Isothermal relaxation kinetics for the reduction and oxidation of SrFeO3 based perovskites.

The perovskite oxide SrFeO3 has favourable redox properties for oxygen exchange applications, including oxygen separation and oxygen production chemical looping cycles. For such applications, lower temperature operation can improve the energy demand and feasibility of the process, but can also lead to kinetic limitations. Here we investigate the oxidation and reduction reaction kinetics of SrFeO3 in the temperature range 450-750 K. Isothermal relaxation techniques are used to observe the reaction rates across this temperature range, using a thermogravimetric analysis system. Experimental data are analysed according to an isoconversional method and fit with a simple power law model to extract activation energies. The apparent activation energy of oxidation and reduction was found to be 92 ± 16 and 144 ± 17 kJ mol-1 respectively. Comparison of oxidation and reduction kinetics together with considerations of particle size indicate that the oxidation reaction rate may be limited by diffusion in the bulk, while the reduction reaction rate is limited by the surface reaction. Furthermore, we also investigated the mixed perovskite Sr0.93Ca0.07Fe0.9Co0.1O3, which exhibited a 4-fold increase in the oxidation rate.

Statistical thermodynamics of non-stoichiometric ceria and ceria zirconia solid solutions.

The thermodynamic redox properties of ceria and ceria zirconia solid solutions are analysed with a new methodology for modelling such systems based on the statistical mechanics of lattice configurations. Experimental thermogravimetric equilibrium data obtained for small non-stoichiometry measurements are combined with literature data to cover a large range of non-stoichiometry (CeO2-δ, δ = 0.001-0.32), temperature (1073-1773 K) and oxygen partial pressure (1-10(-13) bar). A dilute species model of defect clusters , obeying the law of mass action, was sufficient to describe the system over the whole range of conditions, leading to a simple analytical equation of state for the system. This offers new physical insight into the redox properties of ceria based materials, and the theoretical methods developed should also be of great interest for other materials which exhibit continuous oxygen non-stoichiometry similar to ceria, such as perovskite oxides.