RESUMO
OBJECTIVE: This study aimed to compare 3 reciprocating systems regarding design, metallurgy, mechanical properties, and shaping ability. MATERIALS AND METHODS: New Reciproc Blue R25, WaveOne Gold Primary, and REX 25 instruments (n=41 per group) were analyzed regarding design, metallurgy, and mechanical performance, while shaping ability (untouched canal walls, volume of removed dentin, and hard tissue debris) was tested in 36 anatomically matched root canals of mandibular molars. Results were compared using one-way ANOVA post hoc Tukey and Kruskal-Wallis tests with a significant level set at 5%. RESULTS: All instruments showed symmetrical cross sections with asymmetrical blades, no radial lands, no major defects, and an almost equiatomic nickel and titanium ratio. The highest R-phase start temperatures were observed with WaveOne Gold (46.1°C) and REX (44.8°C), while Reciproc Blue had the lowest R-phase start (34.5°C) and finish (20°C) temperatures. WaveOne Gold had the lowest time to fracture (169 s) and the highest maximum load (301.6 gf) (P <0.05). The maximum torque of Reciproc Blue (2.2 N.cm) and WaveOne Gold (2.1 N.cm) were similar (P >0.05), but lower than REX (2.6 N.cm) (P <0.05). No statistical differences were observed among instruments in the angle of rotation (P >0.05) and in the shaping ability in both mesial and distal canals (P >0.05). CONCLUSION: Although the overall design, temperature transition phases and mechanical behavior parameters were different among tested instruments, they were similar in terms of shaping ability. CLINICAL RELEVANCE: All tested heat-treated NiTi reciprocating systems showed similar shaping ability, without clinically significant errors.
Assuntos
Temperatura Alta , Preparo de Canal Radicular , Instrumentos Odontológicos , Desenho de Equipamento , Titânio , Metalurgia , Teste de MateriaisRESUMO
INTRODUCTION: The aim of the present study was to compare the cyclic fatigue resistance of Reciproc R25 (R25) and Reciproc Blue R25 (R25B) instruments, after simulated clinical use in traditional (TradAC) and ultraconservative (UltraAC) endodontic access cavities. METHODS: Forty mandibular molars were randomly assigned into the following groups, according to the type of access and instrument to be used: TradAC and R25, TradAC and R25B, UltraAC and R25, and UltraAC and R25B. Teeth were accessed accordingly, and the root canals were prepared using "RECIPROC ALL" kinematics. The cyclic fatigue resistance of the forty used instruments was obtained measuring the time to fracture in an artificial stainless-steel canal. Ten brand new R25 and R25B were used as control groups. The fracture surfaces and the side cutting edges of the instruments were examined with a scanning electron microscope. Data were statistically analyzed using one-way ANOVA and post hoc Tukey tests with a significance level of P < 0.05. RESULTS: R25B instruments showed significantly higher cyclic fatigue resistance than R25, regardless of the access cavity type (P < 0.05). No differences were observed in the cyclic fatigue resistance between instruments without simulated clinical use and used in TradAC (P > 0.05). R25 and R25B used in UltraAC showed significantly lower cyclic fatigue resistance compared with the instruments used in TradAC and without simulated clinical use (P < 0.05). CONCLUSIONS: R25B files showed improved cyclic fatigue resistance than R25. The use of R25B and R25 files in mandibular molars with UltraACs decreased their cyclic fatigue resistance, compared with TradAC. CLINICAL RELEVANCE: The use of Reciproc and Reciproc Blue files in mandibular molars with ultra-conservative endodontic access cavities reduced their cyclic fatigue resistance. Clinicians should be aware about the reduced cyclic fatigue resistance of these files when used in mandibular molars with UltraAC, due to the synergistic effect of access angulation and severe curvature induced in the endodontic files.
