Lattice Deformation of Tb0.29Dy0.71Fe1.95 Alloy during Magnetization.
Micromachines (Basel)
; 14(10)2023 Sep 28.
Article
en En
| MEDLINE
| ID: mdl-37893297
ABSTRACT
In Tb-Dy-Fe alloy systems, Tb0.29Dy0.71Fe1.95 alloy shows giant magnetostrictive properties under low magnetic fields, thus having great potential for transducer and sensor applications. In this work, the lattice parameters of Tb0.29Dy0.71Fe1.95 compounds as a function of a magnetic field were investigated using in situ X-ray diffraction under an applied magnetic field. The results showed that the c-axis elongation of the rhombohedral unit cell was the dominant contributor to magnetostriction at a low magnetic field (0-500 Oe). As the magnetic field intensity increased from 500 Oe to 1500 Oe, although the magnetostrictive coefficient continued to increase, the lattice constant did not change, which indicated that the elongated c-axis of the rhombohedral unit cell rotated in the direction of the magnetic field. This rotation mainly contributed to the magnetostriction phenomenon at magnetic fields of above 500 Oe. The structural origin of the magnetostriction performance of these materials was attributed to the increase in rhombohedral lattice parameters and the rotation of the extension axis of the rhombohedral lattice.
Texto completo:
1
Colección:
01-internacional
Banco de datos:
MEDLINE
Idioma:
En
Revista:
Micromachines (Basel)
Año:
2023
Tipo del documento:
Article
País de afiliación:
China