Synthesis of Mixed-Valent Lanthanide Sulfide Nanoparticles.

In targeting reduced valent lanthanide chalcogenides, we report the first nanoparticle synthesis of the mixed-valent ferromagnets Eu3 S4 and EuSm2 S4 . Using divalent lanthanide halides with bis(trimethylsilyl)sulfide and oleylamine, we prepared nanoparticles of EuS, Eu3 S4 , EuSm2 S4 , SmS1.9 , and Sm3 S4 . All nanoparticle phases were identified using powder X-ray diffraction, transmission electron microscopy was used to confirm morphology and nanoparticle size, and magnetic susceptibility measurements for determining the ordering temperatures and valence. The UV/Vis, Raman and X-ray photoelectron spectroscopies for each phase were compared. Surprisingly, the phase is influenced by the halide and the reaction temperature, where EuCl2 formed EuS while EuI2 formed Eu3 S4 , highlighting the role of kinetics in phase stabilization. Interestingly, at lower temperatures EuI2 initially forms EuS, and converts over time to Eu3 S4 .

Mononuclear to Polynuclear UIV Structural Units: Effects of Reaction Conditions on U-Furoate Phase Formation.

Uranium(IV) complexation by 2-furoic acid (2-FA) was examined to better understand the effects of ligand identity and reaction conditions on species formation and stability. Five compounds were isolated: [UCl2 (2-FA)2 (H2 O)2 ]n (1), [U4 Cl10 O2 (THF)6 (2-FA)2 ]⋅2 THF (2), [U6 O4 (OH)4 (H2 O)3 (2-FA)12 ]⋅7 THF⋅H2 O (3), [U6 O4 (OH)4 (H2 O)2 (2-FA)12 ]⋅8.76 H2 O (4), and [U38 Cl42 O54 (OH)2 (H2 O)20 ]⋅m H2 O⋅n THF (5). The structures were determined by single-crystal X-ray diffraction and further characterized by Raman, IR, and optical absorption spectroscopy. The thermal stability and magnetic behavior of the compounds were also examined. Variations in the synthetic conditions led to notable differences in the structural units observed in the solid state. At low H2 O/THF ratios, a tetranuclear oxo-bridged [U4 O2 ] core was isolated. Aging of this solution resulted in the formation a U38 oxo cluster capped by chloro and water ligands. However, at increasing water concentrations only hexanuclear units were observed. In all cases, at temperatures of 100-120 °C, UO2 nanoparticles formed.

Dissolution-Precipitation Synthesis and Characterization of Zinc Whitlockite with Variable Metal Content.

In the present work, a series of zinc whitlockite (CaxZny(HPO4)2(PO4)12) powders was synthesized by a low-temperature dissolution-precipitation process for the first time. The phase conversion from calcium hydroxyapatite to zinc whitlockite occurred in an acidic medium in the presence of Zn2+ ions. Variable chemical composition of the synthesis products was achieved by changing Ca-to-Zn molar ratio in the reaction mixture. Investigation of the phase evolution as a function of time demonstrated that phase-pure zinc whitlockite powders can be synthesized in just 3 h. It is also demonstrated that single-phase products can be obtained when the Ca-to-Zn ratio in the reaction medium is in the range from 9 to 30. With higher or lower ratios, neighboring crystal phases such as scholzite or calcium hydroxyapatite were obtained. The morphology of the synthesized powders was found to be dependent on the chemical composition, transforming from hexagonal to rhombohedral plates with the increase of Zn content. Thermal stability studies revealed that the synthesized compounds were thermally unstable and decomposed upon heat treatment.

Giant band splittings in EuS and EuSe magnetic semiconductor nanocrystals.

Using magnetic circular dichroism (MCD) spectroscopy, we demonstrate giant temperature- and field-dependent conduction-band splittings in colloidal EuS and EuSe nanocrystals.