Assuntos
Instrumentos Odontológicos , Preparo de Canal Radicular , Desenho de Equipamento , Falha de Equipamento , Teste de Materiais , Aço Inoxidável , TitânioRESUMO
OBJECTIVES: To evaluate the cyclic fatigue resistance of Reciproc M-Wire R25 (VDW, Munich, Germany) and Reciproc R25 Blue instruments (VDW) driven by Direct® (VDW) contra-angle connected to an ordinary an air-driven motor or an electric motor and compare the results with those obtained by the Reciproc M-Wire R25 or Reciproc Blue R25 instruments driven by an electric torque-controlled motor using "RECIPROC ALL" preset program. MATERIALS AND METHODS: Thirty Reciproc M-Wire R25 (25/0.08v) and 30 Reciproc Blue R25 (25/0.08v) instruments were used. Cyclic fatigue resistance was tested measuring the time to fracture and the number of cycles to fracture in an artificial stainless-steel canal with a 60° angle and a 5-mm radius of curvature. The Reciproc M-Wire and Reciproc Blue instruments were activated with a 6:1 reduction handpiece powered by a torque-controlled motor using "RECIPROC ALL" preset program, with Reciproc Direct® contra-angle powered by an ordinary air-driven motor or with Direct® contra-angle powered by an electric motor (n = 10). The fracture surface of all fragments was examined with a scanning electron microscope. The results were statistically analyzed using Student's t test and one-way ANOVA at a significance level of P < 0.05. RESULTS: Cyclic fatigue life and number of cycles to fracture were significantly higher for Reciproc Blue instruments than for Reciproc M-Wire instruments regardless of the activation mode (P < 0.05). Instruments driven by Direct® contra-angle powered by an electric or by an ordinary air-driven motor revealed significantly longer cyclic fatigue life and number of cycles to fracture than instruments driven by an electric torque-controlled motor using "RECIPROC ALL" preset program (P < 0.05). CONCLUSIONS: Reciproc Blue instruments showed improved performance regarding fatigue resistance when compared to Reciproc M-Wire instruments. Instruments driven by Reciproc Direct® contra-angle showed higher cyclic fatigue life and number of cycles to fracture than instruments driven by an electric torque-controlled motor. CLINICAL RELEVANCE: Recently, Reciproc Direct®, the world's first contra-angle handpiece with integrated reciprocating motion, has been launched in endodontic market. The present study showed improved cyclic fatigue life of endodontic instruments when activated by Reciproc Direct®.
Assuntos
Análise de Falha de Equipamento , Preparo de Canal Radicular/instrumentação , Ligas , Desenho de Equipamento , Falha de Equipamento , Teste de Materiais , Microscopia Eletrônica de Varredura , Estresse Mecânico , Propriedades de Superfície , Torque , Torção MecânicaRESUMO
OBJECTIVES: To evaluate the cyclic fatigue using severely curved canals and torsional resistance of ProDesign R (Easy Equipamentos Odontológicos, Belo Horizonte, MG, Brazil), Reciproc Blue (VDW, Munich, Germany), and WaveOne Gold (Dentsply Maillefer, Ballaigues, Switzerland) reciprocating instruments MATERIALS AND METHODS: Twenty instruments of the ProDesign R (25/0.06) system, 20 instruments of the Reciproc Blue (25/0.08v) system, and 20 instrument of the WaveOne Gold (25/0.07v) system were used. Cyclic fatigue resistance was tested measuring the time to fracture and the number of cycles to fracture in an artificial stainless steel severely curved canal with 80° angle and a 3-mm radius of curvature (n = 10). Torque and angle of rotation at failure of new instruments (n = 10) were measured according to ISO 3630-1. The fracture surfaces of all fragments were examined with a scanning electron microscope. Results were statistically analyzed using one-way ANOVA and Tukey's test at a significance level of p < 0.05. RESULTS: ProDesign R instruments showed a significantly longer cyclic fatigue life than the other tested instruments (p < 0.05). Reciproc Blue showed longer cyclic life than WaveOne Gold (p < 0.05). Reciproc Blue showed the higher torsional strength, followed by WaveOne Gold and ProDesign R instruments (p < 0.05). Moreover, Reciproc Blue showed significantly higher angular rotation to fracture than ProDesign R (p < 0.05). WaveOne Gold showed intermediary results regarding angular rotation to fracture with no differences when compared to Reciproc Blue or ProDesign R instruments (p < 0.05). CONCLUSIONS: ProDesign R presented the highest cyclic fatigue resistance in severely curved canals when compared with Reciproc Blue and WaveOne Gold. However, Reciproc Blue showed the higher torsional strength overall and higher angular rotation to fracture when compared to ProDesign R. CLINICAL RELEVANCE: Despite the numerous advantages of reciprocating instruments, these instruments still have some risk of fracture during its use, especially in severely curved canals. The present study evaluated the cyclic fatigue and torsional resistance of thermally treated reciprocating instruments.
Assuntos
Instrumentos Odontológicos , Análise de Falha de Equipamento , Desenho de Equipamento , Estresse Mecânico , Propriedades de Superfície , TorqueRESUMO
This study assessed the mechanical properties of the Only One File Blue and the Reciproc Blue instruments. A total of 80 new 25 mm reciprocating NiTi instruments (25/.08v) were evaluated for their mechanical performance (n = 40 per group). Cyclic fatigue resistance, torsional fatigue, flexural resistance and buckling resistance tests were conducted. Statistical analysis was employed with a significance level set at 5%. The results indicated no statistically significant differences in resistance to cyclic fatigue neither in the fragment length between the instruments (p > 0.05). However, the Reciproc Blue instrument exhibited greater torque to fracture and a larger rotation angle than the Only One File Blue instrument (p < 0.05). The Only One File Blue instrument demonstrated higher flexibility but lower resistance to buckling compared to the Reciproc Blue instrument (p < 0.05). In conclusion, the tested instruments exhibit differences in mechanical properties, with the Reciproc Blue instrument generally presenting greater advantages than the Only One File Blue.
