Effect of high irradiance and short exposure times on the depth of cure of six bulk-fill resin composites.

This study examined the effect of high irradiance and short exposure times on the depth of cure of six resin-based composites (RBCs). Bluephase PowerCure and the Valo X light-curing units (LCUs) were used to photocure bulk-fill RBCs for their recommended exposure times: Admira Fusion x-tra (AFX/20s), Aura Bulk Fill (ABF/20s), Filtek One Bulk Fill (FOB/20s), Opus Bulk Fill APS (OBF/30s), Tetric EvoCeram Bulk Fill (TEC/10s) and Tetric PowerFill (TPF/10s). In addition, all bulk-fill RBCs were tested for depth of cure with one short 3 s exposure time from the Bluephase PowerCure or the Valo X in the Xtra Power mode. The RBCs (n = 10 per RBC) were inserted into a 4 mm diameter metal mold and covered by a polyester strip before being photocured. After 24 h of storage, uncured RBC was scraped away to determine the depth of cure of the RBCs. None of the RBCs achieved a 4 mm depth of cure. The depth of cure of TEC and TPF was unaffected by the exposure times (recommended or short) when using the Valo X. The depth of cure of AFX/20s, AFX/Xtra Power, ABF/Xtra Power, FOB/Xtra Power, and OBF/30s RBCs was greater when using Valo X compared to the Bluephase PowerCure. It was concluded that short exposure times can reduce depth of cure and should only be used for some RBCs.

The impact of inorganic fillers, organic content, and polymerization mode on the degree of conversion of monomers in resin-matrix cements for restorative dentistry: a scoping review.

PURPOSE: The main aim of the present study was to carry out a scoping review on the differences in degree of conversion of monomers regarding several types resin cements, indirect restorative materials, and light-curing procedures used in dentistry. METHOD: A bibliographic review was performed on PubMed using the following search items: "degree of conversion" OR "filler" AND "resin cement" OR "inorganic cement" AND "organic" OR "radiopacity" OR "refractive" OR "transmittance" OR "type" AND "resin composite." The search involved articles published in English language within the last thirteen years. A research question has been formulated following the PICO approach as follow: "How different is the degree of conversion of monomers comparing several types of resin-matrix cements?". RESULTS: Within the 15 selected studies, 8 studies reported a high degree of conversion (DC) of the organic matrix ranging from 70 up to 90% while 7 studies showed lower DC values. Dual-cured resin-matrix cements revealed the highest mean values of DC, flexural strength, and hardness when compared with light- and self-polymerized ones. DC mean values of resin-matrix cements light-cured through a ceramic veneer with 0.4 mm thickness were higher (~ 83%) than those recorded for resin-matrix cements light-cured through a thicker ceramic layer of 1.5 mm (~ 77%). CONCLUSIONS: The highest percentage of degree of conversion of monomers was reported for dual-cured resin-matrix cements and therefore both chemical and light-induced pathways promoted an enhanced polymerization of the material. Similar degree of conversion of the same resin-matrix cement were recorded when the prosthetic structure showed a low thickness. On thick prosthetic structures, translucent materials are required to allow the light transmission achieving the resin-matrix cement. CLINICAL RELEVANCE: The chemical composition of resin-matrix cements and the light-curing mode can affect the polymerization of the organic matrix. Thus, physical properties of the materials can vary leading to early clinical failures at restorative interfaces. Thus, the analysis of the polymerization pathways of resin-matrix cements is significantly beneficial for the clinical performance of the restorative interfaces.

Degree of conversion and interfacial adaptation of touch-cure resin cement polymerized by self-curing or dual-curing with reduced light.

