RESUMO
High channel current of the high electron mobility transistors (HEMTs) and high relative responsivity of the photodetectors (PDs) were demonstrated in the AlGaN/AlN/GaN channel-stacking epitaxial structures. The interference properties of the X-ray curves indicated high-quality interfaces of the conductive channels. The AlGaN/AlN/GaN interfaces were observed clearly in the transmission electron microscope micrograph. The saturation I ds currents of the HEMT structures were increased by adding a number of channels. The conductive properties of the channel-stacking structures corresponded to the peaks of the transconductance (g m) spectra in the HEMT structures. The depletion-mode one- and two-channel HEMT structures can be operated at the cutoff region by increasing the reverse V gs bias voltages. Higher I ds current in the active state and lower current in the cutoff state were observed in the two-channel HEMT structure compared with one- and three-channel HEMT structures. For the channel-stacking metal-semiconductor-metal photodetector structures, the peak responsivity was observed at almost 300 nm incident monochromic light, which was increased by adding a number of channel layers. The channel current of the HEMT devices and the photocurrent in the PD devices were increased by adding a number of two-dimensional electron gas (2DEG) channels. By using a flat gate metal layer, the two-channel AlGaN/AlN/GaN HEMT structures exhibited a high I ds current, a low cutoff current, and a high peak g m value and have the potential for GaN-based power devices, fast portable chargers, and ultraviolet PD applications.
RESUMO
The conical air-void structure of an InGaN light-emitting diode (LEDs) was formed at the GaN/sapphire interface to increase the light extraction efficiency. The fabrication process of the conical air-void structure consisted of a dry process and a crystallographic wet etching process on an undoped GaN layer, followed by a re-growth process for the InGaN LED structure. A higher light output power (1.54 times) and a small divergent angle (120°) were observed, at a 20 mA operation current, on the treated LED structure when compared to a standard LED without the conical air-void structure. In this electroluminescence spectrum, the emission intensity and the peak wavelength varied periodically by corresponding to the conical air-void patterns that were measured through a 100 nm-optical-aperture fiber probe. The conical air-void structure reduced the compressed strain at the GaN/sapphire interface by inducing the wavelength blueshift phenomenon and the higher internal quantum efficiency of the photoluminescence spectra for the treated LED structure.
RESUMO
InGaN light emitting diodes (LED) structure with an embedded 1/4λ-stack nanoporous-GaN/undoped-GaN distributed Bragg reflectors (DBR) structure have been demonstrated. Si-heavily doped GaN epitaxial layers (n(+)-GaN) in the 12-period n(+)-GaN/u-GaN stack structure are transformed into low refractive index nanoporous GaN structure through the doping-selective electrochemical wet etching process. The central wavelength of the nanoporous DBR structure was located at 442.3 nm with a 57 nm linewidth and a 97.1% peak reflectivity. The effective cavity length (6.0λ), the effective penetration depth (278 nm) in the nanoporous DBR structure, and InGaN active layer matching to Fabry-Pérot mode order 12 were observed in the far-field photoluminescence radiative spectra. High electroluminescence emission intensity and line-width narrowing effect were measured in the DBR-LED compared with the non-treated LED structure. Non-linear emission intensity and line-width reducing effect, from 11.8 nm to 0.73 nm, were observed by increasing the laser excited power. Resonant cavity effect was observed in the InGaN LED with bottom nanoporous-DBR and top GaN/air interface.