RESUMO
Three metal-organic framework (MOF)-based photoanodes were prepared by deposition on TiO2 nanotubes using Ti as substrate (Ti/TiO2NT): i) Ti/TiO2NT-Au@ZIF-8, ii) Ti/TiO2NT-Ru3(BTC)2, iii) Ti/TiO2NT-UiO-66(Zr)NH2. These photoanodes were characterized by FEG-SEM, EDX and DRX. The analyses showed a successful modification and a high homogeneity of the different MOFs on the Ti/TiO2NT surface. The photoanodes were studied in the degradation of Contaminants of Emerging Concern (CECs) in a spiked secondary effluent from a Municipal Wastewater Treatment Plant (MWWTP). Sodium diclofenac (DCF), sulfamethazine (SMT) and carbamazepine (CBZ) were used as CECs at low concentration (200 µg/L each CEC). The samples were preconcentrated using Solid Phase Extraction (SPE) and analyzed by a HPLC-DAD system. The MOF-based photoanodes exhibited a high photoelectrochemical (PEC) activity towards the oxidation of CECs, achieving up to 50%, 70% and 80% of removal using Ti/TiO2NT-Au@ZIF-8, Ti/TiO2NT-UiO-66(Zr)NH2, Ti/TiO2NT-Ru3(BTC), respectively. The influence of the generation of hydroxyl radical was then studied. The results indicate that PEC degradation using Ti/TiO2NT-Ru3(BTC)2 and Ti/TiO2NT-UiO-66(Zr)NH2 is more affected by the concentration of the radical.
Assuntos
Estruturas Metalorgânicas , Nanotubos , Ácidos Ftálicos , Estruturas Metalorgânicas/química , OxirreduçãoRESUMO
The effective removal of organics from winery wastewater was obtained in real residual effluents from the wine industry using anodic oxidation (AO). The effluent had an initial organic load of [COD]0 of 3490â¯mgâ¯L-1 equal to [TOC]0 of 1320â¯mgâ¯L-1. In addition, more than 40 organic compounds were identified by means of GC-MS. Different density currents as well as the addition of electrolytes were tested during electrolysis. The results show the decay of [COD]t by 63.6% when no support electrolyte was added, whereas almost total mineralization and disinfection was reached after adding of 50â¯mM of sodium sulfate and sodium chloride and applying higher density currents. The presence of sulfate and chloride in large concentration favors the production of oxidants such as hydroxyl radicals and active chlorine species that react with organics in solution. Moreover, the addition of a supporting electrolyte to industrial wastewater increases conductivity, reduces cell potential and therefore, decreases the energy consumption of the AO process.