OBJECTIVES: The first aim of this study was to determine whether there is a difference in degree of conversion (DC) of touch-cure cements polymerized by self-curing with adhesive or dual-curing under reduced light. The second aim was to compare interfacial adaptation of zirconia restoration cemented using touch-cure cements self-cured or dual-cured by reduced light. METHODS: The DC of touch-cure resin cements with adhesive was measured continuously using Fourier transform infrared spectrometry. Experimental groups differed depending on touch-cure cement. Each group had three subgroups of polymerization method. For subgroup 1, the DC was measured by self-curing. For subgroups 2 and 3, the DCs were measured by dual-curing with reduced light penetrating 3 mm and 1 mm zirconia blocks, respectively. For interfacial adaptation evaluation, Class I cavity was prepared on an extracted third molar, and zirconia restoration was fabricated. The restoration was cemented using the same cement. Groups and subgroups for interfacial adaptation were the same as those of the DC measurement. After thermo-cycling, interfacial adaptation at the tooth-restoration interface was evaluated using swept-source optical coherence tomography imaging. RESULTS: The DC of touch-cure cement differed depending on the measurement time, resin cement, and polymerization method (p < 0.05). Interfacial adaptation was different depending on the resin cement and polymerization method (p < 0.05). CONCLUSION: For touch-cure cement, light-curing with higher irradiance presented a higher DC and superior interfacial adaptation than light-curing with lower irradiance or self-curing. CLINICAL RELEVANCE: Although some adhesives accelerate the self-curing of touch-cure cement, light-curing for touch-cure cement is necessary for zirconia cementation.

Effect of light-, chemical-, and dual-cured universal adhesives on the internal adaptation of resin composites to pulpal and gingival internal walls.

PURPOSE: To compare the internal adaptation of restorative systems bonded to mid-coronal and gingival dentin using light-cured, chemical-cured, and dual-cured adhesives, both immediately and after aging. METHODS: 60 molars were selected and received occluso-mesial preparations with dentin gingival margins. Restorations were performed using different restorative systems with light-cured, chemical-cured, and dual-cured adhesives. Internal adaptation was assessed by examining the percentage of continuous margin (%CM) at the pulpal and gingival dentin under a scanning electron microscope at x200 magnification. Half of the teeth were stored in sterile water for 24 hours, while the other half underwent 10,000 thermal cycles. Micro-morphological analysis was conducted on representative samples at x1,000 magnification. RESULTS: The restorative system with light-cured adhesive exhibited significantly lower %CM values at the gingival dentin, particularly after aging. Aging had a negative impact on the %CM values of the pulpal and gingival dentin in restorative systems with light-cured and dual-cured adhesives. Regional dentin variations influenced the %CM values, especially after aging, regardless of the restorative system used. The tested restorative system with chemical-cured adhesive is preferable for achieving improved internal adaptation when bonding to both mid-coronal and gingival dentin, compared to the other tested systems. CLINICAL SIGNIFICANCE: The study highlights the variations in adhesive performance between different regional dentin areas using the tested restorative systems.

Shedding light on the problem: Proficiency and maintenance practices of light-curing units among dental assistants.

BACKGROUND: Proper light curing is crucial for the success of restorative dentistry and to bond brackets to teeth, yet the responsibility is often delegated to dental assistants (DAs). This study assessed the proficiency and maintenance protocols of DAs when using light-curing units (LCUs) in Saudi Arabia. METHODS: Self-administered questionnaires were distributed to practicing DAs. The questionnaire contained sections on knowledge, adherence to best practices, and how to maintain the LCU. Demographic data were collected as well. Descriptive statistics and linear regressions at a significance level of (p = 0.05) were conducted to identify any relationships that influenced the DAs' LCU knowledge, practice, and maintenance protocols. RESULTS: Among the surveyed DAs, 66% were responsible for using the LCU during treatment, 16% used their fingers for support when light curing, 50% held the LCU tip 1-2 mm from the restoration during curing, and 51% did not have a specific maintenance protocol at their workplace. 70% did not know the output from the LCU, and their educational background correlated with knowledge (b = -14.42, p < 0.001). The type of institution type correlated with adherence to best practices (b = -13.65, p = 0.011), and level of knowledge and adherence to maintenance protocols showed a direct correlation (b = 0.002, p = 0.041). CONCLUSIONS: The findings revealed that a significant percentage of the DAs who replied had insufficient knowledge and did not follow the best practices and maintenance protocols for the LCUs they were using. Their educational background and workplace factors influenced this knowledge gap, while the absence of a maintenance protocol and suboptimal practices were associated with the type of institution. CLINICAL SIGNIFICANCE: To maintain the best practice, clinicians and institutions should improve the education and training of DAs. Otherwise, inadequate light curing by the DAs may jeopardize the long-term success of many dental procedures.

