RESUMEN
Thin film libraries of Fe-Co-V were fabricated by combinatorial sputtering to study magnetic and structural properties over wide ranges of composition and thickness by high-throughput methods: synchrotron X-ray diffraction, magnetometry, composition, and thickness were measured across the Fe-Co-V libraries. In-plane magnetic hysteresis loops were shown to have a coercive field of 23.9 kA m-1 (300 G) and magnetization of 1000 kA m-1. The out-of-plane direction revealed enhanced coercive fields of 207 kA m-1 (2.6 kG) which was attributed to the shape anisotropy of column grains observed with electron microscopy. Angular dependence of the switching field showed that the magnetization reversal mechanism is governed by 180° domain wall pinning. In the thickness-dependent combinatorial study, co-sputtered composition spreads had a thickness ranging from 50 to 500 nm and (Fe70Co30)100-xVx compositions of x = 2-80. Comparison of high-throughput magneto-optical Kerr effect and traditional vibrating sample magnetometer measurements show agreement of trends in coercive fields across large composition and thickness regions.
RESUMEN
Bimetallic colloidal CoPt nanoalloys with low platinum content were successfully synthesized following a modified polyol approach. Powder X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), thermogravimetric analysis (TGA), and transmission electron microscopy (TEM) studies were performed to estimate the crystal structure, morphology, and surface functionalization of the colloids, respectively, while the room-temperature magnetic properties were measured using a vibrating sample magnetometer (VSM). The particles exhibit excellent uniformity, with a narrow size distribution, and display strong room-temperature hysteretic ferromagnetic behavior even in the as-made form. Upon annealing at elevated temperatures, progressive formation and co-existence of exchange coupled, of both chemically ordered and disordered phases significantly enhanced the room-temperature coercivity.
RESUMEN
Metamagnetic off-stoichiometric Heusler alloys are actively being investigated because of their great potential as magnetocaloric materials. These properties are intimately related to the nanoscale homogeneity of their magnetic properties, mainly due to a strong influence of the nature of the exchange interactions between Mn atoms on the magnetism of the alloys. In this work, a spontaneous exchange bias phenomenon on a Ni-Co-Mn-Sn metamagnetic Heusler sputtered film is presented and studied in detail. More particularly, a series of DC magnetization curves measured as a function of the temperature demonstrates that the system exhibits canonical spin glass-like features. After a careful study of the field-cooling and zero-field-cooling curves measured on this system, the existence of magnetic inhomogeneities is inferred, as a consequence of the competition between ferromagnetic and antiferromagnetic exchange interactions between Mn atoms. Further AC susceptibility measurements on this system demonstrate that the underlying exchange bias phenomenon can be attributed to a magnetic clusters model based on superferromagnetic-like interactions present in the film. These findings suggest that the spontaneous exchange bias exhibited by the studied system is a consequence of the formation of this superferromagnetic-like state.
RESUMEN
A Fe-Co-Nb thin film materials library was deposited by combinatorial magnetron sputtering and investigated by high-throughput methods to identify new noncubic ferromagnetic phases, indicating that combinatorial experimentation is an efficient method to discover new ferromagnetic phases adequate for permanent magnet applications. Structural analysis indicated the formation of a new magnetic ternary compound (Fe,Co)3Nb with a hexagonal crystal structure (C36) embedded in an FeCo-based matrix. This nanocomposite exhibits characteristics of a two-phase ferromagnetic system, the so-called hard-soft nanocomposites, indicating that the new phase (Fe,Co)3Nb is ferromagnetic. Magnetic hysteresis loops at various angles revealed that the magnetization reversal process is governed by a domain wall pinning mechanism.