Sustainable Drying and Torrefaction Processes of Miscanthus for Use as a Pelletized Solid Biofuel and Biocarbon-Carrier for Fertilizers.

Miscanthus is resistant to dry, frosty winters in Poland and most European Union countries. Miscanthus gives higher yields compared to native species. Farmers can produce Miscanthus pellets after drying it for their own heating purposes. From the third year, the most efficient plant development begins, resulting in a yield of 25-30 tons of dry matter from an area of 1 hectare. Laboratory scale tests were carried out on the processes of drying, compacting, and torrefaction of this biomass type. The analysis of the drying process was conducted at three temperature levels of the drying agent (60, 100, and 140 °C). Compaction on a hydraulic press was carried out in the pressure range characteristic of a pressure agglomeration (130.8-457.8 MPa) at different moisture contents of the raw material (0.5% and 10%). The main interest in this part was to assess the influence of drying temperature, moisture content, and compaction pressure on the specific densities (DE) and the mechanical durability of the pellets (DU). In the next step, laboratory analyses of the torrefaction process were carried out, initially using the Thermogravimetric Analysis TGA and Differential Scaning Calorimeter DSC techniques (to assess activation energy (EA)), followed by a flow reactor operating at five temperature levels (225, 250, 275, 300, and 525 °C). A SEM analysis of Miscanthus after torrefaction processes at three different temperatures was performed. Both the parameters of biochar (proximate and ultimate analysis) and the quality of the torgas (volatile organic content (VOC)) were analyzed. The results show that both drying temperature and moisture level will affect the quality of the pellets. Analysis of the torrefaction process shows clearly that the optimum process temperature would be around 300-340 °C from a mass loss ratio and economical perspective.

Acquisition of Torrefied Biomass from Jerusalem Artichoke Grown in a Closed Circular System Using Biogas Plant Waste.

The aim of the research was to investigate the effect of biogas plant waste on the physiological activity, growth, and yield of Jerusalem artichoke and the energetic usefulness of the biomass obtained in this way after the torrefaction process. The use of waste from corn grain biodigestion to methane as a biofertilizer, used alone or supplemented with Apol-humus and Stymjod, caused increased the physiological activity, growth, and yield of Jerusalem artichoke plants and can limit the application of chemical fertilizers, whose production and use in agriculture is harmful for the environment. The experiment, using different equipment, exhibited the high potential of Jerusalem artichoke fertilized by the methods elaborated as a carbonized solid biofuel after the torrefaction process. The use of a special design of the batch reactor using nitrogen, Thermogravimetric analysis, Differential thermal analysis, and Fourier-transform infrared spectroscopy and combustion of Jerusalem artichoke using TG-MS showed a thermo-chemical conversion mass loss on a level of 30% with energy loss (torgas) on a level of 10%. Compared to research results on other energy crops and straw biomass, the isothermal temperature of 245 °C during torrefaction for the carbonized solid biofuel of Jerusalem artichoke biomass fertilized with biogas plant waste is relativlely low. An SEM-EDS analysis of ash from carbonized Jerusalem artichoke after torrefaction was performed after its combustion.

Low-Temperature Plasma Modification of Styrene-Butadiene Block Copolymer Surfaces for Improved Adhesion-A Kinetic Approach.

This paper proposed a kinetic model that can describe the changes in the adhesion properties of styrene-butadiene (SBS) block copolymer surfaces under the influence of low-temperature plasma treatment. As a measure of these changes, the peel strength of joints formed between the copolymer surface and the polyurethane adhesive was chosen. Five types of low-temperature low-pressure RF plasma, two inert plasmas (Ar and He), and three reactive plasmas (O2, CO2, and CCl4) were tested. It was found that for all these types of plasma, the peel strength with the plasma treatment time first increases rapidly reaching a maximum value, and then there is a visible decrease in peel strength, after which the peel strength increases again. This dependence of the peel strength on the plasma treatment time is very well described by the proposed model, which considers three processes: (1) the generation of radical states followed by the creation of functional groups involved in the adhesive bonding process, (2) the surface cross-linking that decreases the concentration of these functional groups, and (3) the formation of nano-roughness. The model analysis revealed differences between the action of reactive and inert plasmas in the SBS surface cross-linking mechanism and preferential etching process, as well as differences in the generation of radical states between the O2 plasma (electron process) and other plasmas tested (ionic processes).

Effect of Carbon Black Nanofiller on Adhesion Properties of SBS Rubber Surfaces Treated by Low-Pressure Plasma.

Studies on the surface modification of commercial styrene-butadiene-styrene (SBS) rubber with different carbon black (CB) nanofiller content (10-80 parts per hundred parts of rubber (phr)) performed by low-pressure oxygen plasma are presented in this paper. The adhesion properties of the rubber were determined by the peel test for adhesive-bonded joints prepared with a water-based polyurethane (PU) adhesive. The chemical structure and morphology of the SBS rubber surface before and after plasma treatment were investigated by X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM), respectively. The peel tests showed that the plasma treatment significantly improved the strength of adhesive-bonded joints in the entire range of CB tested, revealing a clear maximum for approximately 50 phr of CB. It was also found that as a result of plasma treatment, functional groups that are responsible for the reactions with the PU adhesive, such as C-OH and C=O, were formed, and their concentration, similar to the peel strength, showed maximum values for approximately 50 phr CB. The occurrence of these maxima was explained using the bound rubber model.