Influence of curing mode and aging on the bonding performance of universal adhesives in coronal and root dentin.

BACKGROUND: This study aims to evaluate the microtensile bond strength (µTBS) of different resin composite restorations bonded to mid-coronal dentin and proximal root dentin using light-cured, chemical-cured, and dual-cured adhesives immediately and after aging. Nanoleakage and degree of cure were also assessed. METHODS: Eighty-four molars were divided into mid-coronal dentin and proximal root dentin. Each group was further subdivided into three subgroups based on the restorative systems used, which involved the utilization of light-cured, chemical-cured, and dual-cured adhesives. Half of the specimens underwent µTBS testing after 24 h, while the other half after aging. Representative specimens were analyzed for nanoleakage. The degree of cure of the tested adhesive systems was also assessed. RESULTS: Aging showed a significant negative effect on µTBS results and led to increased nanoleakage (p < 0.001). Furthermore, in all subgroups, the µTBS values of proximal root dentin were lower compared to mid-coronal dentin, except in the aged subgroup for the system utilizing the dual-cured adhesive. The restorative systems with chemical and dual-cured adhesives demonstrated comparable bonding properties. However, the system with the light-cured adhesive exhibited the worst bonding properties after aging when bonded to proximal root dentin and cured at a large distance (p < 0.05). CONCLUSIONS: All tested restorative systems were negatively affected by aging, and the regional dentin had variable effects on the bonding properties. Clinicians should exercise caution when using the tested light-cured adhesive in areas where the curing distance exceeds 3 mm.

Effect of shade and thickness on the microhardness of resin-based composite specimens at different points considering curing light beam's inhomogeneity.

BACKGROUND: Recent studies have reported the inhomogeneity in the light emitted by dental light-curing units (LCUs). It is essential to understand how this uneven light distribution affects the physical properties of resin-based composites (RBCs) at various points across their surfaces. This study aimed to evaluate the effect of LCU beam's inhomogeneity on the microhardness of RBCs with different shades and thicknesses. METHODS: Four body (A1B, A2B, A3B, and A4B), one dentin (A3D), and one enamel shade (A3E) of RBC (Filtek Z350 XT) were examined. The specimens were fabricated in four thicknesses (1, 2, 3, and 4 mm) and subjected to a 40-second light-curing. Vickers microhardness testing was performed at the center point, and 3 mm left and right from the center at the bottom surface of each sample. The LCU beam profile was characterized using a beam profiler, while irradiance after specimen passage was measured using a spectrometer. One-way analysis of variance (ANOVA) and Tukey's post-hoc tests were used to analyze the effects of shades and thicknesses on irradiance and microhardness, respectively. One-way repeated-measures ANOVA was used to compare the microhardness across different points. Pearson's correlation analysis examined the relationship between irradiance and microhardness. RESULTS: The beam profile of LCU revealed inhomogeneous light distribution. Light irradiance was decreased with both the increase in thickness and darker shade of the specimens (p < 0.05). Microhardness was found to decline with an increase in sample thickness (p < 0.05), and was consistently higher at the center point compared to the periphery, particularly in thicker (3 and 4 mm) and darker shades (A3B, A4B, and A3D). A positive correlation was found between the irradiance and microhardness across all evaluated points (p < 0.05). CONCLUSIONS: Inhomogeneous light emission from LCU significantly influences the microhardness of RBC samples, depending on the thicknesses and shades. The findings underline the importance of considering LCU beam inhomogeneity in clinical settings to ensure optimal polymerization of RBC.

Influence of light-polymerizing units and zirconia on the physical, chemical and biological properties of self-adhesive resin cements.

