RESUMO
2D <100>-oriented Dion-Jacobson or Ruddlesden-Popper perovskites are widely recognized as promising candidates for optoelectronic applications. However, the large interlayer spacing significantly hinders the carrier transport. <110>-oriented 2D perovskites naturally exhibit reduced interlayer spacings, but the tilting of metal halide octahedra is typically serious and leads to poor charge transport. Herein, a <110>-oriented 2D perovskite EPZPbBr4 (EPZ = 1-ethylpiperazine) with minimized tilting is designed through A-site stereo-hindrance engineering. The piperazine functional group enters the space enclosed by the three [PbBr6]4- octahedra, pushing PbâBrâPb closer to a straight line (maximum PbâBrâPb angle ≈180°), suppressing the tilting as well as electron-phonon coupling. Meanwhile, the ethyl group is located between layers and contributes an extremely reduced effective interlayer distance (2.22 Å), further facilitating the carrier transport. As a result, EPZPbBr4 simultaneously demonstrates high µτ product (1.8 × 10-3 cm2 V-1) and large resistivity (2.17 × 1010 Ω cm). The assembled X-ray detector achieves low dark current of 1.02 × 10-10 A cm-2 and high sensitivity of 1240 µC Gy-1 cm-2 under the same bias voltage. The realized specific detectivity (ratio of sensitivity to noise current density, 1.23 × 108 µC Gy-1 cm-1 A-1/2) is the highest among all reported perovskite X-ray detectors.