RESUMO
OBJECTIVE: The aim of this study was to compare the cyclic fatigue of heat-treated and non-treated instruments. MATERIALS AND METHODS: Twenty instruments with and without heat treatment from Bassi Logic were evaluated (n = 10). All instruments were subjected to dynamic cyclic fatigue through continuous rotations inside a stainless-steel tube (1.4-mm diameter, 9-mm curvature with 6-mm radius, and 90° angle) using a custom-made device, which performed 1 axial oscillation every 2 seconds with an amplitude of 3 mm, powered by a torque-controlled motor (Silver Reciproc, VDW, Germany), with speed adjusting to 950 rpm and torque to 4 N, according to manufacturer's guidance. The groups were compared using the Mann-Whitney test. RESULT: The fracture time of the heat-treated instruments (97.20 ± 39.94 second and non-treated instruments (14.30 ± 6.78 seconds had statistical differences [p < 0.05]). Heat-treated instruments were 6.8 times more resistant to fatigue than non-treated instruments (p < 0.05). CONCLUSION: Heat treatment provides increased fatigue resistance of NiTi alloy with the same design.
RESUMO
A root-end filling material is required to fill the root-end cavity without gaps or voids, to prevent root canal reinfection and to provide periapical healing. Thus, this study evaluated the volume of marginal gaps and voids of three root-end filling materials using microcomputed tomography (micro-CT). Thirty maxillary incisors were prepared and filled with gutta-percha and endodontic sealer. The specimens were scanned using micro-CT and distributed into three groups (n = 10): White MTA, MTA Repair HP, and Bio-C Repair. The root tips were resected at 90° to the longitudinal axis and the cavity (3 mm depth) was prepared with an ultrasonic tip. The materials were handled, and the cavities were filled. The specimens were rescanned and the percentual volume of gaps and voids were analyzed. The data were analyzed using Kruskal-Wallis and Dunn tests (p < .05). No statistical difference was found in the percentage of gaps among the tested materials (p > .05). White MTA presented less voids than Bio-C and MTA Repair HP (p < .05). The materials presented a similar percentual volume of gaps and White MTA presented less voids than other tested materials.
Assuntos
Materiais Restauradores do Canal Radicular , Compostos de Cálcio , Cavidade Pulpar , Guta-Percha , Obturação do Canal Radicular , Preparo de Canal Radicular , Tratamento do Canal Radicular , Silicatos , Microtomografia por Raio-XRESUMO
The aim of the present study was to evaluate the cyclic fatigue, torsional resistance and surface roughness of Reciproc R25 instruments in four different situations, namely as new instruments and as instruments tested after clinical preparation of one, two or three maxillary molars with four root canals. The total time required to perform each root canal preparation was recorded. Cyclic fatigue resistance was determined by the time to fracture using a customized testing device (n = 10 per group). The torsional test evaluated the torque and angle of rotation to failure according to ISO 3630-1 (n = 10 per group). The roughness of the working parts of new and used instruments was evaluated with a profilometer (n = 5 per group). Statistical analysis was performed using one-way ANOVA and Tukey's test. The level of significance was set at 5%. No fractures or deformations were observed after clinical use. Higher preparation time was needed during the third use of the instruments for all root canals (p < 0.05). There were no significant differences among the groups in regard to either cyclic fatigue or torsional resistance (p > 0.05). Regarding the roughness measurements, groove depth was higher on new and one- versus two- or three-maxillary-molar-prepared instruments (p < 0.05). It can be concluded that the clinical use of Reciproc instruments increased preparation time and decreased surface roughness. However, clinical use did not affect the cyclic fatigue or torsional resistance of the Reciproc instruments.
Assuntos
Preparo de Canal Radicular , Titânio , Instrumentos Odontológicos , Desenho de Equipamento , Teste de Materiais , Estresse Mecânico , TorqueRESUMO
INTRODUCTION: The purpose of this study was to evaluate the cyclic and torsional fatigue resistance of the XP-endo Shaper (FKG Dentaire, La Chaux-de-Fonds, Switzerland) and TRUShape (Dentsply Tulsa Dental Specialties, Tulsa, OK) instruments. METHODS: Twenty XP-endo Shaper (30/0.01) instruments and 20 TRUShape (30/0.06v) instruments were used. Cyclic fatigue resistance was tested by measuring the number of cycles and time to fracture in an artificial stainless steel canal with a 60° angle and a 5-mm radius of curvature (n = 10). The torque and angle of rotation at failure of new instruments (n = 10) were measured according to ISO 3630-1. The fracture surface of all fragments was examined with a scanning electron microscope. Results were statistically analyzed using the Student t test at a significance level of P < .05. RESULTS: The XP-endo Shaper instruments showed a significantly longer number of cycles to fracture and time to failure in seconds than the TRUShape instruments (P < .05). The XP-endo Shaper also presented a lower maximum torque load (P < .05) but a significantly higher angular rotation to fracture than TRUShape (P < .05). CONCLUSIONS: The XP-endo Shaper instruments showed a higher cyclic fatigue resistance and angle of rotation to fracture but lower torque to failure than TRUShape instruments.