BACKGROUND: Self-adhesive resin cements (SARCs) are widely used for fixed prostheses, but incomplete cleaning near the gingival margin can cause inflammation. However, the factors influencing cement properties and the biological response of gingival fibroblasts to cement eluates are not well understood. This study examines the impact of two light-polymerizing units (LPUs) on the physical and chemical properties of two SARCs under simulated clinical conditions, as well as the subsequent response of human gingival fibroblasts (hGFs) to these eluates. METHODS: Dental cement discs of SARCs were polymerized using Kerr DemiPlus and 3 M Elipar DeepCure-S LED LPUs with or without a 2-mm thick zirconia screen. Physical properties (microhardness, surface roughness, residual monomers) were evaluated. hGFs' cell viability, wound healing potency, and gene expression were assessed. RESULTS: Both Maxcem and RelyX exhibited reduced microhardness and increased surface roughness when polymerized through zirconia or with DemiPlus LPU. Higher residual monomers (HEMA and GDMA in Maxcem; TEGDMA in RelyX) concentration was observed with DemiPlus and zirconia polymerization. Maxcem polymerized with DemiPlus exhibited lower cell viability, impaired healing, and altered gene expression in hGFs compared to those polymerized with Elipar LPU. Gene expression changes included downregulated NRF2 and HO-1 and upregulated CCR-3. CONCLUSIONS: Light-polymerizing Maxcem through zirconia with DemiPlus LPU compromised SARCs' properties, leading to higher residual monomers and negatively impacting hGFs' viability, healing, and gene expression. Careful material selection and polymerization techniques are crucial to minimize adverse effects on surrounding tissues. CLINICAL SIGNIFICANCE: Clinicians should exercise caution when using LPUs and SARCs, especially when polymerizing through zirconia. This will help optimize the physical and chemical properties of SARCs and minimize potential adverse effects on the surrounding gingival soft tissues.

Influence of radiant exposure and material shade on the degree of conversion and microhardness of a resin-based composite.

This in vitro study evaluated the influence of radiant exposure and material shade on the degree of conversion (DC) and microhardness of a resin-based composite (RBC). Sixty-four RBC specimens in shades A1E (enamel) and A4D (dentin) were light cured at a calibrated exitance of 1000 mW/cm2 for 5, 10, 15, or 20 seconds, resulting in radiant exposure levels of 5, 10, 15, or 20 J/cm2. The DC was determined using Fourier-transform infrared spectroscopy (n = 3 per shade per exposure level). The Knoop hardness number (KHN) was measured on the top and bottom surfaces of each specimen (n = 5 per shade per exposure level). Data were analyzed using 2- and 3-way analyses of variance and post hoc Tukey tests (α = 0.05). The RBC shade did not affect the DC (P = 0.860), and the lowest DC values were achieved with an exposure level of 5 J/cm2 (P < 0.001). The shade did not affect the KHN on the top surface, but the radiant exposure level did, with the application of 5 J/cm2 resulting in significantly lower values (P < 0.05). For the bottom surface, shade A1E showed significantly higher KHN values than A4D (P < 0.001). An increase in the radiant exposure led to increased DC and KHN for both shades of RBC until reaching a saturation point of 10 J/cm2 for A1E and the top surface of A4D. The darker and more opaque shade was not adequately polymerized at a 2-mm depth, even when the highest radiant exposure level was applied.

Evaluation of the effect of high-intensity light-curing device on micro-leakage of pits and fissure sealants.

Reducing treatment time is one of the most important trends in modern dentistry. This study aimed to compare the micro-leakage around the resin sealants when using both high and conventional intensity light-curing systems. The study sample consisted of 30 extracted human maxillary premolar teeth that were divided into two equal groups according to the light-curing system used: Group 1, High-Intensity Light-Curing System and Group 2, Conventional Light-Curing System. Light-curing by Woodpecker I-LED device with two intensities (high and conventional) has been used. All teeth were subjected to 500 cycles of thermocycling. Then, a methylene blue dye microleakage test was performed, and the teeth were sectioned longitudinally and studied under a stereo microscope. The mean of micro-leakage in the high-intensity group (1.33 ± 1.29) was less than in the conventional intensity group (1.63 ± 1.29) without any statistically significant differences (p = 0.320). The high-intensity light-curing system mode may be a good and acceptable alternative to conventional intensity light-curing system mode in polymerization of pits and fissure sealants.

In vitro temperature changes in the pulp chamber caused by laser and Quadwave LED-light curing units.

