NiMo alloys are considered highly promising non-noble Hydrogen Evolution Reaction (HER) catalysts. Besides the synergistic effect of alloying elements, recent attention is drawn to the Mo leaching from the catalyst. This work investigates the role of Mo in NiMo alloys during HER, aiming to understand the interplay between compositional, structural, and electronic factors on the activity, and their effects on the electrode material and catalyst properties. For this purpose, sputter-deposited low roughness NixMo100-x thin films are produced. The investigation of catalyst performance depending on their chemical composition shows a volcano-shaped plot, peaking for the Ni65Mo35 alloy with the highest intrinsic activity in alkaline HER. A comprehensive electrode surface analysis combining transmission electron microscopy, X-ray photoelectron spectroscopy and atomic force microscopy identifies the leaching of Mo on a structural level and indicates the formation of a Ni(OH)2-rich surface area. The ultimate surface characteristics of the NiMo catalysts depend on the initial composition and the electrochemical procedure. Based on the findings, it conclude that the observed catalytic properties of NiMo alloys in HER are determined by a complex interplay of increasing roughness, available surface species and their synergies. The leaching of Mo has a proven structural effect and is considered one of several factors contributing to the enhanced catalyst activity.
RESUMO
Highly effective yet affordable non-noble metal catalysts are a key component for advances in hydrogen generation via electrolysis. The synthesis of catalytic heterostructures containing established Ni in combination with surface NiO, Ni(OH)2, and NiOOH domains gives rise to a synergistic effect between the surface components and is highly beneficial for water splitting and the hydrogen evolution reaction (HER). Herein, the intrinsic catalytic activity of pure Ni and the effect of partial electrochemical oxidation of ultra-smooth magnetron sputter-deposited Ni surfaces are analyzed by combining electrochemical measurements with transmission electron microscopy, selected area electron diffraction, X-ray photoelectron spectroscopy, and atomic force microscopy. The experimental investigations are supplemented by Density Functional Theory and Kinetic Monte Carlo simulations. Kinetic parameters for the HER are evaluated while surface roughening is carefully monitored during different Ni film treatment and operation stages. Surface oxidation results in the dominant formation of Ni(OH)2, practically negligible surface roughening, and 3-5 times increased HER exchange current densities. Higher levels of surface roughening are observed during prolonged cycling to deep negative potentials, while surface oxidation slows down the HER activity losses compared to as-deposited films. Thus, surface oxidation increases the intrinsic HER activity of nickel and is also a viable strategy to improve catalyst durability.