Assuntos
Instrumentos Odontológicos , Desenho de Equipamento , Falha de Equipamento , Estresse Mecânico , Propriedades de Superfície , Torção MecânicaRESUMO
INTRODUCTION: The aim of the present study was to evaluate the influence of blue thermal treatment on the torsional resistance behavior of M-Wire Reciproc files (VDW, Munich, Germany). METHODS: Ten M-Wire Reciproc R25 (25/0.08v) and 10 Reciproc Blue R25 (25/0.08v, VDW) instruments were used. The torque and angle of rotation at failure of new instruments (n = 10) were measured according to ISO 3630-1. Three millimeters of each instrument tip was clamped to a small load cell by a lever arm linked to the torsion axis. The fracture surface of all fragments was examined with a scanning electron microscope. Results were statistically analyzed using the Student t test at a significance level of P < .05. RESULTS: The maximum torsional strength of M-Wire Reciproc was higher than Reciproc Blue instruments (P < .05). Reciproc Blue instruments showed significantly higher angular rotation to fracture than M-Wire Reciproc instruments (P < .05). Scanning electron microscopy of the fracture surface showed similar and typical features of torsional failure for the 2 types of instruments, including concentric abrasion marks and the fibrous dimple marks at the center of rotation. CONCLUSIONS: Reciproc Blue instruments showed a higher angle of rotation to fracture but a lower torque to failure than M-Wire Reciproc instruments.
Assuntos
Preparo de Canal Radicular/instrumentação , Ligas , Falha de Equipamento , Análise de Falha de Equipamento , Humanos , Microscopia Eletrônica de Varredura , Torção MecânicaRESUMO
The aim of the present study was to evaluate the cyclic fatigue of two anatomic finishing files: XP-Endo Finisher and XP-Clean. Roughness pattern and the micro-hardness of the files were also assessed. Instruments were subjected to cyclic fatigue resistance measuring the time to fracture in an artificial stainless-steel canal with a 60° angle and a 5-mm radius of curvature. The fracture surface of all fragments was examined with a scanning electron microscope. The roughness of the working parts was quantified by using a profilometer and the micro-hardness test was carried out using a Vickers hardness tester. Results were statistically analyzed using a student´s t-test at a significance level of P < 0.05. Weibull analysis was also performed. XP-Endo Finisher presented significantly longer cyclic fatigue life than XP-Clean instruments (P<0.05). XP-Endo Finisher was able to withstand 1000% more cycles to fracture when compared to XP-Clean instruments. SEM visual inspection of the fracture surfaces revealed fractographic characteristics of ductile fracture in all tested instruments; wide-ranging forms of dimples were identified and no plastic deformation in the helical shaft of the fractured instruments was observed. When mean life was compared XP-Endo Finisher lasted longer than XP-Clean with a probability of 99.9%. XP-Endo Finisher instruments also exhibited significantly lower roughness than XP-Clean instruments (P<0.05). No differences in the micro-hardness was observed between the files (P>0.05). It can be concluded that XP-Endo Finisher instruments showed improved performance when compared with XP-Clean instruments, demonstrating higher cyclic fatigue resistance and lower roughness.
Assuntos
Instrumentos Odontológicos , Teste de Materiais , Preparo de Canal Radicular/instrumentação , Ligas , Testes de Dureza , Microscopia Eletrônica de Varredura , Níquel/química , Aço Inoxidável/química , Propriedades de Superfície , Titânio/químicaRESUMO
INTRODUCTION: The aim of the present study was to evaluate the influence of Blue thermal treatment on the bending resistance and cyclic fatigue of conventional M-Wire Reciproc files (VDW, Munich, Germany). The roughness pattern and the microhardness of the files were also assessed. METHODS: Flexibility of standard Reciproc R25 files and the corresponding Blue prototypes was determined by 45° bending tests according to the ISO 3630-1 specification. Instruments were also subjected to cyclic fatigue resistance, measuring the time to fracture in an artificial stainless steel canal with a 60° angle and a 5-mm radius of curvature. The fracture surface of all fragments was examined with a scanning electron microscope. The roughness of the working parts was quantified by using a profilometer, and the microhardness test was performed using the Vickers hardness tester. Results were statistically analyzed using the Student t test with a level of significance set at P < .05. RESULTS: Reciproc Blue instruments presented a significantly longer cyclic fatigue life and significantly lower bending resistance than the original Reciproc instrument (P < .05). Regarding the roughness pattern, there was no significant difference between Reciproc Blue and the original Reciproc instruments (P > .05), whereas Reciproc Blue revealed significantly lower microhardness than the original Reciproc instrument (P < .05). CONCLUSIONS: Reciproc Blue nickel-titanium showed improved all-around performance when compared with conventional M-Wire superelastic nickel-titanium, demonstrating improved flexibility and fatigue resistance, and reduced microhardness while maintaining similar characteristics of the surface.