The study evaluated the pulp temperature (PT) increase in Class I and V preparations when exposed to the Monet Laser (for 1 and 3 s), the PinkWave (for 3 and 10 s), the Valo Grand (for 3 and 10 s), the PowerCure, (for 3 and 10 s) and the SmartLite Pro (for 10 s). Non-retentive Class I and Class V cavities were prepared in one molar fixed in an acrylic plate and positioned in a warm water bath. The PT baseline was kept at 32 °C to simulate physiological conditions. Two T-type thermocouples were inserted through the roots into the pulp chamber in two positions: close to the pulp horn and the buccal wall close to the Class V cavity. The water flow was adjusted to 0.026 mL/min, and real-time temperature data were collected every 0.5 s. PT measurements were made with the tip of the LCU 0 and 6 mm away from the tooth surface. The radiant exitance (mW/cm2) and radiant exposure (J/cm2) were calculated. One-way ANOVA compared the effect of the pulpal flow, and ΔT values were subjected to two-way ANOVA, followed by Scheffe's post hoc tests. The Monet Laser used for 3 s and the PinkWave used for 10 s produced the greatest PT rise in the Class I cavity. The simulated pulpal flow did not influence the PT rise. Overall, cavities exposed at the 0 mm distance had higher ΔT values than groups at 6 mm distance. The placement of a rubber dam for Class V restorations may prevent positioning LCUs directly over the cavity, which may affect the rise in PT.

Temperature changes and hardness of resin-based composites light-cured with laser diode or light-emitting diode curing lights.

The temperature and Vickers Hardness (VH) at the top and bottom surfaces of three resin-based composites (RBCs) were measured when light-cured using five light-curing units (LCUs). The spectrum, power, and energy delivered to the top of the RBCs and transmitted through the RBCs were measured. Starting at 32℃, the temperature rise produced by the Monet Laser (ML-1 s and 3 s), Valo Grand (VG-3 s and 10 s), DeepCure (DC-10 s), PowerCure, (PC-3 s and 10 s) and PinkWave (PW-10 s) were measured at the bottom of specimens 2 mm deep × 6 mm wide made of Filtek Universal A2, Tetric Evoceram A2 and an experimental RBC codenamed Transcend UB. The VH values measured at the top and bottom of these RBCs were analyzed using ANOVA and Scheffe's post hoc test (p < 0.05) to determine the effects of the LCUs on the RBCs. The transmitted power from the ML was reduced by 77.4% through 2 mm of Filtek Universal, whereas light from PW decreased by only 36.8% through Transcend. The highest temperature increases from the LCU combined with the exothermic reaction occurred for Transcend, and overall, no significant differences were detected between Filtek Universal and Tetric Evoceram (p = 0.9756). Transcend achieved the highest VH values at the top and bottom surfaces. The PinkWave used for 10 s produced the largest temperature increase (20.2℃) in Transcend. The Monet used for 1 s produced the smallest increase (7.8℃) and the lowest bottom:top VH ratios.

Enhanced effectiveness of silver diamine fluoride application with light curing on natural dentin carious lesions: an in vitro study.

This study aimed to compare the mean mineral density difference (mMDD) and surface morphology of 10- and 60-s silver diamine fluoride (SDF)-applied dentin carious lesions and to study the effect of an additional 20-s light curing (LC) on SDF-treated teeth. Forty primary molar blocks with natural dentin carious lesions were measured for baseline lesion depth and mineral density using Image-Pro Plus software. The samples were randomly distributed into 4 groups; 38% SDF applied for 1) 10-s (10SDF), 2) 60-s (60SDF), 3) 10-s + LC (10SDF + LC), 4) 60-s + LC (60SDF + LC) and an additional control group to assess the outcome of pH-cycling only. Then all the groups underwent a 7-d bacterial pH-cycling. The dentin carious lesions' mMDD was determined by digital subtraction radiographic analysis. The surface morphology and elemental profile were assessed by scanning electron microscopy and energy-dispersive X-ray spectroscopy. The mMDD of the dentin lesions was analyzed using two-way ANOVA, generalized linear models analysis. Light curing was the only factor that affected the mMDD (p = 0.007). The mMDD in the 10SDF + LC and 60SDF + LC groups were significantly higher than those without light curing (p = 0.041 and 0.041, respectively). The 60SDF + LC group demonstrated a significantly higher mMDD than the 10SDF group (p = 0.010), while that in the 10SDF + LC group was similar to the 60SDF group (p = 1.00). Scanning electron microscopy revealed denser mineral content layers, which were likely silver and chloride, in the 10SDF + LC and 60SDF + LC groups than in the 10SDF and 60SDF groups, respectively. In conclusion, shortened application time with light curing enhanced SDF remineralization similarly to the conventional method.

