Push-Out Bond Strength of Glass Fiber Endodontic Posts with Different Diameters.
Materials (Basel)
; 17(7)2024 Mar 25.
Article
em En
| MEDLINE
| ID: mdl-38612007
ABSTRACT
(1) Background:
The retention of intraradicular posts is an important factor for the prognosis of endodontically treated teeth. The purpose of this study was to evaluate the push-out bond strength (PBS) of the posts relating to their diameter and region of the root. (2)Methods:
A total of 40 premolar teeth (decoronated and root canal-filled) were divided into four groups (n = 10). After post-space preparation, different sizes (1.0, 1.2, 1.5, and 2.0 mm) of glass fiber posts were luted with resin cement into the root canals. After placement, 2 mm thick slices were cut from the roots according to their apical, middle, and coronal regions (n = 116). Push-out tests were carried out in a universal testing machine on each slice. A statistical evaluation of the data was applied. (3)Results:
When comparing the diameter, the 2.0 mm posts had the highest PBS (111.99 ± 10.40 N), while the 1.0 mm posts had the lowest PBS (99.98 ± 8.05 N). Divided by the surface of the bonded area, the average PBS value was the highest for the 1.0 mm posts (18.20 ± 1.67 MPa) and the lowest for the 2.0 mm posts (12.08 ± 1.05 MPa). (4)Conclusions:
Within the limitations of the study, when comparing the regions of the roots, no significant differences were found among the PBS values of the three regions (p = 0.219). When comparing the diameters, significant differences were shown between the PBS values of the four groups (p = 0.023 and p = 0.003, respectively).
Texto completo:
1
Coleções:
01-internacional
Base de dados:
MEDLINE
Idioma:
En
Revista:
Materials (Basel)
Ano de publicação:
2024
Tipo de documento:
Article
País de afiliação:
Hungria