Assuntos
Instrumentos Odontológicos , Análise do Estresse Dentário , Estresse Mecânico , Ligas , Desenho de Equipamento , Teste de MateriaisRESUMO
Purpose: The aim of the present study was to verify the knowledge of health professionals being educated in the Medical and Dentistry courses about oral cancer, specifically Oral Squamous Cell Carcinoma (OSCC), in view of this being the most prevalent type of cancer of the head and neck. Methods: A questionnaire contained objective questions was applied with the aim of evaluating knowledge about some aspects of OSCC. Students in the clinical cycle of the Course in Medicine and Course in Dentistry participated. Both groups were in the 5th and 8th semesters at the Campuses 1 (C1) and 2 (C2). A total of 454 questionnaires were answered and evaluated, distributed as follows: 301 and 153 from the C1 and C2, respectively. Results: The results show that the students from Medicine of the C1 and C2 were observed to be "Regular" (40.67%) and "Insufficient" (44.58%), respectively. For the course in Dentistry of C1 and C2, the prevalent response was "Good" for courses, 52.67% and 46.38%, respectively. Conclusion: The results revealed an inadequate level of knowledge of OSCC. Despite the knowledge is transmitted, changes are necessary to allow the students more time in clinical practice to reptai knowledge.
Objetivo: O objetivo do presente estudo foi verificar o conhecimento dos profissionais de saúde formados nos cursos de Medicina e Odontologia sobre câncer bucal, especificamente o Carcinoma de Células Escamosas Bucais (CCEB), tendo em vista que este é o tipo de câncer de cabeça e pescoço mais prevalente. Metodologia: Um questionário contendo perguntas objetivas foi aplicado com o objetivo de avaliar o conhecimento sobre alguns aspectos do CCEB. Participaram os alunos do ciclo clínico dos cursos de Medicina e Odontologia. Ambos os grupos estavam no 5º e 8º semestres nos campi 1 (C1) e 2 (C2). Foram respondidos e avaliados 454 questionários, distribuídos da seguinte forma: 301 e 153 do C1 e C2, respectivamente. Resultados: Os resultados mostram que os estudantes de Medicina dos C1 e C2 foram observados como "Regular" (40,67%) e "Insuficiente" (44,58%), respectivamente. Para o curso de Odontologia dos C1 e C2, a resposta predominante foi "boa" para os cursos, 52,67% e 46,38%, respectivamente. Conclusão: Os resultados revelaram um nível inadequado de conhecimento da CCEB. Apesar do conhecimento ser transmitido, são necessárias mudanças para permitir que os alunos tenham mais tempo na prática clínica para reter conhecimento.
Assuntos
Humanos , Masculino , Feminino , Neoplasias Bucais , Odontologia , Recursos Humanos , Carcinoma de Células Escamosas de Cabeça e Pescoço , MedicinaRESUMO
RESUMEN: La irrigación del sistema de conductos radiculares con soluciones antibacterianas es considerada una parte esencial de la preparación químico-mecánica. Varios factores influyen en la eficacia de la irrigación del conducto radicular, incluyendo tamaño de la preparación apical y ensanchamiento, distancia de penetración de la aguja con respecto al ápice, flujo y volumen de sustancia de irrigante, dimensión de las agujas y la presencia de curvatura del conducto radicular. El tamaño de la preparación apical y la conicidad afectan el recambio del irrigante, el esfuerzo de corte en las paredes del conducto radicular y la presión en el foramen apical. La colocación de la punta de la aguja más cerca del ápice, permite un recambio de la solución más eficiente, resultando una mejor limpieza y desinfección del conducto radicular. La velocidad del irrigante, al lado de la aguja, en las paredes del conducto opuestas y frente a la salida de la aguja es dependiente del diseño de la aguja. El patrón de flujo y recambio del irrigante de las agujas con extremo abierto es diferente al de las agujas cerradas y las que logran mejor recambio de irrigante en la parte apical del conducto radicular también conducen a un aumento de la presión media en el foramen apical, lo que indica un mayor riesgo de extrusión del irrigante hacia el tejido periapical. El objetivo de esta revisión a la literatura, es evaluar los diferentes diseños de agujas y su influencia en la irrigación del sistema de conductos radiculares.