Delayed light-curing of dual-cure bulk-fill composites on internal adaptation and depth of cure.

OBJECTIVE: To evaluate the effect of delayed light-curing of dual-cure bulk-fill composites on internal adaptation and microhardness (KHN) in depth. MATERIALS AND METHODS: Bulk-fill composites were placed in 35 box-shaped preparations and cured according to the following protocols (n = 5): Filtek Bulk-Fill light-cured immediately after insertion (FBF); Bulk-EZ light-cured immediately after insertion (BEZ-I); Bulk-EZ light-cured 90 s after insertion (BEZ-DP); Bulk-EZ self-cured (BEZ-SC); HyperFIL light-cured immediately after insertion (HF-I); HyperFIL light-cured 90 s after insertion (HF-DP); HyperFIL self-cured (HF-SC). After 24 h, the samples were axially sectioned, and the internal adaptation was evaluated using replicas under a scanning electron microscope. The KHN was evaluated at six depths (0.3 mm, 1 mm, 2 mm, 3 mm, 4 mm, and 5 mm). The statistical analysis was performed using α = 0.05. RESULTS: The KHN significantly decreased with depth, except in self-curing mode, when it was similar at all depths. Delayed light-curing significantly increased the KHN at higher depths. The internal adaptation was material-dependent. Light-curing did not influence the internal adaptation of HyperFIL, whereas delayed light-curing significantly reduced the internal gaps (%) of Bulk-EZ. CONCLUSION: Delayed light-curing improved the depth of cure of dual-cure resin composites. Light-curing did not influence the internal adaptation of HyperFIL, but delayed light-curing improved the internal adaptation of Bulk-EZ. CLINICAL SIGNIFICANCE: Light-curing is fundamental for improving the mechanical properties of dual-cure resin composites. Moreover, depending on the dual-cure resin composite, the delay in light-curing can reduce the internal gaps.

Effect of thickness of CAD/CAM materials on light transmission and resin cement polymerization using a blue light-emitting diode light-curing unit.

OBJECTIVE: Evaluate the effect of thickness of high-translucency (HT) CAD/CAM materials on irradiance and beam profile from a blue light-emitting diode light-curing unit (LCU) and on the degree of conversion (DC) and maximum polymerization rate (Rpmax ) of a light-cured resin cement (LCC). MATERIAL AND METHODS: The direct output from the LCU, the light transmission and irradiance ratio (IR) through one conventional composite and nine HT CAD/CAM materials (0.5, 1.0, 1.5, or 2.0-mm thick; n = 5) were measured with a integrating sphere coupled to a spectrometer. The light beam was assessed with a beam profiler camera. The DC at 600 s and the Rpmax of one LCC was determined using a Fourier transform infrared spectrometer (n = 5). Data were analyzed by ANOVA followed by Tukey's tests, and Dunnett's test was also used for irradiance data (α = 0.05). RESULTS: A significant decrease in irradiance through all materials occurred as thickness increased. Thin CAD/CAM materials improved light homogeneity, which decreased with the increase in thickness. The DC of the LCC directly exposed to light was the same as when exposed to 45%, 25%, 15%, or 5% IRs. Rpmax decreased with the decrease in IR. CONCLUSIONS: Although the HT CAD/CAM materials reduced the irradiance from the LCU, minor effects were observed in the LCC's DC. CLINICAL SIGNIFICANCE: Despite the light attenuation of blue light through different CAD/CAM materials that were up to 2-mm thick, the degree of conversion of one brand of light-cured resin cement was clinically acceptable when the LCU was used for 30 s.

Irradiance from 12 LED light curing units measured using 5 brands of dental radiometers.

