Use of single particle inductively coupled plasma mass spectrometry for understanding the formation of bimetallic nanoparticles.

Bimetallic nanoparticles (NPs), including core-shell structure and bimetallic alloy nanoparticles, were synthesized and characterized using flow field-flow fractionation (FlFFF), single particle inductively coupled plasma mass spectrometry (SP-ICP-MS), and transmission electron microscope (TEM) with energy-dispersive x-ray spectroscopy (EDS). For the core-shell particles, a nominal 80 nm commercial core-shell AuAg bimetallic nanoparticle was used to examine the applicability of SP-ICP-MS to determine the core size of Au and shell thickness of Ag. Then, the method was applied to estimate the core size of Au and shell thickness of Ag for the laboratory synthesized particles. The results were compared with those obtained from TEM-EDS. For the alloy nanoparticles, two synthesis protocols, based on the galvanic replacement of Ag seed particles with Au, were used. One was to prepare a hollow AgAu particle by varying the volume of dissolved Au in basic solution (K-gold) to etch some parts of AgNPs to dissolved ionic silver with the formation of AuNPs covering the remaining AgNPs, producing a hole inside the core nanoparticles. Another protocol was to prepare AgAu alloy nanoparticles. SP-ICP-MS was used in combination with FlFFF to provide information on the changes of particle size with varying volume of K-gold reagent. Hydrodynamic diameter increased with increasing K-gold, as observed by FlFFF. With SP-ICP-MS without prior FlFFF, bimodal distributions were observed in the size distribution of Au and Ag. With prior FlFFF, monomodal distributions were observed by SP-ICP-MS, which allow the use of particle concentration and size to estimate the mass concentration of elements on the fractionated bimetallic nanoparticles. This study illustrates the potential use of SP-ICP-MS for gaining information about particle transformation during the synthesis of bimetallic nanoparticles.

Characterisation of Fe-oxide nanoparticles coated with humic acid and Suwannee River natural organic matter.

Iron oxide nanoparticles are becoming increasingly popular for various applications including the treatment of contaminated soil and groundwater; however, their mobility and reactivity in the subsurface environment are significantly affected by their tendency to aggregate. One solution to overcome this issue is to coat the nanoparticles with dissolved organic matter (DOM). The advantages of DOM over conventional surface modifiers are that DOM is naturally abundant in the environment, inexpensive, non-toxic and readily adsorbed onto the surface of metal oxide nanoparticles. In this study, humic acid (HA) and Suwannee River natural organic matter (SRNOM) were tested and compared as surface modifiers for Fe2O3 nanoparticles (NPs). The DOM-coated Fe2O3 NPs were characterised by various analytical methods including: flow field-flow fractionation (FlFFF), high performance size exclusion chromatography (HPSEC) and Fourier transform infrared spectroscopy (FTIR). The stability of the coated NPs was then evaluated by assessing their aggregation and disaggregation behaviour over time. Results showed that both HA and SRNOM were rapidly and readily adsorbed on the surface of Fe2O3 NPs, providing electrosteric stabilisation over a wide range of pH. HPSEC results showed that the higher molecular weight components of DOM were preferentially adsorbed onto the surface of Fe2O3. As SRNOM consists of macromolecules with a higher molecular weight than HA, the measured size of the SRNOM-coated Fe2O3 NPs was 30% larger than the HA-coated Fe2O3 NPs. FTIR results indicated the occurrence of hydrogen bonding arising from electrostatic interaction between the DOM and Fe2O3 NPs. Finally, a stability study showed that after 14 days, small agglomerates and aggregates were formed. The HA-coated Fe2O3 NPs formed agglomerates which were easily disaggregated using a vortex mixer, with the coated NPs returning to their initial size. However, SRNOM-coated Fe2O3 NPs were only partially disaggregated using the same method, which indicates that these aggregates have a more compact structure.