ABSTRACT: Root canal irrigation with antibacterial solutions is considered an essential part of the chemical-mechanical preparation. Several factors influence the efficacy of root canal irrigation, including apical preparation size and taper, needle penetration distance from the apex, flow and volume of irrigant substance, dimension of the needles and the presence of curvature of the root canal. The apical preparation size and the taper affect irrigant replacement, shear stress on the root canal walls, and pressure on the apical foramen. Placing the tip of the needle closer to the apex, allows more efficient solution exchange, resulting in better cleaning and disinfection of the root canal. The velocity of the irrigant, next to the needle, on the opposite canal walls and in front of the needle outlet is dependent on the design of the needle. The flow and irrigant replacement pattern of open ended needles is different from needles with closed tip. The needles that achieve better irrigant exchange in the apical part of the root canal also lead to an increase in mean pressure in the apical foramen which indicates a greater risk of extrusion of the irrigant into the periapical tissue. The objective of this literature review is to evaluate the different needle designs and their influence on the root canal system irrigation.
RESUMO
The current study aimed to evaluate the bending resistance and the cyclic fatigue life of a new heat-treated reciprocating instrument (ProDesign R). Untreated ProDesign R, Reciproc R25, and WaveOne Primary instruments were used as reference instruments for comparison. The bending resistance was performed in ten instruments of each system by using a universal testing machine and a proper apparatus. The cyclic fatigue resistance was tested measuring the number of cycles to failure in an artificial stainless steel canal. Scanning electron microscopy analysis was performed to determine the mode of fracture and possible deformations at the helical shaft. Statistical analysis was performed by using parametric methods; one-way analysis of variance plus post hoc pair-wise Tukey test for multiple comparisons (p < 0.05). Untreated ProDesign R presented significantly higher bending resistance than the other tested systems (p < 0.05). No differences were observed between ProDesign R and Reciproc files regarding the bending resistance (p > 0.05). Moreover, ProDesign R revealed a significantly longer cyclic fatigue life (p < 0.05). In contrast, Untreated ProDesign R and WaveOne instruments presented significantly lower cyclic fatigue life than Reciproc (p < 0.05). The new heat-treated reciprocating instrument ProDesign R have higher cyclic fatigue resistance than Untreated ProDesign R, Reciproc, and WaveOne instruments. ProDesign R and Reciproc were significantly more flexible than Untreated ProDesign R and WaveOne files. SCANNING 38:837-841, 2016. © 2016 Wiley Periodicals, Inc.
RESUMO
OBJECTIVE: The present study aimed to evaluate the bending resistance and cyclic fatigue fracture resistance of a new single-file reciprocating instrument called WaveOne Gold. Reciproc and WaveOne instruments were used as references for comparison. METHODS: Sixty 25-mm NiTi instruments (Reciproc R25, WaveOne Primary and WaveOne Gold Primary) were tested. Flexibility was determined by applying 45° bending tests using a universal testing machine (n=10). A custom-made device was used during cyclic fatigue test (n=10), comprising a stainless steel artificial canal measuring 1.4 mm in diameter, 19 mm in total length with an 86° angle and 6 mm radius of curvature. Possible deformations at the helical shaft and mode of fracture were evaluated using scanning electron microscopy analysis. Statistical analysis was performed using one-way analysis of variance. Post hoc pair-wise comparisons were performed using Tukey's test for multiple comparisons (P<0.05). RESULTS: WaveOne presented significantly higher bending resistance than the other tested systems (P<0.05), whereas Reciproc presented the lowest bending resistance (P<0.05). Reciproc revealed a significantly longer cyclic fatigue fracture resistance than the other systems (P<0.05). CONCLUSION: Although WaveOne Gold presented higher flexibility than WaveOne, no differences in the resistance to fatigue were observed between both systems. The Reciproc files were more flexible and resistant to fatigue for the angle of curvature of 86° and 6 mm radius than WaveOne and WaveOne Gold files.