OBJECTIVE: To evaluate the accuracy of five brands of radiometers in reporting the irradiance (mW/cm2 ) from twelve brands of LCUs compared to a 'Gold Standard' (GS) reference obtained from a hand-held laboratory-grade radiometer. MATERIALS AND METHODS: The irradiance was measured from two examples of twelve brands of previously used LCUs on two examples of five brands of dental radiometers. The emission spectrum was also obtained. Irradiance data from each brand of LCU against each meter was analyzed using the Shapiro-Wilk test for normality. The irradiance values were subjected to a two-way ANOVA followed by Bonferroni tests for each LCU brand. Finally, a descriptive analysis was made using a 95% confidence interval around the mean irradiance. RESULTS: The power output from the LCUs ranged from 271 mW to 1005 mW. Among the tested radiometers, only the Bluephase Meter II could accurately report the irradiance from 11 out of the 12 brands of LCU evaluated in this study. When measured using the "GS" system, the mean irradiance values from the two examples of nine brands of previously used LCU were not always within ±10% of the irradiance values stated by the manufacturer. CONCLUSIONS: The mean irradiance values from 9 of the 12 brands of used LCUs were beyond ±10% of the irradiance values stated by the manufacturer. Only the Bluephase Meter II could accurately report the irradiance from 11 out of the 12 brands of LCU evaluated in this study. CLINICAL SIGNIFICANCE: There was a wide range in the power output from the LCUs tested. It was impossible to accurately measure the irradiance from all the LCUs using the dental radiometers examined. However, dental radiometers should still be used in dental offices to monitor the light output from LCUs and verify that they are working correctly before they are used on patients.

In-vitro pulpal temperature increases when photo-curing bulk-fill resin-based composites using laser or light-emitting diode light curing units.

OBJECTIVE: To evaluate the in vitro pulpal temperature rise (ΔT) within the pulp chamber when low- and high-viscosity bulk-fill resin composites are photo-cured using laser or contemporary light curing units (LCUs). MATERIALS AND METHODS: The light output from five LCUs was measured. Non-retentive Class I and V cavities were prepared in one upper molar. Two T-type thermocouples were inserted into the pulp chamber. After the PT values reached 32°C under simulated pulp flow (0.026 mL/min), both cavities were restored with: Filtek One Bulk Fill (3 M), Filtek Bulk Fill Flow (3 M), Tetric PowerFill (Ivoclar Vivadent), or Tetric PowerFlow (Ivoclar Vivadent). The tooth was exposed as follows: Monet Laser (1 and 3 s), PowerCure (3 and 20 s), PinkWave (3 and 20 s), Valo X (5 and 20 s) and SmartLite Pro (20 s). The ΔT data were subjected to one-way ANOVA followed by Scheffe's post hoc test. RESULTS: Monet 1 s (1.9 J) and PinkWave 20 s (30.1 J) delivered the least and the highest amount of energy, respectively. Valo X and PinkWave used for 20 s produced the highest ΔT values (3.4-4.1°C). Monet 1 s, PinkWave 3 s, PowerCure 3 s (except FB-Flow) and Monet 3 s for FB-One and TP-Fill produced the lowest ΔT values (0.9-1.7°C). No significant differences were found among composites. CONCLUSIONS: Short 1- to 3-s exposures produced acceptable temperature rises, regardless of the composite. CLINICAL SIGNIFICANCE: The energy delivered to the tooth by the LCUs affects the temperature rise inside the pulp. The short 1-3 s exposure times used in this study delivered the least amount of energy and produced a lower temperature rise. However, the RBC may not have received sufficient energy to be adequately photo-cured.

Influence of high-irradiance light curing on the marginal integrity of composite restorations in primary teeth.

