RESUMEN
Langmuir films of 4-{[4-({4-[(trimethylsilyl)ethynyl]phenyl}ethynyl)phenyl]ethynyl} benzenaminium chloride ([1 H]Cl) undergo anion metathesis when assembled on an aqueous auric acid (HAuCl4 ) subphase. Subsequent transfer to solid supports gives well-formed Langmuir-Blodgett (LB) monolayers of [1 H]AuCl4 in which the trimethylsilyl group serves as the surface contacting group. Photoreduction of the aurate on these monolayers leads to the formation of metallic gold nanoislands, which were distributed over the surface of the film. Electrical properties of these nascent devices were determined by recording current-voltage (I-V) curves with conductive atomic force microscopy (c-AFM) using the PeakForce tunneling AFM (PF-TUNA) mode. This gives consistent sigmoidal I-V curves that are indicative of well-behaved junctions free of metallic filaments and short circuits. The photoreduction of a metal precursor incorporated onto monomolecular films is therefore proposed as an effective method for the fabrication of molecular junctions.
RESUMEN
Langmuir films have been fabricated from 4-[4'-(4''-thioacetyl-phenyleneethynylene)-phenyleneethynylene]-aniline (NOPES) after cleavage of the thioacetyl protecting group. Characterization by surface pressure vs area per molecule isotherms and Brewster angle microscopy reveal the formation of a high quality monolayer at the air-water interface. One layer Langmuir-Blodgett (LB) films were readily fabricated by the transfer of the NOPES Langmuir film onto solid substrates. X-ray photoelectron spectroscopy (XPS), surface polarization-modulated infrared reflection-absorption spectroscopy (PM-IRRAS), and quartz crystal microbalance (QCM) experiments conclusively demonstrate the formation of one layer LB films in which the functional group associated with binding to the substrate can be tailored by the film transfer conditions. Using LB methods this molecule could be transferred to gold samples with either the amine or thiol group attached to the gold surface. The amine group is directly attached to the gold substrate (Au-NH(2)-OPE-SH) when the substrate is initially immersed in the subphase and withdrawn during the transfer process; in contrast, monomolecular films in which the thiolate group is attached to the gold substrate (Au-S-OPE-NH(2)) are obtained when the substrate is initially out of the subphase and immersed during the transfer process. The morphology of these films was analyzed by atomic force microscopy (AFM), showing the formation of homogeneous layers. Film homogeneity was confirmed by cyclic voltammetry, which revealed a large passivation of gold electrodes covered by NOPES monolayers. Electrical properties for both polar orientated junctions have been investigated by scanning tunnelling microscopy (STM), with both orientations featuring a nonrectifying behavior.
RESUMEN
Herein trimethylsilane (TMS) is demonstrated to be an efficient binding group suitable for construction of metal-molecule-metal (M-mol-M') junctions, in which one of the metal contacts is an atomically flat gold surface and the other a scanning tunnelling microscopy (STM) tip. The molecular component of the M-mol-M' devices is an oligomeric phenylene ethynylene (OPE) derivative Me(3)Si C≡C{C(6)H(4)C≡C}(2)C(6)H(4)NH(2), featuring both Me(3)SiC≡C and NH(2) metal contacting groups. This compound can be assembled into Langmuir-Blodgett (LB) films on Au--substrates by surface binding through the amine groups. Alternatively, low coverage (sub-monolayer) films are formed by adsorption from solution. In the case of condensed monolayers top electrical contacts are formed to STM tips through the TMS end group. In low coverage films, single molecular bridges can be formed between the gold surface and a gold STM tip. The similarity in the I-V response of a one-layer LB film and the single molecule conductance experiments reveals several points of critical importance to the design of molecular components for use in the construction of M-mol-M' junctions. Firstly, the presence of neighbouring π systems does not have a significant effect on the conductance of the M-mol-M' junction. Secondly, in the STM configuration, intermolecular electron hopping does not significantly enhance the junction transport characteristics. Thirdly, the symmetric behaviour of the I-V curves obtained, despite the different metal-molecule contacts, indicates that the molecule is simply an amphiphilic electron-donating wire and not a molecular diode with strong rectifying characteristics. Finally, the conductance values obtained from the amine/TMS-contacted OPE described here are of the same order of magnitude as thiol anchored OPEs, making them attractive alternatives to the more conventionally used thiol-contacting chemistry for OPE molecular wires.