Avaliação da deformação superficial do osso gerada por cargas axiais em implantes de diferentes comprimentos / Evaluation of superfi cial bone deformation for axial loads with different implants lengths
ImplantNewsPerio
; 2(5): 868-873, set.-out. 2017. ilus, tab
Article
em Pt
| LILACS, BBO
| ID: biblio-877282
Biblioteca responsável:
BR510.1
RESUMO
Objetivo:
avaliar, por meio de extensometria, a transmissão da carga mastigatória axial ao osso de suporte em próteses unitárias implantossuportadas por implantes de diferentes comprimentos. Material emétodos:
em um bloco de poliuretano que simula 2 mm de osso cortical e o restante de medular, segundo a norma ASTMF1839, com 22 mm x 16 mm x 150 mm, foram instalados quatro implantes cone-morse infraósseos 2 mm G1) 4 mm x 7 mm; G2) 4 mm x 9 mm; G3) 4 mm x 11 mm; G4) 4 mm x 13 mm. Sobre os mesmos, foram instalados pilares do tipo esteticone e cilindros metálicos. Dois extensômetros lineares foram colados na superfície do bloco, tangenciando a plataforma de cada implante (mesial e distal). Em uma máquina de ensaio universal, foi aplicada uma carga de 100 N sobre a superfície oclusal de cada cilindro. Para cada grupo, foram realizados cinco medições e os dados obtidos em microdeformacão (µÆ). Foi verificada a normalidade dos dados pelo teste de Shapiro-Wilk e realizada a análise de variância 1 critério (p < 0,05), e o teste Tukey (p ï³ 0,5).Resultados:
as médias e os desvios-padrão das amostras foram, respectivamente, G1 346.16,3 ± 10,28 µÆ; G2 216.91 ± 15,47 µÆ; G3 114,41 ± 2,33 µÆ; e G4 76.83,3 ± 7,13 µÆ. O teste de Shapiro-Wilk constatou a normalidade dos dados, e os testes Anova e Turkey a diferença estatística significante entre todos os grupos.Conclusão:
para cargas axiais, implantes com menor comprimento produziram maior deformação no osso superfi cial.ABSTRACT
Purpose:
the aim of this study was to evaluate, by extensometry, the transmission of the axial masticatory load to supporting bone around implants of different lengths. Material andmethods:
in a block of polyurethane that simulates 2 mm of cortical bone and the remaing of medullary bone, according to the ASTM-F1839 standard, with 22 mm x 16 mm x 150 mm, were installed 4 morse tappered dental implants, 2 mm subcrestal G1) 4 mm x 7 mm; G2) 4 mm x 9 mm; G3) 4 mm x 11 mm; G4) 4 mm x 13 mm. Estheticone-like abutments and metallic cylinders were placed. Two linear strain gauges were bonded on block surface, tangential to the platform of each implant (mesial and distal). A 100 N load on the occlusal surface of each cylinder was applied to a universal test machine. For each group, five measurements and the data obtained in microdeformation (µÆ) were performed. The normality of the data was verified by the Shapiro-Wilk test and (p < 0.05) and Tukey's test (p ï³ 0.5).Results:
the means and standard deviation of the samples were respectively G1 346.16.3 ± 10.28 µÆ; G2 216.91 ± 15.47 µÆ; G3 114.41 ± 2.33 µÆ; G4 76.83.3 ± 7.13 µÆ. The Shapiro-Wilk test exhibit the normality of the data, and the Anova and Turkey tests exhibit statistically significant difference between all groups.Conclusion:
axial load produced more tension for short implants on the superficial bone.Palavras-chave
Buscar no Google
Coleções:
01-internacional
Base de dados:
BBO
/
LILACS
Assunto principal:
Fenômenos Biomecânicos
/
Força de Mordida
/
Análise de Variância
/
Análise de Elementos Finitos
/
Equipamentos de Medição de Riscos
/
Implantação Dentária
Tipo de estudo:
Etiology_studies
/
Evaluation_studies
Limite:
Humans
Idioma:
Pt
Revista:
ImplantNewsPerio
Assunto da revista:
Odontologia
Ano de publicação:
2017
Tipo de documento:
Article
País de afiliação:
Brasil