BACKGROUND: Reducing the necessary time to restore primary teeth improves the cooperation of paediatric patients. This study aimed to investigate the marginal integrity of restorations prepared with a bulk-fill resin-based composite (RBC) containing additional fragmentation chain transfer (AFCT) compared to a conventional RBC when light cured with a rapid high-irradiance (3 s) and a regular (10 s) curing mode. METHODS: Forty class-II cavities were prepared in 40 primary molars. The molars were randomly divided into four groups based on the applied light-curing modes (regular: 10 s @ 1200 mW/cm2 or high-irradiance: 3 s @ 3000 mW/cm2) and the used restorative material (AFCT-containing bulk-fill RBC "Power Fill" or AFCT-free conventional RBC "Prime"). After thermo-mechanical loading, the marginal integrity was analysed using scanning electron microscopy. A beta regression model and pairwise comparisons were used to statistically analyse the data. RESULTS: The mean marginal integrity (% ± SD) of the restorations for each group was as follows: Power Fill (10 s: 79.7 ± 15.6) (3 s: 77.6 ± 11.3), Prime (10 s: 69.7 ± 11.1) (3 s: 75.0 ± 9.7). The difference between the RBCs for the same light-curing mode was statistically significant (p ≤ 0.05). The difference between the light-curing modes for the same RBC was not statistically significant (p ˃ 0.5). CONCLUSIONS: AFCT-containing bulk-fill RBC "Power Fill" achieves similar marginal integrity when light-cured with either high-irradiance or regular light-curing modes. "Power Fill" achieves better marginal integrity than the conventional RBC "Prime" regardless of the applied light-curing mode.

Effects of nanohybrid flowable resin-based composites on fibroblast viability using different light-curing units.

PURPOSE: To investigate the in vitro cytotoxic effects of Bis-GMA-containing and Bis-GMA-free flowable resin-based composites (RBCs) on primary human gingival fibroblast cells (hGFc) using direct and indirect curing methods and three different light-curing units (LCUs). MATERIALS AND METHODS: Cells were isolated and cultured in vitro in 24-well plates. The plates were divided into treatment (cells with RBC), control (cells only), and blank (media only) groups. In the treatment groups, two types of nanohybrid flowable RBCs were used: Bis-GMA-free and Bis-GMA groups. Each treatment group was subdivided according to the curing method, i.e., direct curing (RBC was injected into the wells and cured directly on the attached cells) and indirect curing (the samples were pre-cured outside of the well plate and then added to the well plate with cells). To vary the LCU, the subgroups were further divided into three groups: multiple-emission peak light-emitting diode, single-emission peak light-emitting diode, and quartz-tungsten-halogen units. Curing was conducted for 20 seconds. The hGFc cytotoxicity was evaluated via 3-[4,5-dimethylthiazol-2-yl]-2,5-diphenyltetrazolium bromide (MTT) assay after 24, 48, and 72 hours of culturing. RESULTS: The MTT assay results showed that both RBCs were significantly cytotoxic toward hGFc compared to the control group (p < 0.0001). The Bis-GMA group was significantly more cytotoxic to the cells compared to the Bis-GMA-free group. In addition, the curing method and time interval affected cell viability regardless of the LCU used. CONCLUSION: The Bis-GMA flowable RBC and direct curing method had the highest cytotoxic effects on hGFc regardless of the LCU used. Careful selection of flowable RBCs and proper curing techniques are required to decrease the cytotoxic effects on hGFc and improve the clinical handling of oral tissues.

Novel chairside spectrometer-trained system for measuring the irradiance of light-curing units.

The purpose of this study was to compare the performances of 5 different instruments in measuring the irradiance of light-curing units (LCUs). A novel spectrometer-trained radiometer (CheckUp), 2 conventional chairside radiometers (Bluephase Meter I and Bluephase Meter II), and 2 devices considered to be gold standards for measuring irradiance (an integrating sphere spectrometer and a thermopile sensor) were used to evaluate 7 LCUs. The irradiance of each LCU was measured 10 times with each meter. Data were analyzed using linear regression analysis and a 1-way analysis of variance with Tukey post hoc test (α = 0.05). The mean irradiance values of the LCUs differed significantly depending on which meter was used for measurement (P < 0.05). Bivariate regression analysis demonstrated that the highest correlations in the irradiance values were found between the CheckUp meter and both the integrating sphere (r2 = 0.980) and the thermopile (r2 = 0.933). The absolute mean (SD) percentage deviation between irradiance measured by the CheckUp instrument and irradiance measured by the other meters was 7.2% (2.0%) for the integrating sphere, 7.0% (3.6%) for the thermopile, 21.5% (16.1%) for Bluephase Meter I, and 13.1% (7.1%) for Bluephase Meter II. Compared with the 2 conventional chairside radiometers, the CheckUp meter provided the highest correlation with and lowest absolute percentage deviation from the irradiance measured by the gold standard spectrometers.