A High-Rate and Long-Life Sodium Metal Battery Based on a NaB3H8 â
xNH3@NaB3H8 Composite Solid-State Electrolyte.
Angew Chem Int Ed Engl
; 63(17): e202401480, 2024 Apr 22.
Article
em En
| MEDLINE
| ID: mdl-38351436
ABSTRACT
All-solid-state sodium metal batteries are promising for large-scale energy storage applications owing to their intrinsic safety and cost-effectiveness. However, they generally suffer from sodium dendrite growth or rapid capacity fading, especially at high rates, mainly due to poor wettability, sluggish ionic transport, or low interfacial stability of the solid electrolytes. Herein, we report a novel composite, NaB3H8 â
xNH3@NaB3H8 (x<1), as a new class of solid electrolyte for high-rate batteries. NaB3H8 â
xNH3@NaB3H8 is obtained from the sticky NaB3H8 â
NH3 after removal of NH3 partially at room temperature. It delivers an ionic conductivity of 0.84â
mS cm-1 at 25 °C and reaches 20.64â
mS cm-1 at 45 °C after an order-disorder phase transformation. It also reveals a good capability of dendrite suppression and remarkable stability against sodium metal. These performances enable the all-solid-state Na//TiS2 battery with a high capacity of 232.4â
mAh g-1 (97.2 % of theoretical capacity) and long-term cycling stability at 1â
C. Notably, this battery shows superior long-life cycling stability even at 5 and 10â
C, which has been rarely reported in all-solid-state sodium metal batteries. This work opens a new group of solid electrolytes, contributing to fast-charging or high-power-density sodium metal batteries.
Texto completo:
1
Coleções:
01-internacional
Base de dados:
MEDLINE
Idioma:
En
Revista:
Angew Chem Int Ed Engl
Ano de publicação:
2024
Tipo de documento:
Article
País de afiliação:
China