RESUMO
INTRODUCTION: This study evaluated the bending resistance and cyclic fatigue life of a new single-file reciprocating instrument (Unicone; Medin, Nové Mesto na Morave, Czech Republic). Reciproc (VDW, Munich, Germany) and WaveOne (Dentsply Maillefer) instruments were used as references for comparison. METHODS: Flexibility was determined by 45° bending tests using a universal testing machine. The cyclic fatigue test was performed using a custom-made device. For this test, an artificial canal with a 60° angle and a 5-mm radius of curvature was used. Scanning electron microscopic analysis was performed to determine the mode of fracture and possible deformations at the helical shaft. Statistical analysis for the bending resistance test was performed using parametric methods (ie, 1-way analysis of variance). Post hoc pair-wise comparisons were performed using the Tukey test for multiple comparisons (P < .05). Weibull analysis was used to calculate the mean life, beta, and eta parameters. RESULTS: Reciproc presented significantly lower bending resistance than the other tested systems (P < .05), whereas no differences were observed between WaveOne and Unicone (P > .05). When mean life was compared among the brands, Reciproc lasted longer than WaveOne with a probability of 99.9%, longer than Unicone in the "RECIPROC ALL" mode with a probability of 99.9%, and longer than Unicone in the "WAVEONE ALL" mode with a probability of 99.9% (all statistically significant). Moreover, WaveOne lasted longer than Unicone in the "RECIPROC ALL" mode with a probability of 98.5% and longer than Unicone in the "WAVEONE ALL" mode with a probability of 99.8% (all statistically significant). Finally, Unicone in the "RECIPROC ALL" mode lasted longer than Unicone in the "WAVEONE ALL" mode with a probability of 95.3% (statistically significant). CONCLUSIONS: The new reciprocating instrument Unicone showed lower cyclic fatigue resistance compared with Reciproc R25 and WaveOne Primary files.
Assuntos
Ligas Dentárias/química , Desenho de Equipamento , Níquel/química , Preparo de Canal Radicular/instrumentação , Titânio/química , Instrumentos Odontológicos , Análise do Estresse Dentário/instrumentação , Falha de Equipamento , Teste de Materiais , Microscopia Eletrônica de Varredura , Maleabilidade , Distribuição Aleatória , Rotação , Aço Inoxidável/química , Estresse Mecânico , Propriedades de SuperfícieRESUMO
Abstrac The aim of the present study was to evaluate the cyclic fatigue, torsional resistance and surface roughness of Reciproc R25 instruments in four different situations, namely as new instruments and as instruments tested after clinical preparation of one, two or three maxillary molars with four root canals. The total time required to perform each root canal preparation was recorded. Cyclic fatigue resistance was determined by the time to fracture using a customized testing device (n = 10 per group). The torsional test evaluated the torque and angle of rotation to failure according to ISO 3630-1 (n = 10 per group). The roughness of the working parts of new and used instruments was evaluated with a profilometer (n = 5 per group). Statistical analysis was performed using one-way ANOVA and Tukey's test. The level of significance was set at 5%. No fractures or deformations were observed after clinical use. Higher preparation time was needed during the third use of the instruments for all root canals (p < 0.05). There were no significant differences among the groups in regard to either cyclic fatigue or torsional resistance (p > 0.05). Regarding the roughness measurements, groove depth was higher on new and one- versus two- or three-maxillary-molar-prepared instruments (p < 0.05). It can be concluded that the clinical use of Reciproc instruments increased preparation time and decreased surface roughness. However, clinical use did not affect the cyclic fatigue or torsional resistance of the Reciproc instruments.
Assuntos
Titânio , Preparo de Canal Radicular , Estresse Mecânico , Teste de Materiais , Torque , Instrumentos Odontológicos , Desenho de EquipamentoRESUMO
ABSTRACT Objective: This study compared the fatigue behavior of endodontic instruments manufactured with conventional NiTi alloy electropolishing, RaCe (FKG Dentaire, LaChauxdeFonds, Switzerland), with instruments manufactured with NiTi CM Wire subjected to thermomechanical treatment, in the manufacturing process, HyFlex CM (Coltène Whaledent, Cuyahoga Falls, Ohio, USA), both with similar geometry and dimensions in order to determine the influence of the manufacturing process in the fatigue resistance. Methods: The methodoly consisted of twenty HyFlex CM and RaCe instruments with D0 0.25 mm, taper 0.06 mm / mm, 25 mm length, both with triangular cross section. The fracture resistance was evaluated by static fatigue test, using a stainless artificial canal with 5mm of radius (86°), recording the time and calculating the number of cycles until fracture occurs (NCF). For statistical analysis the Student t test was used The fractured instruments surface was analyzed by SEM. Results: The NCF was significantly higher for HyFlex CM instruments in comparison with RaCe files (P˂0.05) being 1336% more resistant to fatigue. The analysis of the fractured surface by SEM showed ductile-kind morphological characteristics for both instruments and the absence of plastic deformation. Conclusion: HyFlex CM instruments present higher values of NCF. Thus, it can be concluded that the thermal treatment to which these instruments with CM Wire alloy are submitted makes them more resistant to fracture than Race instruments manufactured with conventional NiTi alloy electropolishing.
