Raman spectroscopic study on the structure of water in aqueous solution of alpha,omega-amino acids.

The structure and hydrogen bonding of water in an aqueous solution of various alpha,omega-amino acids were analyzed using the contours of the OH stretching in the polarized Raman spectra. From the relative intensity of the collective band (C value) corresponding to a long-range coupling of the OH stretching in the aqueous amino acid solutions, the number of hydrogen bonds disrupted due to the presence of one amino acid molecule (N(corr) value) was evaluated. The N(corr) value for glycine was slightly positive, whereas with an increase in the number of methylene groups between ammonium and carboxylate groups, the N(corr) value gradually increased. These results suggest that the species with proximal anionic and cationic groups do not disturb the hydrogen-bonded network structure of water significantly, probably due to the counteraction of the electrostatic hydration effect attributable to the anionic and cationic groups.

Raman spectroscopic study on the structure of water in aqueous solution of zwitterionic surfactants.

The structure and hydrogen bonding of water in aqueous solutions of various surfactants were analyzed using the contours of the O-H stretching in the polarized Raman spectra. From the relative intensity of the collective band (C value) corresponding to a long-range coupling of the O-H stretching in the aqueous surfactant solutions, the number of hydrogen bonds disrupted due to the presence of one surfactant molecule (N(corr) value) was evaluated. The N(corr) value for decylsulfobetaine was slightly negative, whereas those for ordinary ionic surfactants such as sodium dodecylsulfate and dodecyltrimethylammonium chloride were large positive values. Furthermore, the N(corr) for carboxybetaine surfactant was a small positive value. These results suggest that zwitterionic surfactants do not disturb the hydrogen-bonded network structure of water significantly, probably due to the counteraction of the electrostriction effect by the proximity between the anionic and cationic groups.

Raman spectroscopic study of the structure of water in aqueous solutions of amphoteric polymers.

Methacrylic acid (MA) and [3-(methacryloylamino)propyl]trimethylammonium chloride (MAPTAC) were polymerized to give amphoteric copolymers with various compositions. The structure and H-bonding of water in an aqueous solution of the copolymer were analyzed using the contours of the O-H stretching in the polarized Raman spectra. For comparison, the H-bonded network structure of aqueous solutions of homopolymers (polyMA and polyMAPTAC) was also examined. From the relative intensity of the collective band (C value) corresponding to a long range coupling of the O-H stretching in the aqueous polymer solutions, the number of H-bonds disrupted due to the presence of one monomer residue of the polymers (Ncorr) was determined. The Ncorr value for polyMA was largely positive, and with an increase in the content of the MAPTAC residue, the Ncorr value became smaller, and after passing a minimum (which was still slightly positive) at a roughly equivalent molar ratio, the Ncorr value increased again. This is in significant contrast with the larger positive Ncorr values for the homopolymers (both polyMA and polyMAPTAC), and other ordinary polyelectrolytes such as sodium polyethylenesulfonate, poly-L-lysine hydrobromide and sodium polyacrylate. Furthermore, the Ncorr value for the copolymer (MA ratio MAPTAC = 56:44) became much smaller by the neutralization of MA residues in the copolymer with sodium hydroxide, and comparable to those for neutral polymers such as poly(ethylene glycol) and poly(N-vinylpyrrolidone) and zwitterionic polymers such as poly(2-methacryloyloxyethyl phosphorylcholine) (PMPC) and poly[3-sulfo-N,N-dimethyl-N-(3'-methacryloylaminopropyl)propanaminium inner salt]. The present results clearly indicate that the amphoteric polymers with comparative contents of cationic and anionic groups do not significantly disturb the H-bonded network structure of water, probably due to the counteraction of the electrostatic hydration effect by the proximity between the anionic and cationic side groups.

Correlation between the structure of water in the vicinity of carboxybetaine polymers and their blood-compatibility.

The structure and hydrogen bonding of water in the vicinity of carboxybetaine homopolymer (poly[1-carboxy-N,N-dimethyl-N-(2'-methacryloyloxyethyl)methanaminium inner salt] (PolyCMB), and a random copolymer of CMB and n-butyl methacrylate, Poly(CMB-r-BMA), with various molecular weights were analyzed in their aqueous solutions and thin film with contours of O-H stretching of Raman and attenuated total reflection infrared (ATR-IR) spectra, respectively. The relative intensity of the collective band (C value) corresponding to a long-range coupling of O-H stretchings of the Raman spectra for aqueous solution of Poly(CMB-r-BMA) was very close to that for pure water, which is in contrast with the smaller C value in aqueous solution of ordinary polyelectrolytes. The number of hydrogen bonds collapsed by the presence of one monomer residue (N(corr) value) of PolyCMB and Poly(CMB-r-BMA) (CMB, 45 mol %) (M(w), 1.14 x 10(4) and 1.78 x 10(4), respectively) could be calculated from the C value. The N(corr) values were much smaller than those for ordinary polyelectrolytes and close to those for nonionic water-soluble polymers such as poly(ethylene glycol) and poly(N-vinylpyrrolidone). Furthermore, a water-insoluble Poly(CMB-r-BMA) with a large BMA content (M(w) = 347 kD, CMB 27 mol %) could be cast as a thin film (thickness, ca. 10 microm) on a ZnSe crystal for the ATR-IR analyses. At an early stage of sorption of water into the Poly(CMB-r-BMA) film, the O-H stretching band of IR spectra for the water incorporated in the film was similar to that for free water, which is in contrast with the drastic change in the O-H stretching band of water incorporated in polymer films such as poly(methyl methacrylate) (PMMA) and poly(n-butyl methacrylate) (PBMA). The theoretical vibrational frequency for water molecules hydrating a betaine molecule calculated by using a density functional method supported the experimental results. The adhesion of human platelets to Poly(CMB-r-BMA) films was much less than that to PMMA and PBMA. With an increase in the content of CMB residue, the number of platelets adhered to the Poly(CMB-r-BMA) film drastically decreased and then gradually increased, probably due to the increase in the roughness of the film surface. These results suggest that the carboxybetaine monomer residues with a zwitterionic structure do not significantly disturb the hydrogen bonding between water molecules in both aqueous solution and thin film systems, resulting in the excellent blood-compatibility of the carboxybetaine polymers.