stereomicroscopy and confocal laser microscopy classified the failure mode. Stress distributions during the push-out test were analyzed using 3D finite element analysis. PBS values (MPa) were submitted to one-way ANOVA and Tukey's post hoc tests and the failure modes using the Kappa coefficient to assess inter-operator agreement. Chi-square test was used to determine significant differences between the methods ( = 0.05). Push-out bond strength was significantly affected by the bubbles presence in all root depth (p<0.05). The stress concentration was higher when the bubbles were present. Adhesive dentin/resin cement interface failure was the most frequent type of failure. Confocal microscopy was better than stereomicroscopy for failure analysis. Bubbles generated during resin cement insertion into the root canal negatively affect the stress distribution and the bond strength. The use of confocal microscopy is recommended for failure analysis.