RESUMO Objetivo: Este estudo comparou a vida em fadiga de instrumentos endodônticos fabricados com a liga de NiTi convencional com eletropolimento de superfície, RaCe (FKG Dentaire, LaChauxdeFonds, Suiça), com instrumentos fabricados com a liga de NiTi CM Wire, submetidos a tratamento termomecânico, no processo de fabricação, HyFlex CM (Coltene Whaledent, Cuyahoga Falls, Ohio, EUA), ambos com geometria e dimensões semelhantes, visando determinar a influência do processo de fabricação das ligas e do acabamento superficial na resistência à fadiga. Métodos: Foram utilizados vinte instrumentos HyFlex CM e RaCe com D0 0,25mm, conicidade 0,06mm/mm, 25mm de comprimento, ambos com seção transversal triangular. A resistência à fratura foi avaliada através de teste estático de fadiga ciclica, utilizando um canal artificial em aço-inoxidável com 5mm de raio (86°), sendo registrado o tempo e calculado o número de ciclos para ocorrer a fratura (NCF). Para análise estatística empregou-se o teste t de Student. As superfícies de fratura dos instrumentos foram analisadas em MEV. Resultados: O NCF foi significativamente maior para os instrumentos HyFlex CM em comparação com as limas RaCe (p˂0,05), sendo 1336% mais resistentes à fadiga. A análise das superfícies fraturadas em MEV revelou características morfológicas do tipo dúctil para ambos os instrumentos e ausência de deformação plástica. Conclusão: Os instrumentos HyFlex CM apresentaram valores mais elevados de NCF. Deste modo, pode-se concluir que o tratamento térmico a qual estes instrumentos com a liga CM Wire foram submetidos os torna mais resistentes à fratura do que os instrumentos Race, fabricados com a liga de NiTi convencional com eletropolimento.
RESUMO
Objetivo: O objetivo do presente estudo foi avaliar a influência do pré-alargamento coronário na resistência à fadiga cíclica de dois instrumentos reciprocantes tratados termicamente. Métodos: 20 instrumentos Reciproc Blue (R25 Blue) e 20 instrumentos X1 Blue (X1) foram utilizados para instrumentar blocos de resina simulando um molar superior com três canais radiculares. Os dentes foram divididos em quatro grupos (n=10), de acordo com o instrumento e com a técnica de instrumentação utilizada: grupos R25 e X1 - instrumentação com R25 Blue (25/0.08) ou X1 Blue (25/0.06), respectivamente, sem alargamento prévio; e grupos R25 ou X1 + pré-alargamento cervical - pré-alargamento com os instrumentos ProTaper Universal SX e S1 antes da instrumentação com R25 Blue ou X1. Os instrumentos foram testados com relação à fadiga cíclica utilizando-se um canal simulado de aço inoxidável com ângulo de curvatura de 86 graus e raio de curvatura de 6 mm. Os instrumentos foram acionados utilizando-se o movimento "RECIPROC ALL" do motor endodôntico (VDW) e o tempo de instrumentação até a fratura do instrumento foi contabilizado. Os resultados foram analisados pelo teste t de Student (p<0,05). Resultados: Os instrumentos X1 apresentaram maior resistência à fadiga cíclica do que R25 Blue em ambas as condições testadas (p<0,05). Não houve diferença entre os grupos com e sem pré-alargamento coronário para os instrumentos R25 Blue e X1 (p>0,05). Conclusão: O instrumento X1 Blue apresentou maior resistência à fadiga cíclica do que o Reciproc Blue. O pré-alargamento coronário não foi capaz de aumentar a resistência à fratura por fadiga cíclica dos instrumentos testados (AU).
Objective: The aim of this study was to evaluate the influence of cervical pre-flaring on the cyclic fatigue resistance of two heat-treated reciprocating instruments. Methods: 20 Reciproc Blue (R25 Blue) instruments e 20 X1 Blue File (X1) were used to instrument resin blocks simulating an upper molar with 3 root canals. The specimens were divided into four groups (n=10) according the instrument and type of instrumentation used: R25 and X1 groups: root canal preparation with R25 Blue (25/0.08) ou X1 Blue (25/0.06), without cervical pre-flaring; R25 or X1 + cervical pre-flaring- pre-flaring with ProTaper Universal SX e S1 before instrumentation with R25 Blue or X1 blue. After instrumentation the instruments were tested for cyclic fatigue using a simulated stainless steel root canal with 86 degree bending angle and 6 mm bending radius. The instruments were triggered using the "RECIPROC ALL" motion of a reciprocating endodontic motor (VDW) and the instrumentation time until instrument fracture was accounted. Results were analyzed by Students t-test (p<0.05). Results: Statistical analysis showed that the X1 Blue showed higher resistance to cyclic fatigue than the R25 Blue under both conditions tested (p<0.05). There were no differences between the groups with and without coronary pre-flaring for the R25 Blue and X1 Blue (p<0.05). Conclusion: X1 Blue showed higher resistance to cyclic fatigue than the R25 Blue. The cervical pre-flaring did not increased the resistance to cyclic fatigue fracture of the tested instruments (AU)